Modification method for protecting crystal form of grammite

A wollastonite powder and modification technology, which is applied in the treatment of fibrous fillers and dyed polymer organic compounds, can solve the problems of reducing the aspect ratio, affecting the enhancement effect, and breaking the needle-shaped wollastonite, so as to protect the crystal shape Effect

Inactive Publication Date: 2010-09-29
CHINA UNIV OF GEOSCIENCES (WUHAN)
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage of this method is that it will break the acicular wollastonite, reduce the aspect ratio, and affect the reinforcement effect
[0003] There is no report on the surface modification of acicular wollastonite powder by fumigation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The surface modification of acicular wollastonite powder is carried out according to the following steps:

[0016] 1), take by weighing 20 grams of 800 mesh acicular wollastonite powder, and pack in the wire mesh;

[0017] 2), weigh 0.5 grams of surface modifier liquid paraffin according to 2.5% of the mass of acicular wollastonite powder, and add 50 milliliters of ethanol to form a solution;

[0018] 3), put the acicular wollastonite powder packed with wire mesh on the solution;

[0019] 4), heating the solution until the solution evaporates, and fumigate the acicular wollastonite powder until the solution is completely evaporated;

[0020] 5), drying the fumigated acicular wollastonite powder at 70°C to obtain a modified acicular wollastonite powder with an activation rate of 95.2%;

[0021] The activation rate is determined according to the method stipulated in the chemical industry standard HG / T2567-94 of the People's Republic of China.

Embodiment 2

[0023] The surface modification operation steps of the acicular wollastonite powder are the same as in Example 1, except that the surface modifier adopts stearic acid, and the amount of the surface modifier stearic acid is 2.0% of the mass of the acicular wollastonite powder. The wollastonite powder is 325 mesh, and the activation rate of the obtained modified acicular wollastonite powder is 96.1%.

Embodiment 3

[0025] The surface modification operation steps of the acicular wollastonite powder are the same as in Example 1, except that the surface modifier adopts liquid paraffin and stearic acid, and the mass ratio of liquid paraffin to stearic acid is 1: 1. The dosage is 2.5% of the mass of the acicular wollastonite powder, the acicular wollastonite powder is 1250 mesh, and the activation rate of the obtained modified acicular wollastonite powder is 96%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a modifying method for protecting the crystal shape of a vilnite. Surface modification is carried out on the needle vilnite powder by a fumigation way, which comprises the following procedures: solving some surface modifier in a solvent to get a solution, holding the needle vilnite powder by a metallic mesh, erecting the held needle vilnite powder above the solution, risingthe temperature till the solution vaporizes, so that the modifier wraps the needle vilnite powder surface to modify the surface of the powder. The surface modifier used is liquid pertrolin and / or stearic acid, the solvent is alcohol, the amount of the surface modifier is 2.0-2.5% of the needle vilnite powder by mass. The activity of the needle vilnite powder modified by the method is more than 95%. The invention needs not mix the powder, so the crystal shape is protected.

Description

technical field [0001] The invention relates to a method for modifying the surface of inorganic powder, in particular to a method for modifying the surface of acicular wollastonite powder. Background technique [0002] Modified acicular wollastonite powder can be added to plastics, rubber, paint, etc., which can not only reduce costs, but also play a role in strengthening. At present, the surface modification method of acicular wollastonite powder is dry modification: the acicular wollastonite powder and a surface modifier are stirred and kneaded at high speed in a high-speed kneader to achieve surface modification. The disadvantage of this method is that it will break the acicular wollastonite, reduce the aspect ratio, and affect the reinforcement effect. [0003] At present, there is no report on the surface modification of acicular wollastonite powder by fumigation. Contents of the invention [0004] The object of the present invention is to provide a method for surfa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09C3/10C09C1/28
Inventor 张德毕巍
Owner CHINA UNIV OF GEOSCIENCES (WUHAN)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com