Method for solidifying nature rubber latex with microwave radiation

A technology of natural rubber emulsion and microwave radiation, which is applied in the field of natural rubber rubber production, can solve problems such as complex processes, easy pollution of the environment, and sandwiching raw rubber, and achieve the effects of simple production process, economical and efficient production, and high production recovery rate

Inactive Publication Date: 2010-09-29
廖芸 +6
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the diversity of microorganisms, natural coagulation or biological coagulation still has problems such as odor, swelling, too soft or too hard clot, and raw rubber, and is greatly affected by natural conditions such as temperature, strain, etc. The production process and product quality The consistency is not easy to control
[0004] The natural rubber emulsion is centrifuged, concentrated and separated to obtain concentrated latex and skim. Due to the high concentration of ammonia and low dry rubber content in the skim, currently the coagulation of the skim is usually coagulated with sulfuric acid. Therefore, the skim wastewater contains a high concentration Sulfate ions and ammonia ions are easy to pollute the environment, and the treatment of glue clear wastewater requires more complicated processes and higher costs to meet the standards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Get dry glue content and be 28% fresh natural rubber latex 1Kg in the beaker, adopt frequency to be 2450MHZ, power be that the microwave radiation treatment latex of 600W occurs flocculation in 30 seconds, ripening 2 hours forms the clot without white water. After the clot is extruded, dehydrated, granulated and dried, the quality index and performance of the dry glue are determined.

[0022] Quality indicators and performance: impurity content is 0.015%, plastic initial value P0 is 40, plastic retention rate PRI is 85%, nitrogen content is 0.55%, ash content is 0.3%, Mooney viscosity is 80 units; vulcanization time of pure rubber formula -90 is 7 minutes, the tensile strength is 27.5 MPa, and the elongation at break is 900%.

Embodiment 2

[0024] Take 1Kg of fresh natural rubber latex with dry glue content of 32% in a beaker, adopt frequency to be 915MHZ, power be 900W microwave radiation to coagulate the latex for 25 seconds to appear flocculation, slaking for 2 hours to form no white water clot. After the clot is extruded, dehydrated, granulated and dried, the quality index and performance of the dry glue are determined.

[0025] Quality indicators and performance: impurity content is 0.018%, plastic initial value P0 is 40, plastic retention rate PRI is 86%, nitrogen content is 0.56%, ash content is 0.3%, Mooney viscosity is 81 units; vulcanization time of pure rubber formula -90 is 6.8 minutes, the tensile strength is 27.5MPa, and the elongation at break is 880%.

Embodiment 3

[0027] Take 1Kg of fresh latex with a dry glue content of 30% in a beaker, and use a long enough rubber tube to make the latex flow through a microwave radiation field with a frequency of 915MHZ and a power of 900W. When the latex flocculates for more than 20 seconds, collect the microwave The flocculated gel emulsion in the field was matured for 2 hours to form no white water clot. After the clot is extruded, dehydrated, granulated and dried, the quality index and performance of the dry glue are determined.

[0028] Quality indicators and performance: impurity content is 0.016%, plastic initial value P0 is 40, plastic retention rate PRI is 83%, nitrogen content is 0.55%, ash content is 0.3%, Mooney viscosity is 80 units; vulcanization time of pure rubber formula -90 is 6.8 minutes, the tensile strength is 27.5MPa, and the elongation at break is 890%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for solidifying nature rubber latex with microwave radiation, which is characterized in that nature rubber latex is radiated by microwave under the flowing or static sThe invention discloses a method for solidifying nature rubber latex with microwave radiation, which is characterized in that nature rubber latex is radiated by microwave under the flowing or static state to obtain flocculent gel, the flocculent gel is solidified and cured to obtain curds, and the curds are pressed to be thinned, dehydrated, granulated and dried. The invention has simple productiotate to obtain flocculent gel, the flocculent gel is solidified and cured to obtain curds, and the curds are pressed to be thinned, dehydrated, granulated and dried. The invention has simple production technology and low cost, realizes the full rubber latex solidification with no chemical substances added to ensure that all the substances in the rubber latex are not influenced by the chemical actin technology and low cost, realizes the full rubber latex solidification with no chemical substances added to ensure that all the substances in the rubber latex are not influenced by the chemical action, preserves the water insoluble components in the rubber latex, keeps high performance of the product, has good quality and high production recovery ratio, and is green and environmentally-friendlyon, preserves the water insoluble components in the rubber latex, keeps high performance of the product, has good quality and high production recovery ratio, and is green and environmentally-friendlyand high efficient and economical in production.and high efficient and economical in production.

Description

technical field [0001] The invention belongs to the technical field of natural rubber rubber production, and in particular relates to a method for coagulating natural rubber emulsion by microwave radiation. Background technique [0002] In addition to rubber hydrocarbons and water, natural rubber emulsion also contains a large amount of non-colloidal substances such as proteins, lipids, organic acids and sugars. The rubber particles in the natural rubber emulsion are protected by an electric double layer composed of hydrophilic substances such as proteins and lipids, so that the natural rubber emulsion can maintain a stable colloidal state. The natural rubber emulsion is contaminated by microorganisms, or adding acid, inorganic salt, heating, freezing, radiation, etc. can cause the rubber emulsion to lose stability and solidify or gel. At present, the coagulation methods of natural rubber emulsion are mainly chemical and biological methods. One is a chemical method, that i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08C1/14
Inventor 廖芸廖建和赵艳芳廖双泉王桂春王向前陈永平
Owner 廖芸
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com