Magnesium alloy and magnesium alloy casting

A magnesium alloy and casting technology, applied in the field of magnesium alloy castings, can solve problems such as low creep strength, achieve excellent high temperature characteristics, excellent castability, and low cost

Inactive Publication Date: 2011-09-21
TOYOTA IND CORP
View PDF11 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In general Mg alloy parts, AZ91D etc. are mostly used, but the creep strength of this kind of Mg alloy parts is very low and it is not suitable for use in high temperature environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Magnesium alloy and magnesium alloy casting
  • Magnesium alloy and magnesium alloy casting
  • Magnesium alloy and magnesium alloy casting

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] Embodiments of the invention will be given to further describe the present invention in detail. In addition, the contents described in this specification, including the following embodiments, are applicable not only to Mg alloys but also to Mg alloy castings, and therefore are simply referred to as “Mg alloys” including Mg alloy castings as appropriate. In addition, whether or not any of the embodiments is optimal varies depending on objects, required performance, and the like.

[0035]

[0036] (1)Al

[0037] Al can be solid-dissolved in Mg crystal grains to increase the room temperature strength of the Mg alloy and improve the corrosion resistance of the Mg alloy. Moreover, if the amount of Al in the Mg alloy is increased, Al solid-solutes to supersaturation in its matrix (dendrites or α grains), thereby forming an Al-rich phase. The rich Al is relatively thermally unstable and will become a Mg-Al compound (Mn 17 al 12 ) and precipitated in the Mg matrix and Mg ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The Mg alloy comprises 2-6% of Al, Ca at a composition ratio (Ca / Al) of 0.5-1.5, 0.1-0.7% of Mn, 1-6% of Sr, and the remainder Mg and inevitable impurities and / or modified elements, when the total is 100 wt%. With this, an Mg alloy with excellent normal-temperature characteristics as well as creep resistance and high-temperature characteristics, such as thermal conductivity, was obtained.

Description

technical field [0001] The present invention relates to a magnesium alloy having excellent high temperature properties and a magnesium alloy casting formed from the magnesium alloy. Background technique [0002] Magnesium alloys (Mg alloys), which are lighter than aluminum alloys, are attracting attention due to an increase in demand for weight reduction in recent years. Magnesium alloys are the lightest among practical metals, and are gradually being used not only as materials for aircraft, but also as materials for automobiles. Parts formed of Mg alloys (Mg alloy parts) are lightweight and have excellent functionality. In addition, the use of Mg alloy parts can reduce the weight of vehicles and the like and achieve energy saving. [0003] Furthermore, when Mg alloy parts are used in vehicles, etc., high-temperature characteristics suitable for use in high-temperature environments, such as thermal conductivity, heat-resistant strength, and creep properties, are required i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C23/02B22D21/04C22C23/00C22F1/06C22F1/00
CPCC22C23/02B22D21/007C22F1/06C22C23/00C22C23/06
Inventor 冈本夕纪木下恭一谷泽元治赤塚裕哉
Owner TOYOTA IND CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap