Artificial stone with photocatalysis

A technology of artificial stone and photocatalyst, which is applied in the direction of manufacturing tools, mixing operation control, chemical instruments and methods, etc., can solve the problems of reducing the strength of finished product materials, high cost, and increased manufacturing cost of finished products, so as to improve the curing speed and production cost. The effect of low and high yield

Inactive Publication Date: 2012-01-11
上海贵雅橱柜有限公司 +1
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Chinese patent CN1453301A reports a method for integrally mixing luminous and light-storing materials in solid surface artificial stone materials, but there are defects such as insufficient hardness, single variety, inability to be used as floor tiles, large amount of luminescent particles, and high cost
The amount of resin used in this patent is relatively large, which will reduce the strength of the finished material; at the same time, it emphasizes the addition of silver and zinc ion antibacterial agents to achieve antibacterial effects by continuously releasing metal ions. Using precious metal ions as antibacterial agents will make the finished product Increased manufacturing cost; and its antibacterial effect will gradually weaken with the release of metal ions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Artificial stone with photocatalysis
  • Artificial stone with photocatalysis
  • Artificial stone with photocatalysis

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Example 1: The production process of luminous environmental protection artificial quartz stone plate. Take the total weight of raw materials as 1kg as an example. Raw material ratio as shown in Table 1

[0031] Ratio of raw materials in table 1 embodiment 1

[0032]

[0033]

[0034] Weigh 3 grams of color paste, 10 grams of luminescent powder, and 10 grams of photocatalyst, add them to 140 grams of resin, stir evenly, then add 120 grams of 325-mesh quartz sand, stir well, and then adjust the order from large to small according to the number of meshes. Add quartz of other meshes in sequence. After each addition of quartz, it needs to be fully stirred. Finally, add accelerator and curing agent. After stirring quickly and evenly, the raw material for board making is obtained, and poured into the board making mold. Send the mold into the vacuum box for vacuuming. When the air pressure reaches -0.1MPa, keep it for about 8 minutes, then take out the mold, and sprinkl...

Embodiment 2

[0036] Example 2: The production process of artificial quartz stone plates containing luminous particles, taking the total weight of raw materials as 1kg as an example. The ratio of raw materials is shown in Table 2.

[0037] Raw material proportioning in table 2 embodiment 2

[0038]

[0039]

[0040] The first is the process of making luminous particles: 40g of unsaturated resin, 25g of light-storing luminescent powder, 30g of aluminum hydroxide powder, 0.4g of accelerator, 0.4g of curing agent, fully stirred, mixed evenly, poured into the mold, and Put the mold into the vacuum box for vacuuming, keep it out of the box for 3 to 5 minutes under the condition that the vacuum degree reaches -0.1MPa, leave it at room temperature for a period of time, make it completely solidified, and then crush and sieve to obtain 20-40 Purpose luminous powder particles. Take 30 grams of 20-40 mesh luminous powder particles and mix them with 250 grams of 20-40 mesh quartz stones for lat...

Embodiment 3

[0041]Embodiment 3: Characterization of photocatalytic effect (taking the effect of decomposing acetaldehyde as an example).

[0042] Grind the prepared artificial stone into a 10cm×10cm×1cm plate, first measure its initial mass m 1 , and then put it into a closed transparent container with a volume of 860ml, and inject 1ml of 40% acetaldehyde solution, absorb it in a dark environment for 2 hours, and measure the mass of the plate in m 2 , and then placed the reactor in the sunlight for 1 hour to carry out the photocatalytic reaction, and the mass of the plate was measured m 3 , and finally re-placed in a dark environment to continue the photocatalytic reaction for 1 hour under the action of its own night light, and its mass m was measured 4 . It can be known that the mass of acetaldehyde adsorbed by the plate sample is (m 2 -m 1 ), the mass of acetaldehyde decomposed by photocatalysis under sunlight irradiation is (m 2 -m 3 ), the mass of acetaldehyde that continues to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of an artificial stone, in particular to a preparation method of an artificial quartz stone with noctilucent function. The artificial quartz stone comprises raw materials containing natural quartz sand, unsaturated resin, accelerator, coupling agent and curing agent, a defined amount of color paste, fluorescent powder and photocatalyst. The artificialstone of the invention has the functions of decoration and indication, has broad-spectrum antibacterial property, can degrade organic pollutants in ambient environment, can remove the waste gas such as nitric oxide and the like, etc.

Description

technical field [0001] The present invention relates to a preparation method of artificial stone, especially a preparation method of artificial quartz stone with luminous function at the same time. Composition of color paste and phosphor. Background technique [0002] Artificial stone is a new type of decorative material formed by mixing natural stone or stone powder with resin and curing. At present, various artificial stone varieties have been disclosed in the market and related technologies. [0003] Chinese patent CN1453301A reports a method for integrally mixing luminescent and light-storing materials in solid surface artificial stone materials, but there are defects such as insufficient hardness, single variety, inability to be used as floor tiles, large amount of luminescent particles, and high cost. [0004] Chinese invention patent application 200810214635.6 discloses a preparation process of artificial quartz stone. The material of this technology contains 0-90% ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B28B1/14B28C7/04B28C5/00B28B11/24B28B11/08C04B26/04C04B14/06
Inventor 吴秋荣肖昉王育华刘斌李艳琴
Owner 上海贵雅橱柜有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com