Integrated optimization and setting method of tension in continuous annealing set furnace of continuous annealing set
A continuous annealing unit, optimized setting technology, applied in the direction of furnace, heat treatment furnace, furnace type, etc., can solve the problems affecting the surface quality of strip steel, and the problem of suppressing vibration of strip steel is not considered
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0031] In order to illustrate the basic idea of the present invention, the continuous annealing process of the steel strip whose specification is SPCC and whose specification is 0.8mm×1250mm is now selected as an example, by means of Figure 4 To describe the tension optimization setting process of strip steel of specific steel type and specification on a specific continuous annealing unit.
[0032] First, in step 1, the characteristic parameters of the steel strip in the annealing process of the continuous annealing unit are collected, and the width of the steel strip obtained is 1250mm, the thickness is 0.8mm, and the steel type is SPCC;
[0033] Subsequently, in step 2, collect the minimum tension allowed by each section to ensure that no deviation is allowed during the continuous annealing process of the specific strip, including the minimum tension T of heating section 1 jr1min =6.96Mpa, the minimum tension T of heating stage 2 jr2min =6.24Mpa, minimum tension T of 3 s...
Embodiment 2
[0046] In order to further illustrate the basic idea of the present invention, the continuous annealing process of strip steel with the incoming material grade of DC04 and the specification of 0.7mm×1670mm is taken as an example. Figure 4 To describe the tension optimization setting process of strip steel of specific steel type and specification on a specific continuous annealing unit.
[0047] First, in step 1, the characteristic parameters of the strip steel during the annealing process of the continuous annealing unit are collected, and the width of the strip steel obtained is 1670mm, the thickness is 0.7mm, and the steel type is DC04;
[0048] Subsequently, in step 2, collect the minimum tension allowed by each section to ensure that no deviation is allowed during the continuous annealing process of the specific strip, including the minimum tension T of heating section 1 jr1min =5.175Mpa, the minimum tension T of heating stage 2 jr2min =4.8Mpa, minimum tension T of 3 s...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap