Electron beam radiation curing film glass and manufacturing method thereof

A technology of electron beam radiation and glass manufacturing, which is applied in the field of glass, can solve the problems of unstable quality of hand-made glass film, scattered fragments and hurt people, and low production efficiency, so as to solve the problems of surface pollution and aging, solve the problem of scattered and hurt people, Life-enhancing effect

Inactive Publication Date: 2011-03-30
王广武
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

3. Transfer the electron beam radiation curing varnish film printing and glazing technology to the manufacture of electron beam radiation curing film glass, so that the electron beam radiation curing film glass can form high-efficiency industrial production and quality assurance, and solve the unstable quality of manual glass film. low production efficiency
5. Coating electron beam radiation curing anti-shatter varnish film on the surface of tempered glass to solve the problem of scattered and injured tempered glass self-explosive glass fragments

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electron beam radiation curing film glass and manufacturing method thereof
  • Electron beam radiation curing film glass and manufacturing method thereof
  • Electron beam radiation curing film glass and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A cross-sectional view of an electron beam radiation-cured film glass figure 1 Shown, wherein: 1 is glass, 2 is electron beam radiation curing film. When manufacturing electron beam radiation curing single-sided varnish film glass, first, use a roll coater to evenly coat the electron beam radiation curing varnish on the surface of the glass 1, and after the electron beam radiation is irradiated, the electron beam radiation curing varnish is cured on the glass 1 surface, an electron beam radiation curing film 2 is formed.

Embodiment 2

[0037] A cross-sectional view of an electron beam radiation-cured film glass containing nano-indium tin oxide figure 2As shown, wherein: 3 is glass, 4 is nano-indium tin oxide electron beam radiation-curable varnish, and 5 is surface layer electron-beam radiation-curable varnish. When manufacturing the electron beam radiation curing film glass containing nano indium tin oxide, at first, the nano indium tin oxide electron beam radiation curing varnish 4 is uniformly coated on the surface of the glass 3 with a roll coater, and after being irradiated by electron beam radiation, the The nano-indium tin oxide electron beam radiation-curable varnish is cured on the surface of the glass 3 to form a nano-indium tin oxide electron-beam radiation-curable varnish film, and the surface layer of electron-beam radiation-curable varnish 5 is evenly coated on the nano-indium oxide with a roll coater The surface of the tin electron beam radiation curing varnish film 4 is irradiated by the ele...

Embodiment 3

[0039] A cross-sectional view of an electron beam radiation-cured sterilized varnish film glass containing nano-silver image 3 As shown, wherein: 6 is glass, and 7 is nano-silver electron beam radiation curing varnish. When manufacturing electron beam radiation curing sterilization varnish film glass, at first, the nano-silver electron beam radiation curing varnish 7 is evenly coated on the surface of the glass 6 with a roll coater, and after being irradiated by electron beam radiation, the nano-silver electron beam is radiated Curing varnish 7 is solidified on the glass surface.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses electron beam radiation curing film glass which comprises glass, an electron beam radiation source and electron beam radiation liquid gloss oil. The electron beam radiation curing liquid gloss oil is sprayed or printed on the surface of the glass; and after being irradiated by the electron beam radiation source, the electron beam radiation liquid glass oil is subjected to rapid polymerization reaction to form an electron beam radiation curing film on the surface of the glass.

Description

[0001] Technical field; The present invention relates to the field of glass. Background technique; [0002] Radiation curing technology is a new curing technology that can effectively control air pollution, especially the emission of volatile organic compounds (voc). The curing mechanism is to irradiate a solvent-free liquid chemical substance with an electron beam to cause a rapid polymerization reaction to form a three-dimensional network structure and form a solid film. [0003] Electron beam radiation curing technology is mainly used in flexographic printing, offset printing and glazing. Ford Motor Company of the United States applies radiation curing technology to auto parts and instrument coatings. [0004] The electron beam radiation curing film does not contain volatile substances voc, has good chemical resistance and friction resistance, and has a short curing time. Generally, it only takes 0.1 seconds to dry completely, which greatly improves the production efficienc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C17/00
Inventor 王广武
Owner 王广武
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap