Modified PET (polyethylene terephthalate) composite material and preparation method thereof
A composite material and modification technology, which is applied in the field of modified PET composite materials and its preparation, can solve the problems of low crystallization degree, poor mechanical properties, slow crystallization rate, etc., achieve low cost, reduce production and accumulation, and increase crystallinity and the crystallization rate effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0034] A kind of preparation method of modified PET composite material, it comprises following preparation steps:
[0035] Step A: Dry 41kg of PET resin with a relative density of 1.35, a melting point of 255°C and an intrinsic viscosity of 0.6dL / g at 100°C for 2 hours, and set aside;
[0036] Step B: Add the dried PET resin and 0.2kg KH-560 into a high-speed mixer, and stir for 3 minutes to obtain the first mixed material;
[0037] Step C: Add 0.8kg of silicone powder, 12kg of brominated epoxy resin with a relative molecular weight of 15000 and a mass content of bromine of 51%, 4kg of antimony trioxide, and 0.5kg of antioxidant in the first mixed material 1010, 0.5㎏ Antioxidant 168, 1㎏ nano-montmorillonite with a particle size of 1-100nm, 2㎏ carboxylate, 0.5㎏TPP, 0.5㎏ PEG-400 and 0.5㎏ PEG-1000, continue stirring for 3-8 Minutes, obtain the second mixed material;
[0038] Step D: The second mixed material and 36.5kg of continuous glass fibers with a diameter of 4-17 microns ...
Embodiment 2
[0040] A kind of preparation method of modified PET composite material, it comprises following preparation steps:
[0041] Step A: Dry 50kg of PET resin with a relative density of 1.36, a melting point of 258°C and an intrinsic viscosity of 0.7dL / g at 100°C for 3 hours, and set aside;
[0042] Step B: Add the dried PET resin and 0.5kg KH-560 into a high-speed mixer, and stir for 4 minutes to obtain the first mixed material;
[0043] Step C: add 1 ㎏ PETS, 10 ㎏ relative molecular weight is 20000, the mass content of bromine is 52% brominated epoxy resin, 3 ㎏ polytetrafluoroethylene, 0.2 ㎏ antioxidant 1010 and 0.4㎏ Antioxidant 168, 0.4㎏ Attapulgite Clay with a particle size of 1-100nm, 1㎏ Aryl Phosphate NA-21 [Methylenebis(2,4-di-tert-butylphenyl) Aluminum Phosphate], 0.3㎏TPP, 0.2㎏PEG-400 and 0.2㎏PEG-1000, continue stirring for 5 minutes to obtain the second mixture;
[0044] Step D: The second mixed material and 32.8 kg of continuous glass fibers with a diameter of 4-17 micron...
Embodiment 3
[0046] A kind of preparation method of modified PET composite material, it comprises following preparation steps:
[0047] Step A: Dry 66 kg of PET resin with a relative density of 1.38, a melting point of 260°C and an intrinsic viscosity of 0.8 dL / g at 100°C for 4 hours, and set aside;
[0048] Step B: Add the dried PET resin and 1kg KH-560 into a high-speed mixer, and stir for 5 minutes to obtain the first mixed material;
[0049] Step C: add 1㎏ silicone powder, 1㎏ PETS, 7㎏ bromine-containing flame retardant to the first mixed material as a brominated epoxy resin with a relative molecular weight of 30000 and a mass content of bromine of 53%, 1㎏ Antimony pentoxide, 1kg polytetrafluoroethylene, 0.2kg antioxidant 1010, 0.8kg antioxidant 168, 0.2kg nano-montmorillonite with a particle size of 1-100nm, 0.3kg carboxylate, 0.1kg TPP, 0.2㎏ PEG-400 and 0.2㎏ PEG-1000, continue stirring for 8 minutes to obtain the second mixed material;
[0050] Step D: The second mixed material and ...
PUM
Property | Measurement | Unit |
---|---|---|
diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
melting point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap