An energy-saving, environment-friendly and functional technology, applied in lubricating compositions, additives, petroleum industry, etc., can solve the problems of durability, high manufacturing cost, uneconomical use, and slow effect in the use process, so as to reduce emissions, save fuel, Enhanced sealing effect

Inactive Publication Date: 2008-02-27
SHANDONG SUN RISES & THE EAST GASOLINEEUM & CHEM CORP
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the commonly used lubricants mainly have many deficiencies and imperfections in the following technical aspects: blanks for the composite use of various solid materials and poo

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Energy-saving environment protecting function type lubricant agent
  • Energy-saving environment protecting function type lubricant agent
  • Energy-saving environment protecting function type lubricant agent

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0051] Example 1:

[0052] Take the 57K6 mineral liquid lubricating oil pretreated by dehydration, pump it into the homogenization kettle all at once, then add 12KG of succinimide dispersant into the kettle after metering, then start stirring and heat up to 60℃, Then add 5KG of molybdenum disulfide powder with a particle size of 300nm and 8KG of graphite powder with a particle size of 500nm into the kettle several times. After the addition, start shearing and dispersion, and control the temperature between 60℃ and 70℃. Circulating cooling water can be used to adjust the temperature. After two hours, 12KG of polymethacrylate adhesive and 6KG of antiwear agent dialkyldithiophosphoric molybdenum oxymolybdenum can be measured and added to the kettle together, and then continue to shear and disperse After two hours, samples can be taken to detect the particle size distribution. When it is qualified, the shearing and dispersion can be stopped, and then the sand mill can be cycled for fo...

Example Embodiment

[0058] Example 2:

[0059] Take 52KG of synthetic liquid lubricating oil pretreated by dehydration, pump it into the homogenization kettle all at once, then add 15KG of succinimide dispersant into the kettle after metering, then start stirring and heat up to 60℃, Then add 6KG of molybdenum disulfide powder with a particle size of 2000nm and 7KG of graphite powder with a particle size of 1500nm into the kettle several times. After adding, start shearing and dispersion, and control the temperature between 60℃-70℃. Circulating cooling water can be used to adjust the temperature. After two hours, 15KG of polymethacrylate adhesive and 5KG of antiwear agent dialkyldithiophosphoric molybdenum oxymolybdenum can be measured and added to the kettle together, and then continue to shear and disperse After two hours, samples can be taken to detect the particle size distribution. When it is qualified, the shearing and dispersion can be stopped, and then the sand mill can be cycled for four hour...

Example Embodiment

[0060] Example 3:

[0061] Take 59KG of mineral liquid lubricant pretreated by dehydration, pump it into the homogenization kettle all at once, then add 10KG of succinimide dispersant into the kettle after metering, then start stirring and heat up to 60℃, Then add 8KG of molybdenum disulfide powder with a particle size of 3000nm and 5KG of graphite powder with a particle size of 2000nm into the kettle several times. After the addition, start shearing and dispersion, and control the temperature between 60℃ and 70℃. Circulating cooling water can be used to adjust the temperature. After two hours, 10KG of polymethacrylate adhesive and 8KG of antiwear agent dialkyldithiophosphoric molybdenum oxymolybdenum are measured and added to the kettle together, and then continue to shear and disperse After two hours, samples can be taken to detect the particle size distribution. When it is qualified, the shearing and dispersion can be stopped, and then the sand mill can be cycled for four hours...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses an energy-saving environment-protective lubricant with lubricating reinforcing and abrasion proof and squeezing proof effect for the lubricating part of kinds of mechanic equipment, which comprises the following parts: 5%-8% molybdenum disulphite with grain size at 30-5000nm, 5%-8% graphite powder with grain size at 30-5000nm, 5%-8% molybdenum oxide dialkyl dithiophosphate as antiwear agent, 10%-15% succinyl imines as dispersant, 10%-15% polymethacrylate ester as adhesive and residual liquid lubricating material. The invention can repair and fill the side-surface abrade by metal automatically to film rapidly and stably, which lengthens the lift of lubricating part of the mechanic equipment by one time and improves the effective efficiency by 4-10%, therefore saving the fuel by 10-15%, reducing the discharge of harmful gas and smoke obviously and the mechanic noise by 1-8 decibel.

Description

technical field [0001] The invention belongs to the technical field of lubricants, and in particular relates to an energy-saving and environment-friendly function that can be used for lubricating parts of various mechanical equipment and can be added to various lubricating oil products to enhance lubrication, anti-wear and anti-extreme pressure effects. type lubricant. technical background [0002] At present, the commonly used lubricants mainly have many deficiencies and imperfections in the following technical aspects: blanks for the composite use of various solid materials and poor instant dissolving effect between products and various lubricating oils, slow effect during use, and stable solid-liquid suspension Persistence, high manufacturing costs, uneconomical use, etc. Contents of the invention [0003] In order to overcome the deficiencies of the above technologies, the present invention provides an energy-saving and environment-friendly functional lubricant, which...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M145/14C10M125/02C10M137/10C10M133/16C10M125/22
Inventor 曹仁忠刘斌
Owner SHANDONG SUN RISES & THE EAST GASOLINEEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap