Preparation method of flame-retardant putty

A technology of putty and main body, applied in the direction of filling slurry, etc., can solve the problems that the putty has no flame retardant performance, the heat resistance and flame retardant performance of the putty cannot meet the special requirements, etc. Good, flexible impact good effect

Inactive Publication Date: 2014-08-06
康月红
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent 94115901 discloses a formula and production method of "normal temperature quick-drying high-grade polymeric putty". The putty is mainly composed of mixed unsaturated resin, and has the characteristics of putty putty, fast drying, strong adhesion, flexibility and sandability. , good brushing properties, etc., but the resin used in this patent is an unsaturated polyester resin commonly used in putty, and the heat-resistant temperature is usually below 150°C. At the same time, the putty has no flame retardant performance, so the putty The heat resistance and flame retardancy cannot meet the special requirements of subway vehicles and other high-temperature places, such as front cars, axles, flues, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A method for preparing flame-retardant putty. The putty is composed of a main body and an initiator: the weight ratio of the main body and the initiator is 100:2, and the two components are mixed uniformly according to the ratio during use That is, the main body is composed of the following components in parts by weight: 50 parts of unsaturated polyester resin, 10 parts of silicone resin, 15 parts of saturated polyester resin, 8 parts of styrene, 0.03 parts of diacetyl oxime, 1.4 parts of cobalt isooctanoate, 5 parts of sodium bentonite, 9 parts of titanium dioxide, 5 parts of barium sulfate, 14 parts of talc; the initiator consists of the following ingredients in parts by weight: Cyclohexanone peroxide: 62 parts, ortho Dibutyl phthalate: 28 parts, SiO 2 : 14 parts, the preparation method includes the following steps:

[0015] (1) Main body: Put the unsaturated polyester resin, silicone resin, and saturated polyester resin into the dispersion tank according to the above ra...

Embodiment 2

[0019] A method for preparing flame-retardant putty. The putty is composed of a main body and an initiator: the weight ratio of the main body and the initiator is 100:2, and the two components are mixed uniformly according to the ratio during use That is, the main body is composed of the following components in parts by weight: 56 parts of unsaturated polyester resin, 15 parts of silicone resin, 12 parts of saturated polyester resin, 12 parts of styrene, and 0.02 parts of diacetyl oxime, 1.8 parts of cobalt isooctanoate, 3 parts of sodium bentonite, 11 parts of titanium dioxide, 3 parts of barium sulfate, 18 parts of talc; the initiator consists of the following components in parts by weight: Cyclohexanone peroxide: 58 parts, ortho Dibutyl phthalate: 32 parts, SiO 2 : 12 parts, the preparation method includes the following steps:

[0020] (1) Main body: Put the unsaturated polyester resin, silicone resin and saturated polyester resin into the dispersion tank according to the abov...

Embodiment 3

[0024] A method for preparing flame-retardant putty. The putty is composed of a main body and an initiator: the weight ratio of the main body and the initiator is 100:2, and the two components are mixed uniformly according to the ratio during use That is, the main body is composed of the following components in parts by weight: 53 parts of unsaturated polyester resin, 12 parts of silicone resin, 13.5 parts of saturated polyester resin, 10 parts of styrene, and 0.025 parts of diacetyl oxime, 1.6 parts of cobalt isooctanoate, 4 parts of sodium bentonite, 10 parts of titanium dioxide, 4 parts of barium sulfate, 16 parts of talc; the initiator consists of the following ingredients in parts by weight: Cyclohexanone peroxide: 60 parts, ortho Dibutyl phthalate: 30 parts, SiO 2 : 13 parts, the preparation method includes the following steps:

[0025] (1) Main body: Put the unsaturated polyester resin, silicone resin and saturated polyester resin into the dispersion tank according to the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thermal resistanceaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of flame-retardant putty and is characterized in that the putty comprises two components, namely a putty main body and initiating agent, wherein the weight ratio of the putty main body to the initiating agent is 100:2. During use, all that is needed to do is uniformly mix the two components in proportion. The putty main body comprises the following components by part by weight: unsaturated polyester resin, organosilicon resin, saturated polyester resin, phenethylene, diacetyl dioxime, cobalt iso-octoate, sodium bentonite, titanium dioxide, barium sulphate and talcum powder; the initiating agent comprises the following components: cyclohexanone peroxide, dibutlyl phthalate and SiO2; and the preparation method comprises the following steps: preparation of the putty main body, the preparation of the initiating agent, and mixing for use.

Description

Technical field [0001] The invention relates to the field of chemical coatings, in particular to a method for preparing flame-retardant putty. Background technique [0002] Flame-retardant putty usually refers to the base coating material of the metal surface inlay material, especially a normal temperature dry air-dry type organic silicon modified unsaturated flame-retardant putty. There are generally two types of filling materials used on metal surfaces: one is water-based putty, and the other is resin putty. Chinese patent CN86101069 discloses a formula named "crosslinked emulsion baking putty" and its production method. The putty uses water instead of organic solvents, which is non-flammable, non-toxic, harmless, and does not pollute the environment. However, the putty made by this patent must be baked at about 110°C for 50 minutes before it can be dried; such drying conditions greatly limit the use of its putty Due to large equipment and inconvenient moving accessories, it ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D5/34
Inventor 卢齐元
Owner 康月红
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com