A water wood grain craft

A kind of technology, water wood technology, applied in the field of water wood grain technology, can solve the problems of inability to achieve beautiful effects, weak corrosion resistance, poor fire resistance, etc., and achieve the effect of being conducive to local heat dissipation, improving heat conduction capacity, and improving fire resistance

Inactive Publication Date: 2020-12-22
WENZHOU KULE DINING TABLE ARTICLES CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Wood is a commonly used decorative material in the field of furniture and construction. It is widely used in laying floors, decorating walls, and making furniture. However, wood products are usually simply coated with a layer of paint on the surface when they are made. The original wood color of furniture wood has a single decorative effect, which cannot achieve an aesthetic effect, and cannot achieve a good anti-aging effect. After long-term use of furniture products, wood rot often occurs. At the same time, due to the tensile strength of wood Low, weak corrosion resistance, prone to blistering and peeling off
In addition, due to the limitation of the material of wood itself, it has the characteristics of poor fire resistance, so there is a safety hazard in use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] 1) Substrate pretreatment step: select a solid wood board, pre-bake the board at 60°C for 8 hours, the degree of baking is subject to no stress deformation; immerse the pre-baked board in the treatment solution for 5 hours , the treatment solution includes didecyldimethylammonium chloride and cyclohexylamine with a volume ratio of 6:4, and hydrochloric acid to adjust the pH value of the treatment solution to 6; the plate after soaking in dry air Blow dry at medium temperature until the moisture content reaches 5%;

[0030] 2), surface carbonization step: use an oxygen welding machine to carbonize the surface of the base material obtained in step 1, and then polish it with sandpaper to obtain a carbon layer with an average thickness of 0.2mm;

[0031] 3), surface strengthening step: the surface of the substrate obtained in step 2 is sprayed with polyurethane primer, the thickness of the primer layer is 0.4mm, and a copper wire mesh is embedded in the primer layer, and th...

Embodiment 2

[0036] 1) Substrate pretreatment step: select solid wood board or composite board, pre-bake the board at 100°C for 4 hours, the degree of baking is subject to no stress deformation; immerse the pre-baked board in the treatment solution Soak in 3h, described treatment liquid comprises the didecyl dimethyl ammonium chloride and cyclohexylamine that the volume ratio is 8:2, and the hydrochloric acid that regulates the pH value of described treatment liquid to be 7; Blow dry at room temperature in dry air until the moisture content reaches 7%;

[0037] 2), surface carbonization step: use an oxygen welding machine to carbonize the surface of the base material obtained in step 1, and then polish it with sandpaper to obtain a carbon layer with an average thickness of 0.5 mm;

[0038] 3), surface strengthening step: the substrate surface obtained in step 2 is sprayed with polyurethane primer, the thickness of the primer layer is 0.6mm, and a copper wire mesh is embedded in the primer ...

Embodiment 3

[0043] 1) Substrate pretreatment step: select solid wood board or composite board, pre-bake the board at 80°C for 6 hours, the degree of baking is subject to no stress deformation; immerse the pre-baked board in the treatment solution Soak in 4h, described treatment liquid comprises the didecyl dimethyl ammonium chloride and cyclohexylamine that volume ratio is 7:3, and the hydrochloric acid that the pH value of described treatment liquid is adjusted is 6; Blow dry in dry air at room temperature until the moisture content reaches 6%;

[0044] 2), surface carbonization step: use an oxygen welding machine to carbonize the surface of the base material obtained in step 1, and then polish it with sandpaper to obtain a carbon layer with an average thickness of 0.4mm;

[0045]3), surface strengthening step: the substrate surface obtained in step 2 is sprayed with a polyurethane primer, the thickness of the primer layer is 0.5mm, and a copper wire mesh is embedded in the primer layer,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a wood grain process. The process comprises steps of base plate dipping and drying pre-treatment, surface carbonization, double layer wood grain drawing treatment and surface protection layer treatment, so that the corrosion resistance, the deformation resistance and the surface wear resistance of a product are improved. The wood grain-drawn base material prepared by the process has excellent corrosion resistance, insect damage resistance, thermal deformation resistance, anti-falling property, fire resistance and moisture resistance, and can be repeatedly scrubbed without fading.

Description

technical field [0001] The invention relates to the field of wood substrate manufacturing, in particular to a water wood grain process. Background technique [0002] Wood is a commonly used decorative material in the field of furniture and construction. It is widely used in laying floors, decorating walls and making furniture. However, wood products are usually simply coated with a layer of paint on the surface when they are made. The original wood color of furniture wood has a single decorative effect, which cannot achieve an aesthetic effect, and cannot achieve a good anti-aging effect. As a result, after long-term use of furniture products, wood rot often occurs. At the same time, due to the tensile strength of wood Low, weak corrosion resistance, prone to blistering and peeling off. In addition, due to the limitation of the material of wood itself, it has the characteristics of poor fire resistance, so it has potential safety hazards during use. Contents of the invent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B44F9/02B44C5/04B27K3/02B27K3/52B27M1/06B05D7/00B05D1/32B05D5/00B05D3/10
CPCB05D1/32B05D3/104B05D5/00B05D7/56B05D2501/00B05D2502/00B05D2503/00B05D2518/10B27K3/02B27K3/0207B27K3/52B27K2240/20B27M1/06B44C5/043B44F9/02B05D2420/01B05D2420/02B05D2420/03B05D2420/04B05D2420/05
Inventor 庄超然
Owner WENZHOU KULE DINING TABLE ARTICLES CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com