Acid-washing hot-rolled low-carbon steel without line defects on surface and production method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A manufacturing method and low-carbon steel technology, applied in the field of steel smelting and rolling, can solve the problems of peak-shaped surface defects, inability to wait for a long time at high temperature, etc., and achieve the effect of reducing surface defects, improving surface quality, and realizing batch production.
Inactive Publication Date: 2012-08-08
武汉钢铁有限公司
View PDF2 Cites 19 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
2) Try to control the time of the slab in the furnace as much as possible. The time of the cold slab in the furnace is controlled at 160-180 minutes.
However, in actual production, it is found that when Cu, Sn, and As are less than 0.02%, hot-rolled low-carbon steel will still produce peak-shaped surface defects after pickling
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0016] Below in conjunction with specific embodiment the present invention is described in further detail:
[0017] A hot-rolled low-carbon steel with no shape defects on the surface after pickling, the composition of the hot-rolled low-carbon steel is calculated by weight percentage: C: 0.02-0.12%, Si: ≤0.05%, Mn: 0.10-0.60%, P: ≤0.015%, S: ≤0.010%, Cu: ≤0.10%, Ni: ≤0.10%, Cr: ≤0.05%, Als: 0.010~0.070%, Sn≤0.010%, As≤0.010%, Sb≤0.010 %, and As+Sn+Sb≤0.015%, the ratio of Ni to Cu≥0.5, and the balance is iron.
[0018] In the above technical solution, the ratio of As to Cu is ≤0.2, the ratio of Sb to Cu is ≤0.2, and the ratio of Sn to Cu is ≤0.2.
[0019] In the above technical solution, the enrichment amount of residual elements on the surface of the steel base is related to the residual element content of the steel. In particular, low-melting residual elements such as Sn, As, and Sb in steel should be strictly controlled. Therefore, the present invention stipulates that the...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses an acid-washing hot-rolled low-carbon steel without line defects on the surface and a production method thereof. The hot-rolled low-carbon steel consists of the following components in percentage by weight: 0.02 to 0.12 percent of C, 0.05 percent or less of Si, 0.10 to 0.60 percent of Mn, 0.015 percent or less of P, 0.010 percent or less of S, 0.10 percent or less of Cu, 0.10 percent or less of Ni, 0.05 percent or less of Cr, 0.010 to 0.070 percent of Als, 0.010 percent or less of Sn, 0.010 percent or less of As, 0.010 percent or less of Sb and the balance of iron; moreover, As plus Sn plus Sb are less than or equal to 0.015 percent, and the ratio of Ni to Cu is greater than or equal to 0.5. The production method of the hot-rolled low-carbon steel includes the following steps: after molten iron desulfurization and converter blowing, a raw sheet billet of the hot-rolled low-carbon steel is obtained, and the raw sheet billet of the hot-rolled low-carbon steel sequentially is subjected to continuous casting, heating, scale removal before rough rolling, rough rolling, finish rolling, laminar flow cooling, rolling, fan cooling and acid-washing. While the mechanical property of the steel is guaranteed by the components of the raw steel, the surface defects of the acid-washinghot-rolled low-carbon steel are reduced, consequently, the surface quality of the steel is greatly increased, and economic loss is reduced.
Description
technical field [0001] The invention relates to the technical field of steel smelting and rolling, in particular to a hot-rolled low-carbon steel with no surface defects after pickling and a manufacturing method thereof. Background technique [0002] With the improvement of users' requirements for steel quality, the requirements for steel surface quality are also getting higher and higher. On the other hand, in order to promote the recycling of steel and reduce the resource consumption of the whole society, steel production enterprises usually add a certain amount of scrap steel when making steel. Since the scrap steel contains a certain amount of residual elements, if the production process is not properly controlled, Will inevitably bring surface quality problems. Especially for low-carbon steel, surface defects like peaks, black lines or dots are more likely to appear on the surface after pickling, which seriously affects the surface quality of the product. economic los...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.