Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A gold alloy and alloy technology, applied in the field of gold alloys, can solve the problems of poor color, affect quality, easy to be oxidized, etc., and achieve the effects of stable chemical properties, quality assurance, and long service life.
Inactive Publication Date: 2016-08-24
北海嘉华珠宝有限公司
View PDF3 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, because 14K gold is mixed with many other elements, some elements are easily oxidized in the case of long-term exposure in the air, and the color is not maintained well, which affects its quality.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0050] The present invention provides a kind of gold alloy, it is characterized in that, by weight percentage, comprises following composition:
[0051] 5% silver, 7% zinc, 5% copper, 2% niobium, 0.5% calcium, 0.5% zirconium, 4.5% erbium, 1% holmium, 1% epoxy resin, 0.2% curing agent, the rest is gold and unavoidable Impurities.
Embodiment 2
[0053] The present invention provides a kind of gold alloy, it is characterized in that, by weight percentage, comprises following composition:
[0054] 6.5% silver, 5% zinc, 4% copper, 3% niobium, 1.0% calcium, 0.8% zirconium, 3.5% erbium, 0.8% holmium, 2% epoxy resin, 0.5% curing agent, the rest is gold and unavoidable Impurities.
Embodiment 3
[0056] The present invention provides a kind of gold alloy, it is characterized in that, by weight percentage, comprises following composition:
[0057] 7% silver, 4.5% zinc, 3.5% copper, 3% niobium, 1.5% calcium, 0.5% zirconium, 4.5% erbium, 0.5% holmium, 3% epoxy resin, 1% curing agent, the rest is gold and unavoidable Impurities.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
Vickers hardness
aaaaa
aaaaa
density
aaaaa
aaaaa
Login to view more
Abstract
The invention relates to the technical field of alloys, and particularly relates to a gold alloy. The gold alloy comprises 5-10% of Ag, 3-7% of Zn, 2-5% of Cu, 2-4% of Nb, 0.5-1.5% of Ca, 0.5-1.5% of Zr, 2-4.5% of Er, 0.5-1% of Ho, 1-3% of epoxy resin and the balance of gold and inevitable impurities. The invention also provides a synthetic method of the gold alloy. The gold alloy provided by the invention has the advantages of excellent high-temperature property, very long service life, high-temperature resistance, oxidization resistance and creep resistance; gold jewelry made from the gold alloy has the advantages of low price, high hardness and long-lasting color and luster and can be worn for a long time.
Description
technical field [0001] The invention belongs to the technical field of alloys, in particular to a gold alloy. Background technique [0002] Gold alloy has a long history as a traditional material for producing gold jewelry. Usually, the gold alloy used in pure gold jewelry is 99.99% gold with 0.09% Cu or Ag metal added. The hardness is generally soft, so pure gold The product is easily deformed and is not suitable for inlaid jewelry. In addition, the color of pure gold is yellow, which is not fashionable enough in today's white jewelry. Therefore, common jewelry is made of 18K or 14K gold with a gold content of 75%. 25% of a piece of 18K gold jewelry is Ni, Cu, Zn, Ag and other metals, 14K gold jewelry has more than 58.33% of gold elements, and the rest are Cu, Zn, Ag and other metals. Since 14K gold can be mixed with more other elements than 18K gold, different colors can be adjusted, the hardness is high, the processing of inlaid gemstones is various, and the price is rel...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more