Agent for cleaning, lustering and protecting surface easy to eliminate and method for producing the same
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A surface cleaning and care agent technology, applied in chemical instruments and methods, polishing compositions, etc., can solve problems such as uneconomical, toxic solvents, and inconvenient use
Active Publication Date: 2010-01-06
北京绿伞科技股份有限公司
View PDF4 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The traditional method is time-consuming and laborious, and the solvent is toxic, flammable and explosive, which is inconvenient and unsafe to use
[0003] Commonly used liquid cleaning and glazing care agents are generally sprayed from aerosol cans. The liquid itself is easy to stratify and has unstable storage performance. It is neither safe nor economical to spray the contents
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0026] Embodiment 1: a kind of surface cleaning polishing care agent that is easy to remove, is prepared by its weight ratio by following raw material:
[0037] Among the above raw materials, silicone oil is an ideal brightener, which can provide good brightening and color enhancing effects; it has good electrical insulation, anti-oxidation, non-volatile, non-corrosive, and non-toxic.
[0038] Chuan wax is used to provide a waxing effect to the hard surface of the utensil, make it smooth, brighten and protect the hard surface of the utensil.
[0039] Paraffin wax can provide a polishing effect on hard surfaces of utensils, and can be used in combination with Sichuan w...
Embodiment 2
[0072] Embodiment 2: In the present embodiment, described raw material is prepared by its following weight ratio:
[0073] Silicone oil 0.2
[0074] Sichuan wax 1.2
[0075] Paraffin 1.2
[0076] Carnauba Wax 1.2
[0077] Stearic acid 2.1
[0078] Triethanolamine 1.5
[0079] Alkylphenol polyoxyethylene ether (4) 0.7
[0080] 1.2 Benzisothiazolin-3-one 0.1
[0081] Fragrance 0.2
[0082] Deionized water 91.6.
[0083] The preparation method of the easy-to-remove surface cleaning and polishing care agent is the same as in Example 1.
Embodiment 3
[0084] Embodiment 3: In the present embodiment, described raw material is prepared by its following weight ratio:
[0085] Silicone oil 3.5
[0086] Sichuan wax 4.5
[0087] Paraffin 4.5
[0088] Carnauba Wax 2.8
[0089] Stearic acid 5.8
[0090] Triethanolamine 3.8
[0091] Alkylphenol polyoxyethylene ether (4) 2.8
[0092] 1.2 Benzisothiazolin-3-one 0.1
[0093] Fragrance 0.2
[0094] Deionized water 72.
[0095] The preparation method of the easy-to-remove surface cleaning and polishing care agent is the same as in Example 1.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
melting point
aaaaa
aaaaa
melting point
aaaaa
aaaaa
Login to View More
Abstract
The invention relates to an easy-erased glazing and protective agent and a preparation method. The invention takes silicon oil, insect wax, paraffine, carnauba wax, stearic acid, trolamine, alkyl phenol polyoxyethylene ether (4), 1.2-benzisothiazdin-3- ketone, essence and de-ionized water as raw materials. In production process, the insect wax, paraffine, carnauba wax and the stearic acid are added to knives barrier emulsified kettle and are heated until reaching from 85 to 88 DEG C; after being hot melted, the raw materials are stirred and then are added with triethanolamine, silicon oil, alkyl phenol polyoxyethylene ether (4) and essence sequentially and stirred evenly. In the process of continuous stirring, the de-ionized water which has a temperature of 85 to 90 DEG C and accounts for from one fifth to two-fifths of the total amount of water is dropped into the emulsified kettle slowly in 30 to 40 minutes, and normal-temperature water is added after phase inversion process of materiels is finished; another 10 minutes is needed for shearing and stirring until all the water are added into the emulsified kettle; the 1.2-benzisothiazdin-3- ketone is added and stirred evenly. At last a nylon screen with 200 meshes is used for filtering, thereby obtaining the easy-erased glazing and protective agent.
Description
technical field [0001] The invention relates to the field of chemical industry, in particular to an easy-to-remove surface cleaning and polishing care agent and a preparation method thereof. Background technique [0002] In people's daily life, all kinds of solid wood, leather, composite floor, marble, granite, furniture, car surface, etc. need to be cleaned, polished and cared for frequently. Usually after removing the dirt with detergent, it is waxed with solid wax, and it can be completed after repeated polishing. When waxing again every time, it is necessary to remove the original wax with solvents such as kerosene before applying new wax. The traditional method is time-consuming and laborious, and the solvent is toxic, flammable and explosive, which is inconvenient and unsafe to use. [0003] Commonly used liquid cleaning and glazing care agents are generally sprayed from aerosol cans. The liquid itself is easy to stratify and has unstable storage performance. It is ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More