Fluorgypsum-based cementing materials for filling tailings and preparation method thereof
A technology of tailings filling and fluorogypsum, which is applied in the direction of cement production, etc., can solve the problems of restricting the use and development of filling technology, the high cost of tailings filling, and the low strength of consolidated bodies, achieving low cost and weathering resistance Good, good filling performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
experiment example 1
[0048] 1. Production of cementitious materials: Step 1: first adjust the pH of the fluorogypsum to make it weakly alkaline; Step 2: weigh 25% of modified fluorogypsum, 13% of cement clinker, 15% steel slag, 47% slag; grind the weighed modified fluorogypsum with a ball mill until the specific surface area is 805.7 m 2 / kg, then mixed with powdered slag, steel slag, cement clinker and mixed uniformly to obtain base material; Step 3: take 98% base material and 2% sulfate activator according to mass percentage, and mix uniformly, That is, the fluorogypsum-based cementitious material for tailings filling is prepared.
[0049] 2. Tailings consolidation experiment. Add the cementitious material prepared above to the tailings according to the lime-sand ratio of 1 / 8, pour into the mortar mixer and mix evenly, add water at a concentration of 70%, stir for 3 minutes, pour the stirred material into the selected test mold (70.7mm ×70.7mm×70.7mm), let stand for a period of time, c...
Embodiment 2
[0053] 1. Production of cementitious materials: Step 1: Prepare modified fluorogypsum for later use; Step 2: Take 25% modified fluorogypsum, 5% cement clinker, 25% steel slag, 45 % of slag; the weighed modified fluorogypsum was ground with a ball mill until the specific surface area was 832.1 m 2 / kg, then mixed with powdered slag, steel slag, cement clinker and mixed uniformly to obtain base material; Step 3: take 99% base material and 1% sulfate activator according to mass percentage, and mix uniformly, That is, the fluorogypsum-based cementitious material for tailings filling is prepared.
[0054] 2. Tailings consolidation experiment: configure cementitious material according to the above ratio, then add tailings according to the ratio of lime to sand 1 / 8, pour into the cement sand mixer and mix evenly, add water according to the concentration of 70%, stir for 3 minutes, and mix the mixed material Pour it into the selected test mold (70.7mm×70.7mm×70.7mm), let it stan...
Embodiment 3
[0058] 1. Production of cementitious materials: Step 1: Prepare modified fluorogypsum for later use; Step 2: Take 38% modified fluorogypsum, 10% cement clinker, 15% steel slag, 37 % of slag; the weighed modified fluorogypsum was ground with a ball mill until the specific surface area was 829.3 m 2 / kg, then mixed with powdered slag, steel slag, cement clinker and mixed uniformly to obtain base material; Step 3: take 97% base material and 3% sulfate activator according to mass percentage, and mix Uniform, that is, the fluorogypsum-based cementitious material for tailings filling is obtained.
[0059] 2. Tailings consolidation experiment: configure cementitious material according to the above ratio, then add tailings according to the ratio of lime to sand 1 / 8, pour into the cement sand mixer and mix evenly, add water according to the concentration of 70%, stir for 3 minutes, and mix the mixed material Pour it into the selected test mold (70.7mm×70.7mm×70.7mm), let it stan...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap