Alcohol-soluble aqueous composite plastic ink for gravure and making method thereof

A composite plastic, alcohol-based technology, used in inks, printing devices, printing and other directions, can solve problems such as human injury and insufficient environmental protection, and achieve the effects of reducing pollution, improving color development, and improving adhesion.

Active Publication Date: 2009-10-07
CHENGDU XINJIN TUOZHAN PRINTING INK
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing plastic gravure printing packaging is not environmentally friendly enough and has certain harm to the human body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Gravure alcohol water-based composite plastic ink (yellow), comprising the following components by weight:

[0025] Multi-component acrylate copolymer resin 32 parts

[0026] 3 parts polyketone resin

[0027] 10 parts yellow paint

[0028] 1 part dispersant

[0029] Adhesion promoter and chelating agent 1 part

[0030] 43 parts of ethanol

[0031] The preparation technology of above-mentioned gravure alcohol water-based composite plastic ink is as follows:

[0032] (1), ethanol and water in the formula are made into a mixed solvent in a ratio of 8:2;

[0033] (2), stirring and dissolving the solid polyketone resin into a 50% polyketone resin solution with a part of the mixed solvent of the above step (1);

[0034] (3), weigh the yellow pigment, dispersant, polyketone resin solution and multi-component acrylate copolymer resin and the remaining mixed solvent in the batching tank according to the above weight ratio, stir and disperse for 30 minutes with a high-speed...

Embodiment 2

[0039] Gravure alcohol water-based composite plastic ink (red), comprising the following components by weight:

[0040] Multi-component acrylate copolymer resin 25 parts

[0041] 2 parts polyketone resin

[0042] 12 parts red pigment

[0043] dispersant 3 parts

[0044] Adhesion promoter and chelating agent 1 part

[0045] 30 parts ethanol

[0046] The preparation technology of above-mentioned gravure alcohol water-based composite plastic ink is as follows:

[0047] (1), ethanol and water in the formula are made into a mixed solvent in a ratio of 7:3;

[0048] (2), stirring and dissolving the solid polyketone resin into a 50% polyketone resin solution with a part of the mixed solvent of the above step 1;

[0049] (3), weigh the yellow pigment, dispersant, polyketone resin solution and multi-component acrylate copolymer resin and the remaining mixed solvent in the batching tank according to the above weight ratio, stir and disperse for 35 minutes with a high-speed dispers...

Embodiment 3

[0054] Gravure alcohol water-based composite plastic ink (red), comprising the following components by weight:

[0055] Multi-component acrylate copolymer resin 35 parts

[0056] 5 parts polyketone resin

[0057] 10 parts red pigment

[0058] Dispersant 2 parts

[0059] Adhesion promoter and chelating agent 1 part

[0060] Ethanol 50 parts

[0061] The preparation technology of above-mentioned gravure alcohol water-based composite plastic ink is as follows:

[0062] (1), ethanol and water in the formula are made into a mixed solvent in a ratio of 6:4;

[0063] (2), stirring and dissolving the solid polyketone resin into a 50% polyketone resin solution with a part of the mixed solvent of the above step (1);

[0064](3), weigh red pigment, dispersant, polyketone resin solution and multi-component acrylate copolymer resin and the remaining mixed solvent in the batching tank according to the above weight ratio, stir and disperse for 28 minutes with a high-speed disperser, ma...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
acid valueaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a gravure alcohol aquosity composite plastic ink, which comprises the following parts: polybasic allyl propionate copolymerized resin, polyketone resin, dye, dispersant, adhesion accelerating and chelant and alcohol. The invention makes ink possess excellent alcohol solubility and solvent releasing property, which improves ink fluidity and adhesion effectively.

Description

technical field [0001] The invention relates to an ink, in particular to a gravure alcohol water-based composite plastic ink and a preparation process thereof. Background technique [0002] In recent years, with the rapid development of the packaging industry, the plastic gravure ink market is also growing. At present, in the printing of plastic films in my country, gravure printing has unique features that cannot be compared with other printings. It is very popular in the industry and is generally optimistic about the development prospects of plastic gravure printing inks. Gravure printing inks are widely used in the plastic packaging industry. , such as plastic packaging for food, medicine, feed, agricultural products, daily necessities, etc., almost includes the packaging of various industries, especially for food packaging. The colorful and novel packaging placed on the food shelves of major shopping malls and supermarkets , A variety of foods are packaged in plastic grav...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/10B41M1/10C09D11/033C09D11/107
Inventor 付勇
Owner CHENGDU XINJIN TUOZHAN PRINTING INK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com