Aqueous coating with high heat-dissipation performance and preparation method thereof

A water-based coating, high heat dissipation technology, applied in anti-corrosion coatings, conductive coatings, epoxy resin coatings, etc., can solve the problems of large pollution, unsatisfactory heat dissipation effect of heat dissipation coatings, etc., to achieve good heat dissipation effect, green environmental protection price, enhanced cooling effect

Inactive Publication Date: 2018-03-06
CHANGZHOU XICAI CARBON MATERIAL TECH CO LTD
View PDF8 Cites 46 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the heat dissipation effect of heat dissipation coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aqueous coating with high heat-dissipation performance and preparation method thereof
  • Aqueous coating with high heat-dissipation performance and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Mix 30 parts of acrylic resin, 10 parts of graphene, and 60 parts of water into the blender, control the speed at 2000 rpm, and stir for 2 hours; add 15 parts of aluminum nitride, 10 parts of silicon carbide, 5 parts of carbon nanotubes, carboxymethyl 4 parts of sodium cellulose, 4 parts of polydimethylsiloxane, 4 parts of ethylenediamine, 4 parts of polyether modified polydimethylsiloxane, 4 parts of aminopropyl trimethoxysilane, control The rotation speed is 2000rpm, and the stirring time is 3h; the above mixture is put into a sand mill to grind and disperse for 1h, and the graphene heat dissipation coating is obtained.

Embodiment 2

[0031] Mix 30 parts of acrylic resin, 1 part of graphene, and 30 parts of water into the mixer, control the rotation speed at 1000 rpm, and stir for 1 hour; add 15 parts of aluminum oxide, 5 parts of carbon black, and 2 parts of sodium carboxymethyl cellulose to the mixer in sequence. 2 parts, 2 parts of polydimethylsiloxane, 2 parts of ethylenediamine, 2 parts of polyether modified polydimethylsiloxane, 2 parts of aminopropyl trimethoxysilane, control the speed of 1000rpm, stirring time 1h; add the above mixture into a sand mill to grind and disperse for 1h to obtain a graphene heat dissipation coating.

[0032] Comparative example 1, this comparative example is basically the same as Example 1, but heat dissipation coating is prepared without adding graphene. Mix 30 parts of acrylic resin and 30 parts of water into the blender, control the speed at 1000 rpm, and stir for 1 hour; add 15 parts of aluminum oxide, 5 parts of carbon black, 2 parts of sodium carboxymethyl cellulose...

Embodiment 3

[0039] Mix 40 parts of acrylic resin, 5 parts of graphene, and 35 parts of water into the mixer, control the rotation speed at 1500 rpm, and stir for 1.5 hours; add 10 parts of aluminum nitride, 5 parts of magnesium oxide, 5 parts of carbon nanotubes, and carboxylate to the mixer in sequence. 3 parts of sodium methylcellulose, 3 parts of polydimethylsiloxane, 3 parts of ethylenediamine, 3 parts of polyether modified polydimethylsiloxane, 3 parts of aminopropyl trimethoxysilane, The rotation speed is controlled at 1500rpm, and the stirring time is 2h; the above mixture is put into a sand mill to grind and disperse for 1h, and the graphene heat dissipation coating is obtained.

[0040]Comparative example 1, this comparative example is basically the same as Example 1, but heat dissipation coating is prepared without adding graphene. Mix 40 parts of acrylic resin and 35 parts of water into the mixer, control the speed at 1500 rpm, and stir for 1.5 hours; add 10 parts of aluminum n...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Impact strengthaaaaaaaaaa
Impact strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of novel coating preparation and in particular relates to an aqueous coating with high heat-dissipation performance which comprises the following components: 30-60 parts of aqueous resin, 1-10 parts of graphene, 10-30 parts of packing, 10-20 parts of an aid and 30-60 parts of a solvent, wherein the radial size of the graphene is 1-100 microns; and the graphene consists of 1-3 layers. The high heat-dissipation performance aqueous coating provided by the invention is good in heat dissipation effect, environmentally friendly and low in cost.

Description

technical field [0001] The invention relates to the technical field of novel paint preparation, in particular to a water-based paint with high heat dissipation performance and a preparation method thereof. Background technique [0002] With the promulgation of environmental protection regulations in various countries and the gradual enhancement of people's awareness of environmental protection, traditional solvent-based coatings have gradually withdrawn from the historical stage due to their high VOC (volatile organic compound) emissions. Environmentally friendly coatings are favored by everyone, and the development of green and environmentally friendly coatings has gradually become the development trend of future coating technology. Among them, water-based coatings stand out with their excellent comprehensive properties. Water-based paint is a kind of paint with water as a solvent. It has the advantages of odorless, non-toxic, non-polluting, low cost, and convenient constr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/00C09D163/00C09D5/24C09D5/08C09D7/61C09D7/65
CPCC09D133/00C08K2003/2227C08K2003/282C08K2201/011C08K2201/014C08L2205/02C08L2205/035C09D5/08C09D5/24C09D163/00C08L1/286C08L83/04C08L83/12C08K13/04C08K3/04C08K7/24C08K3/34C08K3/28C08K13/02C08K3/22C08L23/06
Inventor 李修兵李韦韦莫剑臣
Owner CHANGZHOU XICAI CARBON MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap