A double-sided light-transmitting dye-sensitized solar cell photoanode

A technology of solar cells and dye sensitization, applied in the field of photoanode of double-sided light-transmitting dye-sensitized solar cells, can solve the problems of low short-circuit current density of cells, unfavorable large-scale production, disordered carrier transport, etc. The effect of mobility and low recombination rate, light weight, and easy growth preparation

Active Publication Date: 2016-01-20
PEKING UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its messy nanostructure leads to disordered carrier transport, which is manifested in the low short-circuit current density of the battery macroscopically.
And the complexity of the structure process makes practical application difficult, which is not conducive to large-scale production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A double-sided light-transmitting dye-sensitized solar cell photoanode
  • A double-sided light-transmitting dye-sensitized solar cell photoanode
  • A double-sided light-transmitting dye-sensitized solar cell photoanode

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Embodiment 1, prepare the photoanode of dye-sensitized solar cell

[0030] 1) Soak stainless steel wire mesh (specification: 635 mesh) in acetone solution, ultrasonically clean for 30 minutes to remove surface organic matter; then put the cleaned stainless steel wire mesh into concentrated sulfuric acid (98% by mass) and hydrogen peroxide volume Soak in a mixed solution with a ratio of 4:1 at 95° C. for 30 minutes, then rinse with deionized water three times to obtain a stainless steel wire mesh with a passivated surface.

[0031] 2) Deposit aluminum-doped zinc oxide nanowire arrays on the surface of passivated stainless steel wire mesh by chemical vapor deposition; the specific method is: mix powder of zinc powder and aluminum trichloride (mass ratio 3:1) Put it into a tube furnace and heat it to 700°C, feed 100 sccm of argon as the carrier gas, 8 sccm of oxygen as the reaction gas, stainless steel wire mesh in the downstream of the gas, and the deposition time is 5 mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a double-sided translucent dye-sensitized solar cell photoanode and a preparation method thereof. The photoanode is a stainless steel mesh or pure metal wire mesh deposited with zinc oxide nanowire array or aluminium-doped zinc oxide nanowire array on the surface. The flexible double-sided translucent dye-sensitized solar cell photoanode disclosed by the invention is simple and convenient in preparation method, and takes zinc powder enriched in the natural world as raw material; and the zinc oxide nanowire array is deposited on the stainless steel mesh or pure metal wire mesh, so that the manufacturing cost is greatly lowered. The double-sided translucent dye-sensitized solar cell photoanode is wide in application; if a transparent flexible substrate is used for packaging, real flexibility function can be realized; and under the condition of bending, the photovoltaic property is not obviously reduced. Glass is also can be used for conventional packaging, so that a double-sided light entrance solar cell can be realized. Due to the unique manufacturing technology, large-scale roll-to-roll industrial production can be very easily realized, and the application prospect is very wide.

Description

technical field [0001] The invention relates to a double-sided light-transmitting dye-sensitized solar cell photoanode. Background technique [0002] In order to solve the energy problem, the development of low-cost, easy-to-use, and high-performance new solar cells has been continuously carried out. Dye solar cells have been greatly developed in scientific research and practical applications all over the world due to their low manufacturing cost, high conversion efficiency, and the high abundance of the materials they rely on in the earth's crust. In recent years, dye-sensitized solar cells on flexible substrates have attracted increasing attention due to their good bendability and ease of large-area production. Most flexible dye-sensitized solar cells use metal foils or plastic films as substrates. Stainless steel wire mesh has attracted the attention of the international scientific research field in recent years due to its advantages such as higher surface area to mass ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01L31/0224H01G9/042H01G9/20
CPCY02E10/542Y02P70/50
Inventor 赵清王伟李恒俞大鹏
Owner PEKING UNIV
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com