Method for improving baking finish hardenability of AA6022 aluminum alloy sheet
A technology of aluminum alloy plate and paint hardening, which is applied in the field of aluminum alloy heat treatment, can solve the problems of low strength, achieve the effects of impact resistance, broad market prospect, and increase the stamping yield
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0016] Example 1
[0017] The alloy composition is 1.25% Si, 0.48% Mg, 0.02% Cu, 0.1% Mn, 0.12% Fe, 0.1% Cr, 0.25% Zn, 0.15% Ti, and the balance is AA6022 aluminum alloy ingot of Al. After the homogenization treatment at 480℃×8h+550℃×12h in the circulating air furnace, the sheet is cut and milled, hot-rolled and finally cold-rolled to 1mm; After parking for 10h, heat treatment at 75℃×8h in a circulating air furnace, and then for 1 month at room temperature, perform tensile and cupping tests, simulating 175℃×30min baking paint heat treatment is carried out in an oil bath furnace of.
Example Embodiment
[0018] Example 2
[0019] The alloy composition is 1.25% Si, 0.48% Mg, 0.02% Cu, 0.1% Mn, 0.12% Fe, 0.1% Cr, 0.25% Zn, 0.15% Ti, and the balance is AA6022 aluminum alloy ingot of Al. After the homogenization treatment at 480℃×8h+550℃×12h in the circulating air furnace, the sheet is cut and milled, hot-rolled and finally cold-rolled to 1mm; Immediately conduct heat treatment at 70°C x 30min in a circulating air furnace, and then perform tensile and cupping tests after parking at room temperature for 1 month, simulating 175°C x 30min baking paint heat treatment is performed in an oil bath furnace.
Example Embodiment
[0020] Example 3
[0021] The alloy composition is 1.25% Si, 0.48% Mg, 0.02% Cu, 0.1% Mn, 0.12% Fe, 0.1% Cr, 0.25% Zn, 0.15% Ti, and the balance is AA6022 aluminum alloy ingot of Al. After the homogenization treatment at 480℃×8h+550℃×12h in the circulating air furnace, the sheet is cut and milled, hot-rolled and finally cold-rolled to 1mm; After parking for 3 days, heat treatment at 100°C × 6h in a circulating air furnace, and then at room temperature for 1 month to perform tensile and cupping tests. The heating treatment of the paint simulating 175°C × 30min is carried out in an oil bath furnace. of.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap