Transition brick for joint part of slag line and wall of ladle

A technology of ladle slag line and slag line brick, which is applied in the direction of casting molten material container, metal processing equipment, casting equipment, etc., can solve the problem of increasing the workload of ladle digging or patching, increasing the consumption of single ladle materials, and the large difference in refractory brick materials. and other problems, to achieve the effect of reducing the consumption of single-package materials, improving the service life and improving the compatibility.

Active Publication Date: 2012-05-30
ZHENGZHOU ZHENDONG TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the large difference or incompatibility of the refractory bricks used in the slag line working layer of the ladle lining and the cladding wall working layer, the connection between the slag line working layer and the cladding wall working layer will be corroded in advance during use , which not only shortens the service life of the steel ladle, but also increases the workload of digging or subsidizing the steel ladle, and also increases the material consumption of a single ladle of the steel ladle

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The transition brick used in the ladle slag line and the transition part of the cladding wall according to the present invention is composed of the following raw material proportions by weight:

[0018] a. When the slag line bricks and cladding bricks of the ladle are composed of the following raw material proportions by weight:

[0019] Slag line brick: MgO: 69-86; C: 13-18; Wall brick: Al 2 o 3 : 50-74; MgO: 5-20; C: 0-12;

[0020] The ratio of raw materials in parts by weight of the transition brick is: Al 2 o 3 : 30-40; MgO: 30-45; C: 13-15;

[0021] b. When the slag line bricks and cladding bricks of the ladle are composed of the following raw material proportions by weight:

[0022] Slag line brick: MgO: 69-86; C: 13-18; Wall brick: MgO: 60-65; C: 0-10;

[0023] The ratio of raw materials by weight of the transition brick is: MgO: 69-75; C: 10-12;

[0024] c. When the slag line bricks and cladding bricks of the ladle are composed of the following raw materi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a transition brick for a joint part of a slag line and a wall of a ladle. a, when a slag line brick consists of the following raw materials in part by weight: 69 to 86 parts of MgO and 13 to 18 parts of C, and a wall brick of the ladle consists of the following raw materials in part by weight: 50 to 74 parts of Al2O3, 5 to 20 parts of MgO and 0 to 12 parts of C, the transition brick consists of the following raw materials in part by weight: 30 to 40 parts of Al2O3, 30 to 45 parts of MgO and 13 to 15 parts of C; b, when the slag line brick consists of the following raw materials in part by weight: 69 to 86 parts of MgO and 13 to 18 parts of C, and the wall brick of the ladle consists of the following raw materials in part by weight: 60 to 65 parts of MgO and 0 to 10parts of C, the transition brick consists of the following raw materials in part by weight: 69 to 75 parts of MgO and 10 to 12 parts of C; and c, when the slag line brick consists of the following raw materials in part by weight: 69 to 75 parts of MgO and 14 to 18 parts of C, and the wall brick of the ladle consists of the following raw materials in part by weight: 60 to 68 parts of Al2O3 and 6 to 18 parts of MgO, the transition brick consists of the following raw materials in part by weight: 30 to 40 parts of Al2O3, 30 to 45 parts of MgO and 8 to 10 parts of C.

Description

technical field [0001] The invention relates to a steel ladle inner lining, in particular to a transition brick used for the ladle slag line and the ladle wall junction. Background technique [0002] The ladle is a special equipment used to receive and pour molten steel from the steelmaking furnace. Due to the large difference or incompatibility of the refractory bricks used in the slag line working layer of the ladle lining and the cladding wall working layer, the connection between the slag line working layer and the cladding wall working layer will be corroded in advance during use , which not only shortens the service life of the ladle, but also increases the work load of digging or subsidizing the ladle, and also increases the material consumption of a single ladle of the ladle. Contents of the invention [0003] The purpose of the present invention is to provide a transition brick with long service life for the junction of ladle slag line and cladding wall. [0004...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B22D41/02
Inventor 侯振东
Owner ZHENGZHOU ZHENDONG TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products