Technique for preparing Nano Sn02/Ti02 composite film in use for photovoltaic conversion

A technology for photoelectric conversion and composite film, which is applied in the field of preparation of nano-SnO2/TiO2 composite film for photoelectric conversion, can solve the problems of film sputtering that is not suitable for large area, complicated operation, etc., and achieves low cost, simple process, and photoelectric conversion. improved effect

Inactive Publication Date: 2007-07-25
SHANGHAI UNIV OF ENG SCI
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method can sputter any substance, but due to the need for vacuum and the limitation of the space of the sputtering chamber, the operation is more complicated, and it is not suitable for large-area thin film sputtering

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0028] Preparation of TiO thin film

[0029] (1) Clean the substrate

[0030] Wash the 80mm×60mm×3mm glass substrate with tap water first, then soak it in acetone and ultrasonically clean it for 15 minutes, take it out, wash it with distilled water and soak it for 15 minutes, and finally dry it at 100°C for later use.

[0031] (2) Preparation of sol

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

This invention discloses a method for preparing SnO2 / TiO2 composite nanofilm used for photoelectric conversion. The method comprises: (1) cleaning the substrate; (2) preparing TiO2 sol and SnO2 sol; (3) coating the substrate with a layer of TiO2 sol film, drying, and coating the substrate with a layer of SnO2 sol film; (4) repeating the above procedures to obtain multiple composite film; (5) placing in a muffle furnace, heating, cooling with distilled water, and drying to obtain the composite film. The composite film has low cost and simple process, and better photoelectric conversion property than that of single composition film.

Description

technical field [0001] The invention belongs to the technical field of functional composite thin film materials, and relates to a preparation process of a nanocomposite thin film, in particular to a nano-SnO nanometer for photoelectric conversion. 2 / TiO 2 Preparation process of composite film. Background technique [0002] Due to the excellent optical, electrical and magnetic properties of nano-semiconductor functional films, they have attracted much attention. where TiO 2 Semiconductors are particularly prominent, on the one hand, TiO 2 Abundant sources and large output; on the other hand, due to TiO 2 Non-toxic, stable chemical properties, can be used as a photocatalyst for photolysis of water and photodegradation of organic matter, and can be used as a photoelectrode material for photoelectric conversion. SnO 2 Thin film is also a kind of functional film, which has a wide range of applications in gas sensing, humidity sensing, and optical technology. Nanoization, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C17/25
Inventor 刘继华周细应钱士强
Owner SHANGHAI UNIV OF ENG SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com