Ceramic decorative material, ceramic decoration and ceramic decoration method thereof
A technology of ceramics and ceramic glaze, applied in the field of ceramic decoration, can solve the problems of difficult realization, high protrusion, poor three-dimensional effect, etc., and achieve the effects of simple operation, good three-dimensional effect and strong artistic beauty.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0035] Example 1
[0036] The weight fraction of each component of ceramic decoration materials is: SiO 2 30~50%; B2O3 5~20%; Al 2 O 3 1~10%; Na 2 O 0~10%; K 2 O 0~8%; Li 2 O 0~8%; PbO 0~45%; ZnO; 0~20%; CaO 0~5%; BaO 0~5%; MgO 0~5%; SrO 0~5%; La 2 O 3 0~3%; of which: alkali metal Na 2 O, K 2 O, Li 2 The sum of the weight fraction of O is 6-12%, the sum of the weight fraction of alkaline earth metals CaO, BaO, MgO, and SrO is 4-8%; the expansion coefficient of the decoration material is 40-65×10 -7 In between, the baking temperature is between 800°C and 900°C. First make a steel or plastic mold, such as the diameter of the upper base is 2 mm, the diameter of the lower base is 4 mm, and the height of the tapered column hole is 3.5 mm. Then add the powder ceramic decoration material into the mold hole, and use the corresponding steel The male mold is ejected after being pressed and adhered to the ceramic glaze; the temperature is evenly raised for 2 hours, and the temperature is bak...
Example Embodiment
[0037] Example 2
[0038] The weight fraction of each component of ceramic decoration materials is: SiO 2 30~50%; B2O3 5~20%; Al 2 O 3 1~10%; Na 2 O 0~10%; K 2 O 0~8%; Li 2 O 0~8%; PbO 0~45%; ZnO; 0~20%; CaO 0~5%; BaO 0~5%; MgO 0~5%; SrO 0~5%; La 2 O 3 0~3%; of which: alkali metal Na 2 O, K 2 O, Li 2 The sum of the weight fraction of O is 6-12%, the sum of the weight fraction of alkaline earth metals CaO, BaO, MgO, and SrO is 4-8%; the expansion coefficient of the decoration material is 40-65×10 -7 In between, the baking temperature is between 800°C and 900°C. The ceramic decoration material and the printing ink are adjusted into a paste at 10:4, pressed into a pre-made steel or plastic mold, and adhered to the ceramic glaze after demolding. The temperature is evenly raised for 3 hours. Bake at a constant temperature of 800°C for 10 minutes and cool naturally to form a hemispherical bulge of uniform size. The protrusions can be transparent, white, gold, or other colors, or have a ...
Example Embodiment
[0039] Example 3
[0040] The weight fraction of each component of ceramic decoration materials is: SiO 2 30~50%; B2O3 5~20%; Al 2 O 3 1~10%; Na 2 O 0~10%; K 2 O 0~8%; Li 2 O 0~8%; PbO 0~45%; ZnO; 0~20%; CaO 0~5%; BaO 0~5%; MgO 0~5%; SrO 0~5%; La 2 O 3 0~3%; of which: alkali metal Na 2 O, K 2 O, Li2 The sum of the weight fraction of O is 6-12%, the sum of the weight fraction of alkaline earth metals CaO, BaO, MgO, and SrO is 4-8%; the expansion coefficient of the decoration material is 40-65×10 -7 In between, the baking temperature is between 800°C and 900°C. The ceramic decoration material and the printing ink are adjusted into a paste at 10:10, just like writing and drawing, through a small round mouth continuously and uniformly moving and squeezing the dots on the ceramic glaze, and the temperature is evenly raised for 5 hours. Bake at a constant temperature of 800°C for 10 minutes and cool naturally to form a smooth and convex pattern. The smooth and convex pattern can be tran...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap