Sole material for insulating labor protection shoes
A technology for shoe sole materials and safety shoes, applied in shoe soles, organic insulators, plastic/resin/wax insulators, etc., can solve problems such as low insulation capacity and difficulty in meeting safety protection requirements, meet high insulation requirements, and have a reasonable composition ratio Effect
Inactive Publication Date: 2010-03-10
JIANGSU PROVINCE PAIDENG SHOES IND
View PDF0 Cites 15 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0002] The rubber soles of existing insulated labor insurance shoes generally have low insulation capacity. Usually, under the condition of power frequency voltage 20kv and duration of 1min, the leakage current is greater than 1.8mA, which is difficult to meet the higher safety protection requirements.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0006] The composition and weight ratio of the sole material of the insulated labor protection shoes of the embodiment of the present invention are: 29.2 parts of natural rubber, 29.2 parts of styrene butadiene rubber, 0.96 parts of sulfur, 0.67 parts of accelerator DM, 0.2 part of accelerator TMTD, and zinc oxide 4.3 parts, white carbon black 20.5 parts, magnesium oxide 14.6 parts, stearic acid 0.5 parts. The above components are conventionally mixed, rubberized, vulcanized, and molded into shoe sole products.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Login to view more
Abstract
The invention relates to a material for manufacturing a labor protection article, in particular to a sole material for insulating labor protection shoes with insulating protection function. The material comprises the following components in portion by weight: 26.2 to 31.2 portions of natural rubber, 26.2 to 30.2 portions of styrene-butadiene rubber, 0.93 to 1.02 portions of sulfur, 0.6 to 0.73 portion of accelerating agent DM, 0.18 to 0.22 portion of accelerating agent TMTD, 4 to 4.5 portions of zinc oxide, 20 to 22.5 portions of white carbon black, 14.3 to 15.2 portions of magnesium oxide, and 0.48 to 0.52 portion of stearic acid. The components of the material are mixed reasonably; and actual detections show that the leakage current of a sole product manufactured by adopting a componentformula of the material is smaller than 1.8 mA under the condition that the temperature is 20+/-5 DEG C, the relative humidity is less than 85 percent, the power frequency testing voltage is 20 kv andthe duration is 1 minute, and thus the material can meet high insulating use requirements.
Description
Technical field [0001] The invention relates to a material for manufacturing labor protection products, in particular to a sole material for insulating labor protection shoes with insulation protection function. Background technique [0002] The rubber soles of current insulated labor protection shoes generally have low insulation capabilities. Usually, under the conditions of a power frequency voltage of 20kv and a duration of 1min, the leakage current is greater than 1.8mA, which is difficult to meet the higher safety protection requirements. Summary of the invention [0003] The technical problem to be solved by the present invention is to provide a sole material for insulating labor protection shoes with strong insulating ability. [0004] The composition and weight ratio of the sole material of the insulated labor protection shoes of the present invention are: natural rubber 26.2-31.2 parts, styrene butadiene rubber 26.2-30.2 parts, sulfur 0.93-1.02 parts, accelerator DM0.6-0.7...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L9/06C08K13/02A43B13/04H01B3/30C08K3/06C08K5/47C08K5/40C08K3/22C08K3/36
Inventor 姚广鹏
Owner JIANGSU PROVINCE PAIDENG SHOES IND
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap