A kind of acrylic flexible anticorrosion primer and preparation method thereof

An acrylic flexible and anti-corrosion primer technology, applied in the field of coatings, can solve the problems such as the inability to meet the requirements of large deformation conditions, the detachment of the elastic coating, the cracking of the primer coating, etc., to ensure the feasibility of testing and good film compactness. , the effect of broad application prospects

Active Publication Date: 2022-02-25
天津灯塔涂料工业发展有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] For high-thickness coating systems, coating cracking will occur under the conditions of large deformation of various vehicles, equipment, facilities, construction machinery, etc., and the deformation ability of elastic substrates does not match that of ordinary coatings, resulting in primer coatings Therefore, it is urgent to develop a new type of high-quality acrylic flexible anti-corrosion primer, which not only requires excellent physical properties, but also has anti-corrosion and weather resistance effects when used alone, and requires its Effectively solve the problem of detachment and cracking of the existing primer due to stretching and deformation of the matching elastic coating, and has a good matching with the elastic coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of acrylic flexible anticorrosion primer and preparation method thereof
  • A kind of acrylic flexible anticorrosion primer and preparation method thereof
  • A kind of acrylic flexible anticorrosion primer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A kind of acrylic flexible anticorrosion primer, is prepared by following method:

[0037] Mix 50 parts of butyl acetate, 30 parts of xylene, 10 parts of mixed dibasic acid ester, and 10 parts of propylene glycol methyl ether acetate to obtain a diluent.

[0038] 45g of homemade flexible acrylic resin with a solid content greater than 45%, 0.5g of dispersant BYK161, 15g of titanium dioxide, 5g of zinc yellow, 8g of talc powder, 4g of zinc phosphate, 1.5g of mica powder, 1.5g of light calcium, 0.2g of bentonite, Add 8.5g of diluent into the mixing container and stir in sequence, then grind until the particle size is below 35μm, add 0.2g of leveling agent BYK306, 0.3g of adhesion promoter EDL-6026F, 0.3g of UV absorber Tinuvin 1130 and 10g of diluent to adjust the solid The content is more than 55% to obtain the first component.

[0039] Where: Homemade flexible acrylic

[0040]

[0041] 1) Divide xylene and benzoyl peroxide into five equal parts for subsequent use a...

Embodiment 2

[0054] Preparation of a novel acrylic flexible anti-corrosion primer:

[0055] Mix 40 parts of butyl acetate, 30 parts of xylene, 15 parts of mixed dibasic acid ester, and 15 parts of propylene glycol methyl ether acetate to obtain a diluent.

[0056] 48g of homemade flexible acrylic resin with a solid content greater than 45%, 0.6g of dispersant DA-703-50, 14g of titanium dioxide, 7g of zinc yellow, 8g of talcum powder, 5g of zinc phosphate, 1.2g of mica powder, 1.2g of light calcium, Add 0.2g of bentonite and 3.9g of diluent into the mixing container and stir in sequence, then grind until the particle size is below 35μm, add 0.2g of leveling agent LHP91, 0.3g of adhesion promoter EDL-6019B, 0.4g of ultraviolet absorber Tinuvin 5060 and dilute 10g of the agent is used to adjust the solid content to be more than 55% to obtain the first component.

[0057] Where: Homemade flexible acrylic

[0058]

[0059] 1) Divide xylene and benzoyl peroxide into five equal parts for sub...

Embodiment 3

[0072] Preparation of a novel acrylic flexible anti-corrosion primer:

[0073] Mix 45 parts of butyl acetate, 35 parts of xylene, 10 parts of mixed dibasic acid ester, and 10 parts of propylene glycol methyl ether acetate to obtain a diluent.

[0074] 50g self-made flexible acrylic resin with a solid content greater than 45%, 0.8g dispersant BYK110, 13g titanium dioxide, 7g zinc yellow, 7g talcum powder, 5g zinc phosphate, 2g mica powder, 2g light calcium, 0.3g bentonite, diluent Add 1.8g into the mixing container and stir in turn, then grind until the particle size is below 35μm, add 0.3g of leveling agent BYK300, 0.4g of adhesion promoter EDL-6019B, 0.4g of ultraviolet absorber Tinuvin 5060 and 10g of diluent to adjust the solid content to More than 55% get A component.

[0075] Where: Homemade flexible acrylic

[0076]

[0077] 1) Divide xylene and benzoyl peroxide into five equal parts for subsequent use according to the specified amount in the formula;

[0078] 2) A...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides an acrylic flexible anti-corrosion primer and a preparation method thereof. The primer is composed of component A and component B, and the ratio of component A and component B is 100:15-20 by weight Component A consists of flexible acrylic resin liquid with a solid content greater than 45%, dispersant, leveling agent, adhesion promoter, ultraviolet absorber, thinner, titanium dioxide, zinc yellow, talcum powder, zinc phosphate, mica powder, Composed of light calcium and bentonite; component B is an elastic isocyanate resin solution with a solid content greater than 90%; the primer can cover the stretching vibration cracks and elongation at break caused by the difference in elastic modulus between various substrates during equipment operation. Elongation ≥ 100%, tensile strength ≥ 10Mpa, and has excellent anti-corrosion function.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to an acrylic flexible anticorrosion primer and a preparation method thereof. Background technique [0002] For high-thickness coating systems, coating cracking will occur under the conditions of large deformation of various vehicles, equipment, facilities, construction machinery, etc., and the deformation ability of elastic substrates does not match that of ordinary coatings, resulting in primer coatings Therefore, it is urgent to develop a new type of high-quality acrylic flexible anti-corrosion primer, which not only requires excellent physical properties, but also has anti-corrosion and weather resistance effects when used alone, and requires its It effectively solves the problem of detachment and cracking of the existing primer due to stretching and deformation of the matching elastic coating, and has a good matching with the elastic coating. Contents of the invention [00...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/04C09D5/08C09D5/00C09D7/61C08G18/62C08F220/18C08F220/06C08F220/20C08F212/08
Inventor 黄震高萌何效凯孙瑞翟菁赵蕊
Owner 天津灯塔涂料工业发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com