Foamed polystyrene curtain plate sheet and manufacturing method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of expanded polystyrene and curtain panels, which is applied in the field of curtain panels, can solve the problems of high heat deformation temperature, and achieve the effects of good heat deformation resistance, broad application prospects, and simple and practical preparation methods
Active Publication Date: 2014-08-20
广东波斯科技股份有限公司
View PDF2 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] The purpose of the present invention is to solve the problems existing in the use of the above-mentioned existing expanded polystyrene plastic curtain panels, and to provide a curtain panel with light weight, high heat distortion temperature and high stiffness
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0018] Weigh HIPS 7000g, GPPS3000g, PP 2000g, oxidized polyethylene wax 50g, K glue 200, calcium carbonate 3000g, AC foaming agent 30g, zinc oxide 150g, antioxidant 1010 5g, DCP 10g, titanium dioxide 2g in a high-speed mixer Mix evenly in the medium, then put it into the extruder, the temperature of the extruder is 160-170°C, the speed of the extruder is 300 rpm, the extruded sheet is 4mm thick and 50mm wide, and cut into strips of 900mm after cooling and shaping.
Embodiment 2
[0020] Weigh HIPS 10000g, PP 2000g, polypropylene grafted polystyrene 800, calcium carbonate 3000g, OBSH foaming agent 100g, zinc stearate 30g, antioxidant 1076 3g, antioxidant 168 6g, DCP 10g, commercially available Mix 400g imitation wood grain masterbatch evenly in a high-speed mixer, then put it into the extruder, the temperature of the extruder is 160-170°C, the speed is 300 rpm, the extruded sheet is 4mm thick and 50mm wide, after cooling and shaping Cut into strips of 900mm.
Embodiment 3
[0022] Mix 14000g of HIPS, 6000g of GPPS, 2000g of PC, high-impact polystyrene grafted maleic anhydride 200, mix them uniformly and granulate them in a twin-screw extruder at a granulation temperature of 230°C. Weigh 11100g of the above masterbatch, 1000g of glass fiber, 1000g of acicular wollastonite, 1000g of montmorillonite, 40g of EBS, 50g of AC foaming agent, 100g of sodium bicarbonate, 10g of BIBP and mix them uniformly in a high-speed mixer, then put Extruder, the temperature of the extruder is 190-200°C, the rotating speed is 300 rpm, the thickness of the extruded sheet is 4mm, and the width is 50mm, which is cut into strips of 900mm after cooling and shaping.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention discloses a foamed polystyrene curtain plate sheet and a manufacturing method thereof. The foamed polystyrene curtain plate sheet consists of the following components in part by weight: 100 parts of polystyrene, 1 to 50 parts of blended resin, 1 to 50 parts of filler, 0.1 to 20 parts of compatilizer, 0 to 1 part of antioxidant, 0 to 5 parts of processing aid, 0.1 to 10 parts of foaming agent and 0.1 to 10 parts of cross-linking agent. The foamed polystyrene curtain plate sheet manufactured according to a formula of the invention has light weight, aging resistance, corrosion resistance, heat insulation and insulating property, and the most outstanding advantage of high thermal deformation resistance, and can adapt to direct sunlight under a hot weather condition in summer in low-latitude regions. The manufacturing method of the foamed polystyrene curtain plate sheet is simple and practical, and has wide application prospect.
Description
technical field [0001] The invention relates to the field of curtain panels, in particular to a foamed polystyrene curtain panel and a preparation method thereof. Background technique [0002] Curtain panels are usually prepared from plastic materials, aluminum materials, and wood. Aluminum has high mechanical strength, but the production process is easy to pollute the environment and cause harm to the human body; wood texture is better, but it requires higher requirements for the required wood, and at the same time has poor strength, requires a certain thickness, and is more expensive; plastic materials can Overcome the shortcomings of aluminum and wood, and obtain thin and flexible sheets. After being heated and melted, plastic material curtain panels can be processed by traditional processes such as extrusion and injection molding, which are easy to produce quickly and automatically. Widely favored. Expanded polystyrene plastic curtain panels are light in weight, aging-...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More 