Voltage sensitive material, preparation and application thereof

A voltage-sensitive, raw material technology, used in varistors, conductive materials dispersed in non-conductive inorganic materials, overvoltage protection resistors, etc. The effect of electrical conductivity and good resistance to environmental oxidation

Active Publication Date: 2010-06-23
上海神沃电子有限公司
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, the conductive particles used in polymer voltage sensitive materials are metal materials such as nickel and aluminum, which are prone to surface oxidation, which affects the stability of the composite material and causes an increase in the trigger voltage.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Voltage sensitive material, preparation and application thereof
  • Voltage sensitive material, preparation and application thereof
  • Voltage sensitive material, preparation and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Table 1 The numbers in the table are volume percentages

[0032] Numbering

epoxy resin

Silica

Silicon carbide

Titanium carbide

Titanium nitride

1

48%

3%

40%

-

9%

2

52%

3%

40%

5%

-

3

51%

3%

40%

4%

2%

4

70%

6%

10%

14%

-

5

47.9%

0.1%

50%

2%

-

Numbering

epoxy resin

Aluminum oxide

Silicon carbide

Titanium carbide

Titanium nitride

6

30%

50%

15%

5%

-

7

46%

22%

12%

-

20%

[0033] Note: epoxy resin HUITIAN 6308

[0034] Silica CABOT, Cab-O-Sil

[0035] Aluminum oxide particle size 45nm

[0036] Silicon Carbide Saint t-Gobain

[0037] Titanium carbide particle size 80nm

[0038] Titanium nitride particle size 40nm

[0039] The numbers in Table 2 are volume percentages

[0040] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a voltage sensitive material, which is prepared by compounding the raw materials comprising the following components in volume percent: 30-70% of organic high polymer; 2-20% of conducting particles and 10-50% of semiconductor particles. The voltage sensitive material can be applied in preparing voltage-sensitive elements.

Description

technical field [0001] The invention relates to polymer materials, in particular to voltage sensitive materials and their preparation and application. Background technique [0002] Functional polymer materials are currently a hot spot in material science research, and polymer voltage-sensitive materials with voltage-sensitive properties are among the best. So far, the academic and industrial circles are actively researching and developing them. The so-called high molecular voltage sensitive materials are usually composed of high molecular polymers, conductive particles, insulating particles and semiconductor particles. The high molecular polymer can be a thermoplastic polymer, such as polyolefin, polyvinylidene fluoride, polyamide, polyester, etc., or a thermosetting polymer, such as epoxy resin, silicone resin, phenolic resin, polyamide imide resin, etc. Conductive particles can be silver, copper, nickel, aluminum, graphite, carbon black and other materials. Insulating p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L101/00C08K3/00C08K3/36C08K3/34C08K3/14C08K3/28C08K3/22C08K3/08C08L63/00H01B1/20H01C7/10H01C7/12
Inventor 李凯宋华
Owner 上海神沃电子有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products