Cooking process for carrying out composite modification on natural color bamboo paper pulp and natural color wood pulp to form dissolving pulp

A composite modification, bamboo pulp technology, applied in the field of dissolving pulp, can solve the problems of large chemical consumption, the quality index of dissolving pulp cannot reach the dissolving pulp, and the raw materials are single.

Active Publication Date: 2012-09-19
YIBIN GRACE GROUP CO LTD
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the bamboo pulp prepared by this invention has the following disadvantages: 1, the yield is low, and the highest yield is only 85%
2. The α-cellulose content fluctuates greatly, from 85% to 95%, which makes the modified bamboo pulp α-cellulose content unstable
3. The average length of fibers is lower than that of paper-making wood fibers, and the content of ash and polypentose in the production process is high, and the bamboo fibers are hard, have more thick-walled fibers, narrow cell lumens, dense fiber tissues, and the presence of air in the cells leads to dissolution Difficult, large amount of chemicals
4. The viscose fiber produced by a single bamboo pulp has monotonous performance and does not show individuality
But this invention is only applicable to the modification of cotton linters and is prepared into viscose fiber. If the composite material is modified by the method provided by the invention to prepare dissolving pulp, the quality index of the modified dissolving pulp cannot reach that of dissolving pulp. Requirements, and high energy consumption, low yield
[0007] To sum up, the above-mentioned invention patents mainly have the following disadvantages: 1. The raw material is single, and the dissolving pulp produced has single performance and does not show individuality
2. A single raw material has its own disadvantages, such as high production cost, low yield, and unstable product quality
3. Outdated production equipment, high energy consumption, and uneven cooking

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A. Prepare materials

[0036] The composite pulp board in which natural bamboo pulp accounts for 40% of the composite pulp board is dispersed with a dispersing device such as a bagger, meal feeder, leaf splitter, etc., and the cutting equipment and crushing equipment such as a pulper and a pulverizer are used to disperse the mixed pulp board. Crush the pulp sheet into flocculent form, and send the flocculent composite pulp sheet into the cooking equipment with conveying equipment (fan, cyclone separator, screw conveyor). Liquid, this stock preparation method is called dry stock preparation, and its technological requirements are: a, pulp input amount 4 tons / batch, b, alkali addition amount (with fiber dry weight percentage) 13 ~ 30%, C, liquid ratio 1: 2.0, d. Requirements for quality indicators: Natural bamboo pulp has a cellulose content of 94%, a degree of polymerization of 1200, and an ash content of 0.5%. The natural color wood pulp has a cellulose content of 91%, ...

Embodiment 2

[0049] A. Prepare materials

[0050] The composite pulp board in which natural bamboo pulp accounts for 40% of the composite pulp board is dispersed with a dispersing device such as a bagger, meal feeder, leaf splitter, etc., and the cutting equipment and crushing equipment such as a pulper and a pulverizer are used to disperse the mixed pulp board. Crush the pulp sheet into flocculent form, and send the flocculent composite pulp sheet into the cooking equipment with conveying equipment (fan, cyclone separator, screw conveyor). liquid, this preparation method is called dry preparation, and its process requirements are: a, 5 tons / batch of pulp input, b, 15% alkali addition (percentage of absolute dry weight of fiber), C, liquid ratio 1:3.0, d. Requirements for quality indicators: Natural bamboo pulp has a cellulose content of 95%, a degree of polymerization of 1000, and an ash content of 0.5%. The natural color wood pulp has a cellulose content of 93%, a degree of polymerizatio...

Embodiment 3

[0063] A. Prepare materials

[0064] The composite pulp board in which natural bamboo pulp accounts for 40% of the composite pulp board is dispersed with a dispersing device such as a bagger, meal feeder, leaf splitter, etc., and the cutting equipment and crushing equipment such as a pulper and a pulverizer are used to disperse the mixed pulp board. Crush the pulp sheet into flocculent form, and send the flocculent composite pulp sheet into the cooking equipment with conveying equipment (fan, cyclone separator, screw conveyor). Liquid, this method for preparing materials is called dry method for preparing materials, and its process requirements are exactly the same as in Example 1.

[0065] Material preparation can also be prepared by wet method. The specific steps are: using dispersing device (packing machine, meal feeder, pulper, deflagging machine) → alkali mixing device → mixing device (dipping bucket) → dehydration device (pressing machine) , Pulping machine) → crushing ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
Ash contentaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a cooking process for carrying out composite modification on natural color bamboo paper pulp and natural color wood pulp to form dissolving pulp. Composite paper pulp is fed into a continuous digester to be cooked; a continuous steaming pipe of the continuous digester is provided with three sections; the section connected with a pre-reaction bin is provided with a T-shaped pipe for adding alkali liquor and a steam pipe for adding steam; the other two sections are provided with steam pipes for adding the steam; the liquor ratio is 1:(2.0 to 4.0); the alkali liquor is NaOH and Na2SO3 and is added according to 17 percent to 30 percent of the oven dry weight; and the compression ratio is 1:(2 to 3.0). According to the invention, the natural color bamboo paper pulp and the natural color wood pulp are used as the raw materials, so that the cost of preparing the dissolving pulp is reduced to a great extent and the quality requirement of the dissolving pulp for viscose is also met.

Description

technical field [0001] The present invention relates to a method for compound modification of natural bamboo pulp and natural wood pulp into dissolving pulp, in particular to a method for compound modification of natural color bamboo pulp and natural wood pulp into dissolving pulp, wherein the dissolving pulp refers to pulp for viscose fiber Meal, cellulose and cellulose derivatives. Background technique [0002] The application number is 200710050470.9, the authorized announcement number is CN101158125, and the authorized announcement date is April 9, 2008. The Chinese invention patent discloses a paper-making grade coniferous wood pulp board modification process, wherein the cooking process uses paper-making grade wood pulp board Use caustic soda method, sulfate method or sulfite method for cooking, and the cooking agents are NaOH, NaOH+Na 2 S, Na 2 SO 3 + NaOH, the process conditions are: 1. The total alkali concentration of the cooking liquid by the caustic soda meth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21C3/04D21H11/20
Inventor 薛勤徐发祥于渭东刘爱兵陈昌明谢鹏于彬杨大平竭发全邬龙
Owner YIBIN GRACE GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products