Novel environment-friendly coating with superhigh marine environment corrosion resistance and preparation method and application thereof

An environmentally friendly coating and marine environment technology, applied in the direction of anti-corrosion coatings, epoxy resin coatings, coatings, etc., to achieve the effects of excellent salt spray resistance, excellent anti-corrosion performance, and low VOC content

Active Publication Date: 2012-02-15
CHINA PAINT MFG CO SHENZHEN
View PDF8 Cites 46 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] In view of the above-mentioned deficiencies in the prior art, the purpose of the present invention is to provide a new type of environmentally friendly coating with super corrosion resistance to marine environment and its preparation method and application, aiming to solve the long-standing problems of heavy anti-corrosion coatings in my country

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel environment-friendly coating with superhigh marine environment corrosion resistance and preparation method and application thereof
  • Novel environment-friendly coating with superhigh marine environment corrosion resistance and preparation method and application thereof
  • Novel environment-friendly coating with superhigh marine environment corrosion resistance and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0096] The following components are calculated in parts by weight: 29 parts of low-viscosity solvent-free bisphenol A epoxy resin E-51, 10 parts of reactive diluent hydrocarbon petroleum resin, 0.5 parts of organic silicon defoamer as auxiliary agent, 7 parts of organic solvent, Among them, 5 parts of S-100, 2 parts of anhydrous alcohol, 5.5 parts of toner namely phthalein white powder, 14 parts of the first filler, including 7 parts of talcum powder, 7 parts of kaolin, 32 parts of the second filler, including 6 parts of glass fiber powder, 26 parts of hollow microspheres and 2 parts of organic bentonite as a thixotropic agent are added into the tank and stirred evenly to form a coating base material.

[0097] The following components are calculated by weight: 72 parts of aromatic polyamine resin, 21 parts of reactive diluent hydrocarbon petroleum resin, 5.0 parts of auxiliary agent tertiary amine drier K-54, 2 parts of organic solvent S-100 are added to the tank Stir in mediu...

Embodiment 2

[0119] According to the specified components corresponding to Example 2 in Table 3, repeat the corresponding operation of Example 1 to obtain a cured paint film. And test its technical performance as described in embodiment 1. The test indicators are shown in Table 1. The test results show that the technical performance is good, as shown in Table 4.

Embodiment 3

[0121] According to the specified components corresponding to Example 3 in Table 3, repeat the corresponding operation of Example 1 to obtain a cured paint film. And test its technical performance as described in embodiment 1. The test indicators are shown in Table 1. The test results show that the technical performance is good, as shown in Table 4.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a novel environment-friendly coating with superhigh marine environment corrosion resistance and a preparation method and application thereof. The environment-friendly coating with superhigh marine corrosion resistance consists of the following components in part by weight: a main agent comprising 22 to 35 parts of low-viscosity solvent-free epoxy resin, 9 to 15 parts of activated thinner, 0.2 to 5 parts of aid, 5 to 8 parts of organic solvent, 0.5 to 15 parts of toner, 10 to 25 parts of first filler, 20 to 45 parts of second filler and 0.5 to 5 parts of thixotropic agent, and a curing agent comprising 60 to 90 parts of amine resin, 10 to 30 parts of activated thinner, 2 to 8 parts of aid and 2 to 10 parts of organic solvent. During use, the main agent and the curing agent are uniformly mixed, and the mixture is applied to the surface of a substrate. A film formed by the coating is high in corrosion resistance and low in content of volatile organic compounds (VOC), does not contain any toxic or harmful substance, can be universally used in a drinking water tank, and also can be used for a ship ballast tank, a ship bottom, a deck and each position of a marine platform.

Description

technical field [0001] The invention relates to the field of environment-friendly coatings, in particular to a novel environment-friendly coating with super corrosion resistance to marine environment, its preparation method and application. Background technique [0002] Heavy-duty anti-corrosion coatings are playing an increasingly important role in national economic construction and national defense construction. For example, shipbuilding, machinery and equipment manufacturing, national defense industry and other fields are inseparable from heavy-duty anti-corrosion coatings. Since the reform and opening up, my country's heavy-duty anti-corrosion coatings have developed rapidly and have made great progress. However, most of the anti-corrosion coatings are still based on solvent-based coatings. The comprehensive performance of the entire heavy-duty anti-corrosion industry is not high, and there is still a significant gap compared with developed countries. Most of the occas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D163/02C09D163/04C09D5/08
Inventor 蔡江波伍学军
Owner CHINA PAINT MFG CO SHENZHEN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap