Illumination aging resisting polycarbonate/styryl resin composition and preparing method thereof

A technology of styrene-based resin and polycarbonate, which is applied in the field of light-aging-resistant polycarbonate/styrene-based resin composition and its preparation field, can solve problems such as large differences, and achieve low production cost and good light-aging resistance. characteristics, the effect of improving the anti-precipitation ability

Active Publication Date: 2008-07-02
CHONGQNG PRET NEW MATERIAL +2
View PDF2 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But in fact, the highest molecular weight of this macromolecular light stabilizer is only a few thousand, which is still far from the polymer resin base material with a molecular weight of hundreds of thousands in the composite material system. Migration is still inevitable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] Below in conjunction with embodiment, the present invention is described in further detail:

[0034]In the composite material formulations of Examples and Comparative Examples, the polycarbonate is bisphenol A type aromatic polycarbonate. In a preferred embodiment, the weight average molecular weight of the polycarbonate resin of the present invention is 10000-20000 g / mol, and the intrinsic viscosity is 0.3-1.5 deciliter per gram. In the composite material formulations of the examples and comparative examples, the PC resin produced by Dow Company of the United States is selected, and the brand is 201-15. Described styrene base resin is selected from ABS (acrylonitrile-butadiene-styrene copolymer), ASA (acrylate-styrene-acrylonitrile copolymer), SAN (styrene-acrylonitrile copolymer ), HIPS (High Impact Polystyrene) or their blends. In the composite material formulations of this example and the comparative example, the ABS high-glue powder produced by GE Company of the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a polycarbonate / styryl resin composition which has light fastness and aging resistance and a preparation method thereof. The components and mixture ratio (weight proportion) of the composition are that: 50 percent-80 percent of polycarbonate, 10 percent-50 percent of styryl resin, 0.1-5 percent of molecular sieve, 0.1-1.0 percent of antioxidant 168, 0.1-1.0 percent of antioxidant 245, 0.1-2.0 percent of ultraviolet absorber, 0.1-2.0 percent of free radical quencher, etc. The resin composition prepared by the technical proposal of the invention can not only improve the anti-precipitation efficiency of light stabilizer in a composite material system to lead the prepared polycarbonate / styryl resin composition has better light fastness and aging resistance performance, but also has the advantage that all the physical mechanical performances and thermodynamic property of the material are basically not affected; furthermore, the method presented for improving the light fastness and aging resistance of polycarbonate / styryl resin composition has simple preparation technique and low production cost.

Description

technical field [0001] The invention relates to a polycarbonate / styrene-based resin composition resistant to light aging and a preparation method thereof, in particular to improving the stability of light-stabilizing additives in polycarbonate / styrene by adding a molecular sieve with adsorption effect. The anti-precipitation performance in the base resin composition, thereby improving the long-term light aging resistance performance of the polycarbonate / styrene-based resin composition, belongs to the field of polymer modification and processing. Background technique [0002] Polycarbonate and ABS composition has good heat resistance, high impact resistance and excellent processability. This alloy is widely used in auto parts, home appliances and electronic components. The ABS in the composition is synthesized from three chemical monomers of acrylonitrile, butadiene and styrene. Polymerization of the three monomers produces a terpolymer with two phases, a continuous phase o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08K5/3492B29C47/92B29C70/02B29B9/12C08L25/06C08K5/315C08K5/3472C08K5/18B29C48/40B29C48/92B29C48/95
CPCB29C48/92B29C2948/92704B29C48/04B29C48/40B29C2948/92514B29C2948/92561B29C2948/92895B29C48/95
Inventor 张鹰张祥福周文
Owner CHONGQNG PRET NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com