High solid content core-shell structure nano acrylic ester micro-emulsion and synthetic method thereof

A technology of acrylate and core-shell structure, applied in the field of chemical polymer materials

Inactive Publication Date: 2012-11-21
上海骏虔实业发展有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004]The above acrylic microemulsions all have a solid content below 45%, and when the solid content is large, the viscosity is high, so that the synthesized microemulsion is The use is limited, the amount of emulsifier is large, and its synthesis is more time-consuming, labor-intensive and energy-consuming than ordinary emulsion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High solid content core-shell structure nano acrylic ester micro-emulsion and synthetic method thereof
  • High solid content core-shell structure nano acrylic ester micro-emulsion and synthetic method thereof
  • High solid content core-shell structure nano acrylic ester micro-emulsion and synthetic method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Embodiment 1 (percentage by weight)

[0045] Core Mixed Monomer (40%) Shell Mixed Monomer (60%)

[0046] Alkyl Acrylate 12% Alkyl Acrylate 30%

[0047] Vinyl aromatic compound 24% Alkyl methacrylate 23%

[0048] Hydroxy Acrylate 1.2% Hydroxy Acrylate 2.8%

[0049] Alkyl Acrylic Acid 1.2% Alkyl Acrylic Acid 1.8%

[0050] AE-100 0.8% AE-100 1.2%

[0051] MPS 0.8% MPS 1.2%

[0052] Core Shell

[0053] Initiator 0.16% Initiator 0.24%

[0054] Water 18% Water 28%

[0055] seed emulsion

[0056] Core mixed monomer 5%

[0057] Non-ionic emulsifier 0.5%

[0058] Anionic emulsifier 2.5%

[0059] Viscosity modifier 0.7%

[0060] Initiator 0.1%

[0061] Water 76%

[0062] Viscosity: 116mpa.s, solid content: 46%, particle size: 70nm (see attached figure 1 ).

Embodiment 2

[0063] Embodiment 2 (percentage by weight)

[0064] Core mixed monomer (50%) Shell mixed monomer (50%)

[0065] Alkyl Acrylate 15% Alkyl Acrylate 28.3%

[0066] Vinyl aromatic compound 30% Alkyl methacrylate 26.7%

[0067] Hydroxyacrylate 1.5% Hydroxyacrylate 1.5%

[0068] Alkyl Acrylic Acid 1.5% Alkyl Acrylic Acid 1.5%

[0069] AE-100 1% AE-100 1%

[0070] MPS 1% MPS 1%

[0071] Core Shell

[0072] Initiator 0.2% Initiator 0.2%

[0073] Water 23% Water 23%

[0074] seed emulsion

[0075] Core mixed monomer 14%

[0076] Non-ionic emulsifier 0.5%

[0077] Anionic emulsifier 2.5%

[0078] Viscosity modifier 0.7%

[0079] Initiator 0.1%

[0080] Water 81%

[0081] Viscosity: 120mpa.s, solid content: 45.1%, particle size: 65nm (see attached figure 2 ).

Embodiment 3

[0082] Embodiment 3 (percentage by weight)

[0083] Core Mixed Monomer (40%) Shell Mixed Monomer (60%)

[0084] Alkyl Acrylate 12% Alkyl Acrylate 30%

[0085] Vinyl aromatic compound 24% Alkyl methacrylate 24%

[0086] Hydroxyacrylate 1.2% Hydroxyacrylate 1.8%

[0087] Alkyl Acrylic Acid 1.2% Alkyl Acrylic Acid 1.8%

[0088] AE-50 0.8% AE-50 0.8%

[0089] MPS 0.8% MPS 0.8%

[0090] Core Shell

[0091] Initiator 0.16% Initiator 0.24%

[0092] Water 18% Water 28%

[0093] seed emulsion

[0094] Core mixed monomer 5%

[0095] Non-ionic emulsifier 0.5%

[0096] Anionic emulsifier 2.5%

[0097] Viscosity modifier 0.7%

[0098] Initiator 0.1%

[0099] Water 65%

[0100] Viscosity: 130mpa.s, solid content: 48.4%, particle size: 65nm (see attached image 3 ).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to chemical polymer materials, which in detail relates to high solid content nanometer microemulsion polymerization with core-shell structure. The granular size is 30-100 nanometer, solid content is 46- 49%, and core mixed monomer is 40-70% of that of total core-shell monomer. The core mixed monomer comprises alkyl acrylate, methacrylate and alkyl methacrylate esters orvinyl aromatic compounds, acrylate-hydroxy ester, alkyl acrylic acid. The shell mixed monomer comprises alkyl acrylate, methacrylate and alkyl methacrylate esters, acrylate-hydroxy ester, alkyl acrylic acid. The proportion of said components are as follows: alkyl acrylate 39-48%, methacrylate and alkyl methacrylate esters 20-53%, vinyl aromatic compounds 0-30%, acrylate-hydroxy ester 3- 4%, alkyl acrylic acid 3- 4%. The invention is characterized by high solid content of more than 45% and reduced viscosity.

Description

Technical field: [0001] The invention belongs to the field of chemical polymer materials, in particular to an acrylate microemulsion with a particle size of 30-100nm and a solid content greater than 45% and a preparation method thereof Background technique: [0002] Microemulsion was first proposed by Hoar and Schulman, it is a thermodynamically stable, optically transparent or translucent dispersion system, its particle size is less than 100nm, while the particle size of the microemulsion is 100-400nm, and the particle size of the ordinary emulsion is generally several Hundreds of nanometers to thousands of nanometers. The application of microemulsion technology to the synthesis and research of water-based polymers began in the early 1980s. As a kind of nanomaterial, nano-polymer particles obtained by microemulsion polymerization have excellent properties different from those under normal conditions, which quickly attracted people's attention. of great attention. [0003]...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F20/10C08F2/24C08F2/38
Inventor 王永法王小兵
Owner 上海骏虔实业发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com