Method for preparing metachromatic linear flat polyester filaments

A polyester filament and in-line technology is applied in the field of preparation of hetero-dyed in-line flat polyester filaments, which can solve the problems of lack of theoretical and practical guidance in the production of flat hetero-dyed polyester, and achieve a fresh appearance effect. Elegant, breathable, lightweight effect

Inactive Publication Date: 2012-07-18
SHAOXING UNIV YUANPEI COLLEGE
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Moreover, there are many researches on the specific process of acrylic fiber or cellulose fiber in the production and development of flat fiber at home and abroad, while there are few researches on the forming of flat polyester fiber, and there are fewer researches on product transformation on the basis of flat cross section. The production of flat heterodyed polyester lacks theoretical and practical guidance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing metachromatic linear flat polyester filaments
  • Method for preparing metachromatic linear flat polyester filaments
  • Method for preparing metachromatic linear flat polyester filaments

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0041] In this example, the main production materials and equipment are as follows: crystallization drying: FBCD-1 type of Beijing Dehoupu Chemical Technology Co., Ltd.; screw extruder: JWM65 of JWELL Machinery Manufacturing Co., Ltd.; filtration: Weihai Haida Technology Co., Ltd. The company's RLB7-30 type; metering, spinning box, and spinning components: Dalian Synthetic Fiber Institute; cooling air conditioner: Hangzhou Zhongfu Company; winding: Japanese Teijin machine; experimental materials: polyester chips and fiber materials. All raw materials etc. used in the present invention are all routinely used except special instructions, and can be purchased from the market; The equipment used is all purchased from the market except special instructions; The process method used, if not done In particular, all refer to conventional processes, such as the melting step in filament preparation or conventional processes in other steps, so details will not be repeated. In the present ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing metachromatic linear flat polyester filaments, which includes the steps of drying, melting, spinning, cooled oiling and hot-rolled winding. In the step of drying, crystallization temperature is 170 DEG C, crystallization time ranges from 15 minutes to 30 minutes, drying temperature is 175 DEG C, drying time ranges from 8 hours to 10 hours, the intrinsic viscosity of slices is lower than 0.005dL / g, and water content is below 20ppm. According to the technical scheme, thick-and-thin yarns are ingeniously applied to the flat filaments by means of non-uniform stretching on a conventional one-step spinning and drawing combination machine, the characteristics of flat sections and longitudinal non-uniform thicknesses are sufficiently combined, a fabric made of the flat filaments has the unique appearance effect of silk rain grains, and the defect of single style of a fabric made of pure flat fibers is overcome.

Description

technical field [0001] The invention relates to the field of chemical fibers, in particular to a method for preparing differently dyed in-line flat polyester filaments. Background technique [0002] With the rapid development of my country's economy, the textile industry has also ushered in another era of rapid development. People's consumption on food, clothing, housing and transportation has driven the development of the textile economy. Among them, the market not only has a strong demand for the quantity of textiles, but also requires the continuous improvement of the quality of textiles, and people's demand for the use and performance of textiles is developing in the direction of diversification and high quality. The performance requirements of fabrics that people expect are often excellent optical properties; good moisture absorption and breathability; light weight, water and sweat absorption, easy to wash and quick-dry; more comfortable hand feeling; Anti-fouling effe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01D5/253D01D1/00D01D5/088D01D5/096D01D5/12D01D7/00D01D10/02
Inventor 楼利琴
Owner SHAOXING UNIV YUANPEI COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap