Manufacturing process of shearing rib mold

A mold manufacturing and process technology, applied in the field of shear rib mold manufacturing process, can solve the problems of high cost, high shrinkage rate and deformation rate, and achieve the effect of cost saving and labor efficiency improvement

Inactive Publication Date: 2011-03-30
昆山华风风电科技有限公司
View PDF5 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problems in the prior art that the shear rib mold is made of glass fiber reinforced plastics, the cost is high, and the shrinkage rate and deformation rate of the mold are relatively high after the mold is completed, the invention provides a manufacturing process for the shear rib mold using steel plates as raw materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing process of shearing rib mold
  • Manufacturing process of shearing rib mold
  • Manufacturing process of shearing rib mold

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] Such as figure 1 As shown, the specific process is as follows:

[0030] 1. A manufacturing process of a shear rib mould, characterized in that it comprises the following steps:

[0031] (1), puzzle, stakeout

[0032] After putting the 1.5m X 2.5m cold-rolled board into a plane, place the finished shear ribs on the plane;

[0033] (2), metal folding

[0034] Fold the placed cold-rolled board into a right angle to make the flanging of the shearing rib, and use the newly-added L-shaped board to lean on the finished product of the shearing rib, a section of 1 meter, such as figure 2 As shown, the flanging size is determined according to the size of the finished shear rib, the flanging width is 20 cm and the height is 9 cm;

[0035] (3), welding plate

[0036] Use an electric welder to weld the gaps between the cold-rolled plates after folding;

[0037] (4), welding seam pressure

[0038] Keep pressure on each weld of the flat plate, first paste the sealing doctrine at the weld position,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a manufacturing process of a shearing rib mold, which is characterized by comprising the following steps: (1) splicing plates, and lofting; (2) folding a metal edge: folding a steel plate into a right angle at the edge of the steel plate to manufacture the edge of a shearing rib, and ensuring the angle; (3) welding a flat plate; (4) maintaining pressure of welded seams; (5) manufacturing an inner cavity of the mold; (6) laying heating strips; (7) laying heat-insulating cotton; and (8) adjusting the level of the mold. In the invention, the problems that in the prior art, the shearing rib mold is manufactured by adopting glass fiber reinforced plastics, the cost is high, and the shrinkage rate and the deformation rate of the finished mold are higher are solved. The invention provides the manufacturing process for manufacturing the shearing rib mold by using the steel plate as a raw material.

Description

Technical field [0001] The invention relates to a mold manufacturing process, in particular to a cutting rib mold manufacturing process. Background technique [0002] At present, there are many kinds of molds used to make FRP, such as wooden molds, silicone molds, plaster molds, FRP molds, steel molds, etc. The method of making FRP molds: Lay FRP cloth, and then lay copper pipes for heating, mix resin and aluminum powder evenly, spread on it, and then spread a layer of FRP cloth. FRP molds include female molds, male molds, paired molds, etc. The specific inner type to be selected depends on the structure, process, and quality requirements of the product. First of all, the original part is the male mold. In the past, most of them were made of wood in China. However, for wind turbine blades of this length, most foreign countries use paste wood instead of wood to construct and use machines to operate. Then turn the negative film on this male mold, and after the parting surface is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B23P15/24
Inventor 黄凯健张传智高伟陈曙明
Owner 昆山华风风电科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com