Bi-component room temperature vulcanizing silicone rubber for photovoltaic component
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A room temperature vulcanization and photovoltaic module technology, applied in the field of silicone rubber, can solve the problems of poor anti-aging performance, affecting efficiency, slow curing speed, etc., achieve good bonding performance, fast curing speed, improve high temperature resistance and damp heat aging resistance Effect
Inactive Publication Date: 2011-07-20
YANTAI DARBOND TECH
View PDF0 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0007] The purpose of the present invention is to overcome the deficiencies of the above-mentioned prior art, and provide a two-component room temperature vulcanized silicone rubber for photovoltaic modules, which mainly solves the problem of poor aging resistance and poor curing of the existing room temperature vulcanized silicone rubber used as a photovoltaic module sealant. Slow speed, affecting efficiency and other issues
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0019] Example 1: A component: Weigh 200g of 20000mPa.s hydroxyl-terminated polydimethylsiloxane, 80g of 1000mPa.s dimethyl silicone oil, 160g of nano-calcium carbonate, 20g of R202 white carbon black, after premixing, Blend 3 times through a three-roll mill;
[0020] Component B: 0.2g of bismuth triheptanoate, 0.2g of bis(acetylacetonate)diisopropoxytitanium, 2g of hydroxyl silicone oil, mixed for 15min under nitrogen protection, added 16g of ethyl orthosilicate, γ-aminopropyltri Ethoxysilane 3g, mixed for 10min under nitrogen protection.
Embodiment 2
[0021] Example 2, component A: Weigh 200g of 20000mPa.s hydroxyl-terminated polydimethylsiloxane, 80g of 1000mPa.s dimethyl silicone oil, 160g of nano-calcium carbonate, and 20g of R202 white carbon black. After premixing, Blend 3 times through a three-roll mill;
[0022] Component B: 2g of bismuth triheptanoate, 1g of bis(acetylacetonate)diisopropoxytitanium, 1g of hydroxyl silicone oil, mixed for 15min under nitrogen protection, added 16g of ethyl orthosilicate, γ-aminopropyltriethoxy base silane 3g, mixed for 10min under nitrogen protection.
Embodiment 3
[0023] Example 3, component A: Weigh 200g of 20000mPa.s hydroxyl-terminated polydimethylsiloxane, 80g of 1000mPa.s dimethyl silicone oil, 160g of nano-calcium carbonate, and 20g of R202 white carbon black. After premixing, Blend 3 times through a three-roll mill;
[0024] Component B: 1 g of bismuth triheptanoate, 0.5 g of bis(acetylacetonate) diisopropoxy titanium, 3 g of hydroxyl silicone oil, mixed for 15 minutes under nitrogen protection, added 16 g of ethyl orthosilicate, γ-aminopropyl triethyl 3 g of oxysilane, mixed for 10 min under nitrogen protection.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
specific surface area
aaaaa
aaaaa
viscosity
aaaaa
aaaaa
viscosity
aaaaa
aaaaa
Login to View More
Abstract
The invention discloses a bi-component room temperature vulcanizing silicone rubber for a photovoltaic component, which comprises an A component and a B component. During use, the A component and the B component are uniformly coated on a work piece according to proportion through a bi-component glue spreader. The bi-component room temperature vulcanizing silicone rubber is characterized in that: the A component is prepared by grinding the following raw materials in part by weight: 100 parts of hydroxyl-terminated dimethyl silicone polymer, 20 to 50 parts of plasticizer, 60 to 100 parts of stuffing and 6 to 10 parts of thixotropic agent through a three-roll grinder; the B component is prepared by mixing the following raw materials in part by weight: 5 to 10 parts of cross-linking agent, 0.2 to 1.5 parts of compound catalyst, 1 to 2 parts of adhesion agent and 0.5 to 1.5 parts of catalyst carrier under the protection of nitrogen. The invention overcomes the shortcomings of poor aging resistance of the room temperature vulcanizing silicone rubber catalyzed by conventional organotin, and has characteristics of excellent outdoor aging resistance, good adhesiveness, fast curing speed, no reversion after the curing and no color change; the invention greatly improves the high temperature resistance and the damp-heat aging resistance, and can meet the requirement on the process procedure by controlling the curing speed.
Description
Technical field: [0001] The invention relates to the technical field of silicone rubber, specifically a two-component room temperature vulcanized silicone rubber, which has excellent outdoor aging resistance, good bonding performance, fast curing speed, and does not return to its original state after curing, and does not change color. Especially suitable for photovoltaic module sealing. Background technique: [0002] Today, with the rapid development of industrial electronic technology, energy issues and environmental issues are becoming increasingly severe. Green energy has become a global development trend. In the 1990s, the world began to pay attention to solar power generation, and the United States, Japan, and Europe took the lead in using it. At the beginning of this century, photovoltaic power generation began to take shape, doubling every year. [0003] At the heart of photovoltaic power generation is the silicon wafer. Since silicon wafers are fragile, they need...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 