Acidic coating super two-phase stainless steel electrode
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A duplex stainless steel and coating technology, which is applied in welding medium, welding equipment, welding/cutting medium/material, etc., can solve the problems of difficult ratio of ferrite-austenite phase structure, difficult manufacturing, high strength, etc. Achieve excellent pitting resistance, excellent mechanical properties, and excellent operational performance
Inactive Publication Date: 2008-12-17
LUOYANG SHUANGRUI SPECIAL ALLOY MATERIALS
View PDF0 Cites 30 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
At present, super duplex stainless steel has been widely used in my country's engineering construction. Due to the high strength of super duplex stainless steel welding materials, it is difficult to control the appropriate ferrite-austenite phase structure ratio, and it is very difficult to manufacture. Matching manual welding rod with excellent welding process performance
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0020] The mass percentages of electrode coating composition and content are: rutile 35, potassium feldspar 20, marble 6, phlogopite 1.5, titanium dioxide 5, molybdenum iron 2, metal manganese 2, metal chromium 18, cryolite 2, fluoride rare earth 1.5 , Soda Ash 1.0, Chrome Green 6.
Embodiment 2
[0022] The mass percentages of electrode coating composition and content are: rutile 37, potassium feldspar 17, marble 5, phlogopite 3, titanium dioxide 7, molybdenum iron 3.5, metal manganese 3, metal chromium 13, cryolite 2.5, fluoride rare earth 0.5 , soda ash 0.5, chrome green 8.
Embodiment 3
[0024] The mass percentages of electrode coating composition and content are: rutile 40, potassium feldspar 15, marble 10, phlogopite 1, titanium dioxide 3, molybdenum iron 1.5, metal manganese 3.5, metal chromium 16.5, cryolite 3, fluoride rare earth 1 , soda ash 0.5, chrome green 5.
[0025] One of embodiment effects
[0026] Chemical composition of deposited metal %
[0027]
[0028] Ferrite content in weld metal %
[0029]
[0030] Deposited Metal Mechanical Properties
[0031]
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
tensile strength
aaaaa
aaaaa
Login to view more
Abstract
The invention relates to an acidic coating super duplex stainless steel welding rod and belongs to welding material technology. The invention adopts 2507 duplex stainless steel wires as the welding core; the components and the weight percentages of the components of the welding rod coating are as follows: 30-40 of rutile, 3-7 of titanium dioxide, 15-20 of potash feldspar, 1-3 of phlogopite, 5-10 of marble, 16-20 of metal powder, 0.5-1.5 of rare earth fluoride, 2-3 of cryolite, 5-8 of chrome green, 0.5-1.0 of soda, and 1.5-3.5 of ferroalloy. The welding rod of the invention has the advantages, showed by the test results of manufacturability, metallographic observation, mechanical property and corrosion resistance, that the welding rod has extremely good welding technical property; electric arc is stable during welding, and spattering does not basically exist; the formation of weld joints is good; slag detachability is good; the manipulability of the welding rod is excellent; through metallographic observation, the content of ferrite in the structure of welding joints ranges from 40 percent to 60 percent, and the phase ratio can meet engineering application requirement; the welded welding joint has excellent mechanical property, and tensile strength can be more than 800 MPa; low temperature toughness is good; the stress corrosion resistance and pitting corrosion resistance of the welding joint are excellent.
Description
technical field [0001] The invention belongs to welding material technology, and mainly relates to an acid-coated super duplex stainless steel welding rod. Background technique [0002] Super duplex stainless steel has high strength, good toughness and excellent corrosion resistance, especially excellent in chloride stress corrosion resistance and pitting corrosion resistance, and also has excellent welding performance. Super duplex stainless steel has been widely used in the construction of corrosion-resistant pressure vessels and pipelines, large chemical tankers, and offshore construction facilities. At present, super duplex stainless steel has been widely used in my country's engineering construction. Due to the high strength of super duplex stainless steel welding materials, it is difficult to control the appropriate ferrite-austenite phase structure ratio, and it is very difficult to manufacture. Matching manual welding rod with excellent welding process performance. ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more