A method for preparing titanium alloy thin plates by cladding and rolling of steel plates

A titanium alloy plate and titanium alloy technology, applied in metal rolling and other directions, can solve problems such as high cost, poor bending performance, and poor surface condition, and achieve uniform vertical and horizontal properties, ensure performance stability, and reduce rolling costs. cheap effect

Inactive Publication Date: 2011-12-14
BAOJI TITANIUM IND
View PDF9 Cites 29 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to address the shortcomings of the above-mentioned prior art, and provide a method that can effectively solve the problems of long processing cycle, high cost, low product yield, low product elongation, poor surface condition and poor bending performance of the existing titanium alloy sheet. The method of preparing titanium alloy thin plate by cladding and rolling of steel plate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Finished product size 4.0×B×L mm

[0026] The steel plate used for cladding is Q235 with a thickness of 14mm; the titanium alloy plate clad with the steel plate is TC4 titanium alloy (corresponding to foreign brands such as GR5 / Ti6Al4V, etc.). The total thickness of the superimposed titanium alloy plate is 17mm; firstly, the surface of the steel plate and the titanium plate is cleaned; then the cleaned two steel plates are covered on the upper and lower sides of the titanium alloy plate, and steel strips are covered on the front, rear, left, and right sides of the titanium alloy plate; Gas-shielded welding is used to weld the upper and lower steel plates and side steel bars, and the titanium plate is sealed inside the steel plate to form a stacked rolling bag; uniformly distributed through holes are left on the side sealing plates around the stacked rolling bag, and the area of ​​the through holes occupies the entire side seal 3%~20% of the board area.

[0027] The sta...

Embodiment 2

[0032] Finished product size 4.0×B×L mm

[0033] Cladding rolling similar to Example 1. The difference is that the thickness of the titanium alloy sheet is increased to 10mm during cladding, the total cladding rolling deformation is increased to 60-70%, and the rolling temperature of cladding rolling is 900°C.

[0034] The steel plate used for cladding is Q235 with a thickness of 14mm; the titanium alloy plate clad with the steel plate is TC4 titanium alloy (corresponding to foreign brands such as GR5 / Ti6Al4V, etc.). The total thickness of the titanium alloy plate is 20mm; firstly, the surface of the steel plate and the titanium plate is cleaned; then the cleaned two steel plates are covered on the upper and lower sides of the titanium alloy plate, and steel strips are covered on the front, rear, left, and right sides of the titanium alloy plate; Gas shielded welding welds the upper and lower steel plates and side steel bars, and the titanium plate is sealed inside the steel ...

Embodiment 3

[0040] Finished product size 4.0×B×L mm

[0041] Cladding rolling similar to Example 1. The difference is that the thickness of the titanium alloy plate increases to 10mm during cladding, the total cladding rolling deformation increases to 60-70%, and the rolling temperature of cladding rolling is 950°C.

[0042] The steel plate used for cladding is Q235 with a thickness of 14mm; the titanium alloy plate clad with the steel plate is TC4 titanium alloy (corresponding to foreign brands such as GR5 / Ti6Al4V, etc.). The total thickness of the titanium alloy plate is 20mm; firstly, the surface of the steel plate and the titanium plate is cleaned; then the cleaned two steel plates are covered on the upper and lower sides of the titanium alloy plate, and steel strips are covered on the front, rear, left, and right sides of the titanium alloy plate; Gas shielded welding welds the upper and lower steel plates and side steel bars, and the titanium plate is sealed inside the steel plate ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a titanium alloy thin plate by cladding and rolling of a steel plate, and relates to a processing method of a metal plate. It is characterized in that the rolling process is that the titanium alloy plate is hermetically covered by a steel plate to form a stacked rolling bag, and then rolling is carried out. The method of the invention has low rolling cost, and the titanium alloy thin plate is produced by cladding, welding, stacking and hot rolling, the process is simple, and the comprehensive performance of the obtained material is excellent.

Description

technical field [0001] The invention discloses a method for preparing a titanium alloy thin plate by cladding and rolling of a steel plate, and relates to a processing method of a metal plate. Background technique [0002] Titanium alloy is a metal material with excellent performance, which is widely used in aviation, aerospace, chemical industry, electronics, sporting goods and other fields. Titanium alloy plate is an important product form, accounting for 40~60% of the total, but it is generally commercially available. The cold working capacity of titanium alloys is relatively low (about 20%). [0003] According to the traditional single-sheet rolling process, multiple hot rolling processes and multiple cold rolling processes are required to produce titanium alloy thin plates. Repeated heating in the middle of the hot rolling processes causes material surface contamination. In order to eliminate surface contamination, repeated alkali pickling is required, which increases t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B21B1/38
Inventor 任连保王俭王红武汪汉臣刘润生胡清熊陈东杨伟郑建民
Owner BAOJI TITANIUM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products