Freight car compartment powder metallurgy brake block

A technology of powder metallurgy and carriage, applied in the direction of friction linings, mechanical equipment, etc., can solve problems such as unstable friction coefficient, wheel tread damage, poor heat dissipation, etc., achieve reasonable shape and structure design, stable friction performance, and improve production efficiency. Effect

Inactive Publication Date: 2009-12-09
贵州新安航空机械有限责任公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the braking materials of railway freight cars are mostly high-phosphorus cast iron tiles and synthetic brake shoes. During the operation of the train after the speed is increased, its defects are gradually exposed. The friction coefficient decreases, resulting in longer braking distance. Because the cast iron tile has a large specific gravity and hardness and directly brakes on the train wheel, it is easy to cause damage to the wheel tread; and the synthetic brake shoe is easy to cause friction on the wheel tread due to poor heat dissipation. damage or even surface peeling, the metallographic structure of the wheel changes
At the same time, the friction coefficient of the above two brake shoes is also very unstable in rainy and snowy weather conditions, and the friction coefficient decreases sharply during braking, which leads to a significant extension of the braking distance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Freight car compartment powder metallurgy brake block
  • Freight car compartment powder metallurgy brake block
  • Freight car compartment powder metallurgy brake block

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] The powder metallurgy brake shoe of the truck compartment of the present invention is mainly composed of a tile back 4 and four brake blocks 3, the tile back 4 is formed by one-time casting of nodular cast iron or low-carbon cast steel; the brake block 3 is composed of a skeleton 5 and a powder metallurgy friction block 6; The powder metallurgy friction block 6 is made by mixing various powder metallurgy materials evenly in proportion, and after cold pressing, it is heated and pressure-sintered with the skeleton 5; the tile back 4 and the brake block 3 are welded around the rigid back 5 through the welding point 7 to the tile back or riveted together with the tile back through rivet 1 and rivet 2. The powder metallurgy friction block 6 is made of copper powder, tin powder, aluminum powder, molybdenum disulfide powder, graphite powder, alumina, iron powder, etc. according to the following weight ratio:

[0018] Copper powder 2~10 Tin powder 1~7 Aluminum powder 5~11 Molyb...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a powder metallurgy brake shoe for a freight car, which is composed of a tile back (4) and a brake block (3). The tile back material is QT400-18, which is formed by one-time casting. The brake block and the tile back adopt a welding or riveting connection structure , the powder metallurgy friction block (6) on the brake block (3) adopts powder metallurgy friction material: take iron as the matrix, add lead, graphite, molybdenum disulfide, copper, aluminum oxide, etc. , Pressurized sintering. The invention has the characteristics of reliable structure, stable braking friction performance, low surface temperature rise, small dispersion, good wear resistance, etc., and can be applied to the braking of railway freight cars with a speed of 160 km / h and below.

Description

technical field [0001] The invention relates to a brake shoe for a railway vehicle, in particular to a powder metallurgy brake shoe for a carriage of a freight car. Background technique [0002] With the continuous development of the railway science and technology industry, the operating speed of railway trains is constantly increasing, and railway freight cars are developing in the direction of speed-up and heavy load. Therefore, the requirements for braking performance of brake shoes are also getting higher and higher. Not only brake shoes are required to have good Braking performance, and it is required that the brake shoes do not cause abnormal wear and damage to the wheel tread, no material transfer during braking, no harmful substances, and no pollution to the environment. At present, the braking materials of railway freight cars are mostly high-phosphorus cast iron tiles and synthetic brake shoes. During the operation of the train after the speed is increased, its def...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): F16D69/00F16D69/02
Inventor 冯友琴彭旭光范艳芳
Owner 贵州新安航空机械有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products