Antioxidation coating for high temperature billet

A technology for anti-oxidation paint and steel billet, applied in the field of anti-oxidation paint, can solve the problems of cracking and falling off, poor chemical stability, etc., and achieve the effect of low production cost and low raw material cost

Inactive Publication Date: 2012-12-12
本钢第三轧钢厂 +2
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The object of the present invention is to provide a kind of steel sheet for high temperature steel slabs to solve the problems of poor chemical stability and cracking and falling off by improving the adhesion and high temperature resistance. Antioxidant coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Take 60Kg of magnesia brick powder, 10Kg of fused magnesia, 10Kg of quartz sand, 20Kg of high alumina powder, and 35Kg of glass water. When making coatings, first grind magnesia brick powder, fused magnesia, quartz sand, and high alumina powder into fine particles of 180 mesh or more, mix the separately ground aggregate particles, and then add Glass water promptly makes the coating proposed by the present invention.

Embodiment 2

[0018] Get 20Kg of magnesia brick powder, 30Kg of fused magnesia, 30Kg of quartz sand, 20Kg of high alumina powder, 60Kg of glass water, and prepare the coating according to the method in Example 1.

Embodiment 3

[0020] Get 30Kg of magnesia brick powder, 30Kg of fused magnesia, 30Kg of quartz sand, 10Kg of high alumina powder, 50Kg of glass water, and prepare the coating according to the method in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an antioxidation coating for a high temperature billet. The antioxidation coating comprises an aggregate and a glass washing liquid of which mass is 35 to 60% of mass of the aggregate, wherein the aggregate comprises magnesia brick powder, fused magnesite, quartz sand and high-aluminum powder. The aggregate in the antioxidation coating has ideal high-temperature resistance and water resistance, and does not cause expansion between raw material molecules at a high temperature. The glass washing liquid has excellent adhesion. Therefore, the antioxidation coating does not powder, crack and fall off, is suitable for surface coating of various types of billets and prevents billet oxidation.

Description

technical field [0001] The invention relates to an anti-oxidation coating used on high-temperature steel slabs. Background technique [0002] In the process of rolling steel, the steel billet is firstly transported into the heating furnace by means of steel pushing to heat it. For ordinary steel billet rolling, the temperature of the heating furnace is usually set between 1100-1180°C. After the billet is heated to a predetermined temperature, it is transported to the rolling mill for rolling. Because the steel billet can stimulate the activity of iron ions in it at this temperature, making it diffuse from the inside to the outside, and the oxygen atoms in the heating furnace will diffuse to the surface of the billet under the absorption of iron ions. The chemical reaction that occurs after the encounter will produce iron oxides, which include ferric oxide and ferric oxide, and iron oxide, and its chemical formula is: Fe 2 o 3 +Fe 3 o 4 +FeO, the greater the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66
Inventor 易贵科叶永菁
Owner 本钢第三轧钢厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com