Epoxy modified unsaturated resin concrete for road and bridge

A technology of resin concrete and epoxy modification, which is applied in the field of epoxy modified unsaturated resin concrete, can solve problems such as poor bonding effect, hidden dangers of vehicle safety, traffic accidents, etc., save time and effort for maintenance, reduce safety hazards, The effect of enhancing the adhesive force

Inactive Publication Date: 2008-05-28
王军 +2
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This is not only time-consuming and labor-intensive, but also closed traffic for a long time will cause potential safety hazards for vehicles, and traffic jams and traffic accidents are more likely to occur
Use new cement concrete to repair the damaged parts, the bonding effect between them is poor, and it is easy to cause damage again

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Take 220kg of unsaturated resin, 8.8kg of curing agent, 8.8kg of accelerator, 12kg of polyester fiber, 450kg of yellow sand, and 600kg of stone in a stirrer and stir evenly before use. The solidification period is about 1-2 hours. The curing agent and accelerator are compound mixtures. The main component of the curing agent is benzoyl peroxide, and the main component of the accelerator is cobalt isooctanoate. Epoxy-modified unsaturated polyester resin is formed by polycondensation of polybasic acid and polyhydric alcohol, and can be purchased directly from the market.

Embodiment 2

[0014] Take 100kg of unsaturated resin, 0.2kg of curing agent, 0.2kg of accelerator, 0.5kg of polyester fiber, 100kg of yellow sand, and 200kg of stone in a stirrer and stir evenly before use. The solidification period is about 1-2 hours. The curing agent and accelerator are compound mixtures. The main component of the curing agent is benzoyl peroxide, and the main component of the accelerator is cobalt isooctanoate. Epoxy-modified unsaturated polyester resin is formed by polycondensation of polybasic acid and polyhydric alcohol, and can be purchased directly from the market.

Embodiment 3

[0016] Take 100kg of unsaturated resin, 1kg of curing agent, 1kg of accelerator, 5kg of polyester fiber, 500kg of yellow sand, and 1000kg of stone in a stirrer and stir evenly before use. The solidification period is about 1-2 hours. The curing agent and accelerator are compound mixtures. The main component of the curing agent is benzoyl peroxide, and the main component of the accelerator is cobalt isooctanoate. Epoxy-modified unsaturated polyester resin is formed by polycondensation of polybasic acid and polyhydric alcohol, and can be purchased directly from the market.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an epoxy-modified unsaturated resin concrete used in roads and bridges, pertaining to a construction material, which is characterized in that the invention is synthesized by epoxy-modified unsaturated resin, curing agent, accelerant, polyester fiber, yellow sand and stone, and the proportion of the invention is: the unsaturated resin : the curing agent : the accelerant : the polyester fiber : the yellow sand : the stone is equal to 1: (0.002-0.01): (0.002-0.01) : (0.005-0.05) : (1-5) : (2-10). The invention can rapidly maintain damaged cement concrete roads and bridges and achieve or surpass the intensity of the original cement concrete, and strengthen the cohesive force between the epoxy-modified unsaturated resin concrete and the roads and the bridges. Besides, the invention is characterized by simple operation, time and labor saving when in maintenance, high efficiency and low cost and being propitious to reduce the hidden danger of vehicles. The invention is solidified after being stirred for 1-2 hours and achieves or surpasses the intensity of the original cement concrete.

Description

technical field [0001] The invention relates to an epoxy-modified unsaturated resin concrete used for roads and bridges. Background technique [0002] Cement concrete is the main material used in road and bridge structures. After a period of use, cement concrete will naturally be damaged, but it is troublesome to repair. If it is not repaired and continues to be used, it will cause more damage to the cement concrete, and even Damage to roads and bridges. Thereby affecting the safety of vehicles on the road, causing traffic accidents. In the past, the maintenance method after the damage of cement concrete was found was to first seal the traffic part of the damaged part of the cement concrete on the road, then cut the damaged part of the cement concrete neatly with a slotting machine, and then use a jack machine to cut the damaged part of the cement concrete Chisel off, and finally use the well-mixed cement concrete to pour into the damaged part of the cement concrete, and w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/18C04B14/06
CPCC04B2111/0075C04B2111/72C04B28/02
Inventor 王军吴宁翟岷
Owner 王军
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com