Manufacturing method of artificial marble plate adhesive

A technology of marble slabs and manufacturing methods, applied in the direction of adhesive types, ester copolymer adhesives, etc., can solve the problems of inability to achieve seamless splicing, damage to the integrity of the appearance of solid surface materials, etc.

Inactive Publication Date: 2008-12-17
姚志明
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, if ordinary adhesives are used to bond artificial marble slabs, marks will often be left at the interface, which will destroy the integrity of the appearance of the solid surface material and cannot achieve seamless splicing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] With 34kg of unsaturated polyester resin, 63kg of 400 mesh aluminum hydroxide, 1.1kg of carbon black, 0.5kg of accelerator cobalt liquid, 0.8kg of curing agent, mixing, pouring and leveling, after curing, the material block is broken into 200 mesh particles, as Available in black color.

[0017] With 34kg of unsaturated polyester resin, 63kg of 400 mesh aluminum hydroxide, 2.5kg of titanium dioxide, 0.5kg of accelerator cobalt liquid, 0.8kg of curing agent, mixing, pouring and leveling, after curing, the block is broken into 200 mesh particles, as Available in white color.

[0018] Mix 95kg of unsaturated polyester resin, 1.5kg of white color particles, 0.3kg of black color particles, 1.0kg of green pigment, 0.5kg of accelerator cobalt liquid, and 0.8kg of curing agent to make an emerald green artificial marble board adhesive .

Embodiment 2

[0020] With 40kg of unsaturated polyester resin, 70kg of 400 mesh aluminum hydroxide, 1.2kg of carbon black, 0.6kg of accelerator cobalt liquid, 0.9kg of curing agent, mixing, pouring and leveling, after curing, the material block is broken into 200 mesh particles, as Available in black color.

[0021] With 40kg of unsaturated polyester resin, 68kg of 400 mesh aluminum hydroxide, 2.5kg of titanium dioxide, 0.5kg of accelerator cobalt liquid, 0.8kg of curing agent, mixing, pouring and leveling, after curing, the block is broken into 200 mesh particles, as Available in white color.

[0022] Mix 95kg of unsaturated polyester resin, 1.5kg of white color particles, 0.1kg of black color particles, 1.0kg of orange pigment, 0.5kg of accelerator cobalt liquid, and 0.8kg of curing agent to make a light orange artificial marble slab adhesive.

Embodiment 3

[0024] With 40kg of unsaturated polyester resin, 68kg of 400 mesh aluminum hydroxide, 2.5kg of titanium dioxide, 0.5kg of accelerator cobalt liquid, 0.8kg of curing agent, mixing, pouring and leveling, after curing, the block is broken into 200 mesh particles, as Available in white color.

[0025] 95kg of unsaturated polyester resin, 1.5kg of white colored particles, 1.0kg of brown pigment, 0.5kg of accelerator cobalt liquid, and 0.8kg of curing agent are mixed to make a brown artificial marble slab adhesive.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a manufacturing method of a scagliola adhesive, which is characterized in that: the manufacturing method comprises the steps as follows: (1) manufacturing color master batch: calculated by weight, 60 pbw (parts by weight) to 75 pbw of aluminum hydroxide, 25 pbw to 40 pbw of unsaturated polyester resin, 0 pbw to 15 pbw of toner, 0.5 pbw to 4 pbw of curing agent are taken, mixed and cast for curing and then the obtained lump material is crashed; (2) preparing by mixing: 75 pbw to 99 pbw of acrylate resin high molecular polymer, 0 pbw to 8 pbw of color paste and 0.1 pbw to 25 pbw of the color master batch are taken and mixed so as to obtain the scagliola adhesive. The manufacturing method of the invention introduces the color master batch structure resembling the structure of the scagliola to the adhesive, thus ensuring the color to be the same as that of scagliola boards after re-bonding and joints to have the same visual effects as the scagliola boards.

Description

technical field [0001] The invention describes a method for the manufacture of an adhesive for artificial marble slabs. Background technique [0002] The solid plate made of aluminum hydroxide and unsaturated polyester resin as the main raw materials has various colors, has the appearance and texture of natural granite, and has the machinability of synthetic materials. It is widely used in the field of architectural decoration and is known as artificial marble slab. [0003] However, if ordinary adhesives are used to bond artificial marble slabs, traces will often be left at the interface, which will destroy the integrity of the appearance of the solid surface material and cannot achieve seamless splicing. Contents of the invention [0004] The object of the present invention is to solve the above problems, and to provide a method for manufacturing an adhesive for artificial marble slabs, which can produce an adhesive that can meet the bonding requirements of artificial m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J133/08C08L67/06C08K3/22C08J5/18
Inventor 姚志明
Owner 姚志明
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com