Lead paste for carbon lead storage battery and preparation method thereof

A battery and lead paste technology, which is applied to lead-acid battery electrodes, battery electrodes, circuits, etc., can solve problems such as difficulty in filling the lead paste, abnormal pressure of the opening and closing valve of the battery, and failure to reflect the efficacy of the carbon-lead plate.

Inactive Publication Date: 2012-06-13
河南晶能电源有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the current conventional formula and refining method of carbon-lead batteries, the maximum carbon black content can only account for 1% of the total proportion, which cannot reflect the efficacy of carbon-lead plates. When the carbon black content is high, it is very easy to appear refining and Inhomogeneity makes the filling operability of the lead paste very difficult, and the active material of the lead paste is prepared by conventional methods. During use, carbon black is easy to precipitate into the electrolyte and adhere to the rubber safety valve of the battery, causing the battery to open and close. Abnormal valve pressure, thus affecting the quality and service life of the battery

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Step 1: Uniformly disperse 70Kg lead powder, 0.2Kg fiber, 0.2Kg lignin, 0.3Kg humic acid, 0.3Kg barium sulfate, 20Kg PVA solution and 4Kg carbon black for 5-45 minutes to prepare a paste;

[0014] Step 2: Add 5Kg of sulfuric acid to the paste of the first step at a uniform speed for preparation. The time for adding sulfuric acid is controlled within 20 minutes. When adding sulfuric acid, the temperature is controlled not to exceed 40°C, and the temperature during the entire preparation process does not exceed 60°C. After the carbon lead viscosity is stable, the modulation is ended.

Embodiment 2

[0016] Step 1: Uniformly disperse 75Kg lead powder, 0.2Kg fiber, 0.15Kg lignin, 0.15Kg humic acid, 1.5Kg barium sulfate, 15Kg PVA solution and 3Kg carbon black for 5-45 minutes to prepare a paste;

[0017] Step 2: Add 5Kg of sulfuric acid to the paste of the first step at a uniform speed for preparation. The time for adding sulfuric acid is controlled within 20 minutes. When adding sulfuric acid, the temperature is controlled not to exceed 40°C, and the temperature during the entire preparation process does not exceed 60°C. After the carbon lead viscosity is stable, the modulation is ended.

Embodiment 3

[0019] Step 1: uniformly disperse 80Kg lead powder, 0.1Kg fiber, 0.1Kg lignin, 0.3Kg humic acid, 1.5Kg barium sulfate, 5Kg PVA solution and 8Kg carbon black for 5-45 minutes to prepare a paste;

[0020] Step 2: Add 5Kg of sulfuric acid to the paste of the first step at a uniform speed for preparation. The time for adding sulfuric acid is controlled within 20 minutes. When adding sulfuric acid, the temperature is controlled not to exceed 40°C, and the temperature during the entire preparation process does not exceed 60°C. After the carbon lead viscosity is stable, the modulation is ended.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a lead paste for carbon lead storage battery. The lead paste is prepared by the following raw materials of: by weight, 70-80 parts of lead powder with oxidisability being more than 73%, 0.02-0.2 part of fiber, 0.05-0.3 part of lignin, 0.05-0.3 part of humic acid, 0.3-1.5 parts of barium sulfate, 5-20 parts of a PVA solution with its content being 0.1-20%, 0.01-5 parts of sulfuric acid with its specific gravity being 1-1.4g / ml and 1-10 parts of carbon black. A preparation method of the lead paste contains steps of: preparing a paste, adding metered sulfuric acid into the prepared paste at uniform speed, modulating until the lead viscosity of carbon lead is stabilized. By the adoption of the formula and the preparation technology, the carbon distribution of the carbon lead paste can be uniform; the content of carbon black is raised up to more than 3%; and there will appear no carbon drawback. Therefore, advantages of carbon lead batteries can be fully presented.

Description

technical field [0001] The invention relates to a lead paste for a carbon-lead storage battery and a preparation method thereof, belonging to the technical field of lead-acid storage batteries. Background technique [0002] In the current conventional formula and refining method of carbon-lead batteries, the maximum carbon black content can only account for 1% of the total proportion, which cannot reflect the efficacy of carbon-lead plates. When the carbon black content is high, it is very easy to appear refining and Inhomogeneity makes the filling operability of the lead paste very difficult, and the active material of the lead paste is prepared by conventional methods. During use, carbon black is easy to precipitate into the electrolyte and adhere to the rubber safety valve of the battery, causing the battery to open and close. The abnormality of the valve pressure will affect the quality and service life of the battery. Contents of the invention [0003] The purpose of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/14H01M4/36H01M4/62
CPCY02E60/126Y02E60/10
Inventor 刘继民何海军
Owner 河南晶能电源有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com