Method for embedding thermoplastic material into metal material

A technology of thermoplastic materials and metal materials, applied in the direction of metal material coating process, etc., can solve the problems of peeling off, inability to use for a long time, and inability to tightly bond thermoplastic resins, etc., to achieve effective treatment effects

Inactive Publication Date: 2010-01-13
CHENMING MOLD IND CORP
View PDF1 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Since the surface of the above-mentioned aluminum alloy has no holes or the holes are too shallow, it is impossible to tightly bond the thermoplastic resin to t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for embedding thermoplastic material into metal material
  • Method for embedding thermoplastic material into metal material

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0016] See figure 1 , figure 1 It is a flowchart of an embodiment of a method for embedding a thermoplastic substance into a metal material according to the present invention. in figure 1 In the method, the method for embedding the thermoplastic substance into the metal material includes the following steps:

[0017] First, in step S11, a single acidic or mixed acidic solution, an aqueous hydroxide solution, and high-temperature water at 50°C to 120°C are provided. The metal material can be one of aluminum stampings or aluminum materials. The thermoplastic material may be a thermoplastic resin compound, and the thermoplastic resin compound is one of a combination of polyphenylene sulfide components and a combination of polybutylene terephthalate components.

[0018] Next, in step S12, a single acid or a mixed acid solution is used to clean the metal material by means of a high-pressure water curtain to corrode the metal material, so that multiple holes are formed on the surface of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for embedding a thermoplastic material into a metal material, which comprises the following steps: providing single-acid or mixed-acid solution, water solution of hydroxide and high temperature water with a temperature between 50 and 120 DEG C; utilizing the single-acid or mixed-acid solution to corrode the metal material to produce a plurality of holes on the surface of the metal material; washing the metal material repeatedly with the water solution of hydroxide and continuing to corrode the interiors of the plurality of holes by providing current to the metal material; and then washing the metal material with the high temperature water to produce an oxide film on the metal material, molding the thermoplastic material on the metal material by injection, and combining the thermoplastic material and the metal material into a whole by injecting the thermoplastic material deeply into the plurality of holes.

Description

technical field [0001] The invention relates to a method for embedding thermoplastic substances in metal materials, in particular to a method for repeatedly using aqueous hydroxide solution to clean metal materials and using electric current to corrode metal materials so that thermoplastic substances are embedded in metal materials. Background technique [0002] It is a well-known fact in the industry that the material of ordinary aluminum alloy is relatively soft and not wear-resistant. Therefore, based on the aforementioned characteristics, in order to make the aluminum alloy practically usable, special processing is required during manufacture, and then an oxide film is formed after baking, and finally resin is injected on the surface of the aluminum alloy. [0003] Since the above-mentioned aluminum alloy has no holes or the holes are too shallow, it is impossible to tightly bond the thermoplastic resin to the metal material. Therefore, the thermoplastic resin and metal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29C70/84C23F17/00C23C22/05C25F3/04B29K101/12B29K81/00B29K67/00B29K705/02
Inventor 杜柏桢范淑惠
Owner CHENMING MOLD IND CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap