Piezoelectric ceramic fibre containing metal core painted by electrode partly

A technology of piezoelectric fibers and piezoelectric ceramics, applied in piezoelectric devices/electrostrictive devices, piezoelectric/electrostrictive/magnetostrictive devices, circuits, etc. scope and other issues to achieve the effect of overcoming application defects

Active Publication Date: 2008-11-12
NANJING UNIV OF AERONAUTICS & ASTRONAUTICS
View PDF1 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The surface of the existing fiber is all plated with electrode materials, and the parameters in the stretching mode can only be measured along the length direction, that is to sa...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Piezoelectric ceramic fibre containing metal core painted by electrode partly
  • Piezoelectric ceramic fibre containing metal core painted by electrode partly
  • Piezoelectric ceramic fibre containing metal core painted by electrode partly

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Embodiment one: if figure 1 , figure 2 As shown, the piezoelectric fiber containing a metal core of the partially coated electrode of this embodiment includes a metal core 1, a piezoelectric material 2 coated on the metal core 1, and a coated electrode 3 coated on the outer surface of the piezoelectric material 2 , the surface of the piezoelectric material 2 includes a coated electrode portion 3 and an uncoated electrode portion 4, the coated electrode portion 3 is a coated electrode 31, which partially covers the piezoelectric material 2 along the direction in which the piezoelectric fiber containing the metal core extends The surface; Wherein, coating electrode part 3 occupies half of the surface area of ​​piezoelectric material 2;

[0022] The diameter of the metal core 1 is 25 microns, and the material of the metal core 1 is platinum;

[0023] The section of the piezoelectric fiber containing the metal core of the partially coated electrode of this embodiment is ...

Embodiment 2

[0029] like figure 1 , image 3 As shown, the piezoelectric fiber containing a metal core of the partially coated electrode of this embodiment includes a metal core 1, a piezoelectric material 2 coated on the metal core 1, and a coated electrode 3 coated on the outer surface of the piezoelectric material 2 , the surface of the piezoelectric material 2 includes a coated electrode portion 3 and an uncoated electrode portion 4, the coated electrode portion 3 is a coated electrode 31, which partially covers the piezoelectric material 2 along the direction in which the piezoelectric fiber containing the metal core extends The surface; Wherein, the coated electrode part 3 occupies one-third of the surface area of ​​the piezoelectric material 2;

[0030] The piezoelectric fiber containing the metal core of the partially coated electrode of this embodiment, the diameter of the metal core 1 is 10200 microns, and the metal core 1 is made of a high temperature resistant material, such a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a piezoelectric fiber containing a metal core with part coated with an electrode, which comprises a metal core (1), a piezoelectric material (2) coating the metal core (1) and a coating electrode (3) coating the outer surface of the piezoelectric material (2). The surface of the piezoelectric material (2) comprises an electrode coated part (3) and a non electrode coated part (4); the electrode coated part (3) is a coated electrode (31) which partially covers the surface of the piezoelectric material (2) along the extending direction of the piezoelectric fiber containing a metal core. The piezoelectric fiber containing a metal core with part coated with electrode of the invention can realize the driving functions of driving components such as traditional piezoelectric bimorphs, can be used as micro-drivers and for energy recycling and vibration control, and especially can realize the function of bending vibration, thus overcoming the application disadvantages of the existing piezoelectric fibers.

Description

1. Technical field [0001] The invention relates to a piezoelectric fiber, in particular to a piezoelectric fiber containing a metal core. 2. Background technology [0002] Most smart structures adopt the structural form of integrating functional devices and matrix structures. In order to facilitate integration with the structural matrix, this puts forward new requirements for the geometric shape and size of functional components in smart structures. Traditional piezoelectric functional devices are mostly in the form of blocks and sheets. Due to their large volume, they are not easy to integrate with the matrix structure. When embedded in the matrix structure, it will have a great impact on the strength and reliability of the structure, and will also change many properties of the structure. , and even affect the use of the structure and shorten the service life of the structure. Ideal geometries to meet the ease of integration requirements imposed by smart structures are thi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01L41/09H01L41/047
Inventor 裘进浩朱孔军边义祥季宏丽
Owner NANJING UNIV OF AERONAUTICS & ASTRONAUTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap