Extrusion rolling composite method for producing copper clad aluminum row

A copper-clad aluminum strip, rolling and compounding technology, applied in metal rolling, metal rolling, rolling mill control devices, etc., can solve the problem of low total processing rate, fracture of cladding layer and core material, reduction of yield and electrical conductivity and other problems, to achieve the effect of reducing production costs, saving limited resources, and saving copper resources

Inactive Publication Date: 2011-04-20
厦门火炬特种金属材料有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The problems of the above various processes are: the cleanliness of the billet is very high, the total processing rate from the wire billet to the finished product is low, and multiple annealing is required. Due to the large difference in mechanical properties between copper and aluminum, it is easy to Lead to defects such as local cracking of the interface, fracture of the cladding layer and the core material during the drawing process with a small processing rate, resulting in a decrease in yield and conductivity
However, casting liquid metal is prone to defects such as pores, looseness, uneven composition, coarse grains, and thermal stress.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Extrusion rolling composite method for producing copper clad aluminum row
  • Extrusion rolling composite method for producing copper clad aluminum row

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Embodiment 1: 1. select the copper pipe with uniform wall thickness and the aluminum rod that is transitionally matched with the copper pipe inner wall size, then soak the copper pipe and aluminum rod with 15wt%~30wt% sulfuric acid solution, after soaking for a period of time, rinse with clear water After rinsing and drying, brush the inner wall of the copper tube and the outer wall of the aluminum rod with a steel brush to remove impurities and oxide layers on the surface. ②Press the above-mentioned aluminum rod into the copper tube, and seal both ends tightly with the ends of the copper tube to make a composite billet; then heat the composite billet to 300°C, keep it warm for 60 minutes, and preheat the extrusion die to 300°C , keep warm for 30 minutes, and then extruded into copper-clad aluminum row. ③Heat the above-mentioned composite billet to 540°C, keep it warm for 30 minutes, preheat the rolls to 300°C, keep it warm for 30 minutes, and carry out rolling. First,...

Embodiment 2

[0017] Embodiment 2: 1. select the copper pipe with uniform wall thickness and the aluminum rod that is transitionally matched with the copper pipe inner wall size, then soak the copper pipe and the aluminum rod with 15wt%~30wt% sulfuric acid solution, after a period of soaking time, rinse with clear water After rinsing and drying, brush the inner wall of the copper tube and the outer wall of the aluminum rod with a steel brush to remove impurities and oxide layers on the surface. ②Press the above-mentioned aluminum rod into the copper tube, and seal both ends tightly with the ends of the copper tube to make a composite billet; then heat the composite billet to 480°C, keep it warm for 50 minutes, and preheat the extrusion die to 300°C , keep warm for 30 minutes, and then extruded into copper-clad aluminum row. ③Heat the above-mentioned composite billet to 400°C, hold it for 40 minutes, preheat the rolls to 300°C, hold it for 30 minutes, and carry out rolling. First, two passe...

Embodiment 3

[0018] Embodiment 3: 1. select the copper pipe with uniform wall thickness and the aluminum rod that is transitionally matched with the copper pipe inner wall size, then soak the copper pipe and aluminum rod with 15wt%~30wt% sulfuric acid solution, after soaking for a period of time, rinse with clear water After rinsing and drying, brush the inner wall of the copper tube and the outer wall of the aluminum rod with a steel brush to remove impurities and oxide layers on the surface. ②Press the above-mentioned aluminum rod into the copper tube, and seal both ends tightly with the ends of the copper tube to make a composite billet; then heat the composite billet to 540°C, keep it warm for 30 minutes, and preheat the extrusion die to 300°C , keep warm for 30 minutes, and then extruded into copper-clad aluminum row. ③Heat the above-mentioned composite billet to 300°C, keep it warm for 60 minutes, preheat the rolls to 200°C, keep it warm for 30 minutes, and carry out rolling. First,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an extrusion rolling composite method for producing a copper clad aluminum row, which comprises the following steps: 1, selecting a copper pipe with uniform wall thickness and an aluminum bar in transition fit with the inner wall of the copper pipe, and cleaning the copper pipe and the aluminum bar to remove oil stains and oxidation layers; 2, pressing the aluminum bar into the copper pipe to form a composite blank, heating the composite blank to between 400 and 540 DEGC, preserving the heat for 30 minutes, and then extruding the composite blank to form a copper clad aluminum row semi-finished product through a horizontal extruder; 3, heating the semi-finished product to between 300 and 540 DEG C, preserving the heat for 30 to 60 minutes, and then thermally rollingand coldly rolling the semi-finished product; 4, straightening and acid-washing the semi-finished product; 5, carrying out diffusion treatment for the copper clad aluminum row at the temperature of between 200 and 550 DEG C under the protection of nitrogen of one atmospheric pressure, and preserving the heat for 1 to 3 hours; and 6, drawing the copper clad aluminum row to form a final product. The extrusion rolling composite method for producing the copper clad aluminum row not only has short process flow and high production efficiency, but also can save limited resources and reduce the cost.

Description

technical field [0001] The invention relates to a production method of a copper-clad aluminum bar. The copper-clad aluminum bar is a kind of metal composite material used for conducting large currents, especially for connecting multi-phase power sources. Background technique [0002] At present, copper-clad aluminum bar is a new type of bimetal composite material, which is economical and applicable, green and environmentally friendly, and saves copper resources. It is an ideal material to replace the existing copper bar. About 10,000 tons, as my country gradually becomes the manufacturing center of electronics, daily consumer goods and electrical products in the world, the demand for copper-clad aluminum bars in the domestic market will continue to grow, and it is expected to reach 150,000 to 200,000 tons within five years . This product is manufactured with unique technology and has good mechanical and electrical properties. It is widely used in the connecting line bar of el...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01B13/00B21D3/00B21C23/22H01B5/02B21B1/38B21B37/00
Inventor 李彦利沈健于隆祥朱明胡捷舒旭东曹代河金其坚盛文李子睿
Owner 厦门火炬特种金属材料有限公司