Lubricating grease composition for automobile glass lifter and preparation method of lubricating grease composition

A grease composition and technology for automotive glass, applied in the field of grease, can solve problems such as poor lubrication, low oxidation resistance, low evaporation loss, shear stability, poor performance, etc., and achieve outstanding water resistance and excellent low temperature and viscosity-temperature performance, and the effect of low oil separation rate

Active Publication Date: 2013-01-16
CHINA PETROLEUM & CHEM CORP
View PDF2 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The object of the present invention is to propose a kind of lubricating grease composition and preparation method thereof for automotive window regulators, the lubricating grease has outstanding water resistance, Good oxidation resistance, low oil separation rate, small evaporation loss, high shear stability, high and low temperature performance and excellent anti-corrosion protection effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lubricating grease composition for automobile glass lifter and preparation method of lubricating grease composition
  • Lubricating grease composition for automobile glass lifter and preparation method of lubricating grease composition
  • Lubricating grease composition for automobile glass lifter and preparation method of lubricating grease composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Embodiment 1: each component comprises by the total weight of composition:

[0027] (1) Base oil 89.5%;

[0028] (2) Thickener 9.5%;

[0029] (3) Antioxidant 0.5%;

[0030] (4) Antirust agent 0.03%;

[0031] (5) 0.5% tackifier.

[0032] Mix 80 grams of 12-hydroxystearic acid, 20 grams of hexadecanoic acid and 430 grams of base oil (the freezing point is -30°C, the viscosity at 100°C is 8mm 2 / s) into the reaction kettle, heated to 80-85°C, and added an aqueous solution of 11.2 grams of lithium hydroxide monohydrate and 2.2 grams of calcium hydroxide. Heat to 90-105°C to start timing saponification. After saponification, heat up to 200-220°C and cool with 215g of base oil in the reactor. After cooling, when the temperature is controlled at 160-190°C, add 6.5g of poly Methacrylate and the remaining 430g of base oil, after the temperature drops to 80°C, add 3.75 grams of 4,4-methylene bis-2,6-di-tert-butyl p-cresol, 3.75 grams of dibutyloctyldithioamino Zinc formate ...

Embodiment 2

[0035] Embodiment 2: each component comprises by the total weight of composition:

[0036] (1) Base oil 88.0%;

[0037] (2) Thickener 11.0%;

[0038] (3) Antioxidant 0.5%;

[0039] (4) Antirust agent 0.03%;

[0040] (5) 0.5% tackifier.

[0041] Mix 90 grams of 12-hydroxystearic acid, 15 grams of hexadecanoic acid and 378 grams of base oil (the freezing point is -40°C, and the viscosity at 100°C is 6mm 2 / s) into the reaction kettle, heated to 80-85°C, and added an aqueous solution of 11.5 grams of lithium hydroxide monohydrate and 2.3 grams of calcium hydroxide. Heat up to 90-105°C to start timing saponification. After saponification, heat up. After the temperature rises to 200-220°C, use 189g of base oil to cool in the reactor. After cooling, when the temperature is controlled at 160-190°C, add 5.3 grams of ethyl alcohol. Propylene copolymer and the remaining 378g of base oil, after the temperature reaches 80°C, add 2.65 grams of 2,6-di-tert-butyl-p-cresol and 2.65 grams...

Embodiment 3

[0044] Embodiment 3: each component comprises by the total weight of composition:

[0045] (1) Base oil 91.5%;

[0046] (2) Thickener 7.5%;

[0047] (3) Antioxidant 0.5%;

[0048] (4) Antirust agent 0.03%;

[0049] (5) 0.5% tackifier.

[0050] Mix 80 grams of 12-hydroxystearic acid, 10 grams of hexadecanoic acid and 508 grams of base oil (the freezing point is 42°C, the viscosity at 100°C is 8mm 2 / s) into the reaction kettle, heated to 80-85°C, and added 13.41 grams of lithium hydroxide monohydrate aqueous solution. Heat up to 90-105°C to start timing saponification. After saponification, heat up. After the temperature rises to 200-220°C, cool with 254g of base oil in the reactor. After cooling, when the temperature is controlled at 160-190°C, add 6.94g of polyform base acrylate and remaining 508g of base oil. After the temperature drops to 80°C, add 3.47 grams of 2,6-di-tert-butyl-p-cresol and 3.47 grams of zinc dibutyloctyldithiocarbamate additives and 0.42 grams of ca...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
dew pointaaaaaaaaaa
dew pointaaaaaaaaaa
dew pointaaaaaaaaaa
Login to view more

Abstract

The invention provides a lubricating grease composition for an automobile glass lifter and a preparation method of the lubricating grease composition. The lubricating grease for the automobile glass lifter comprises the following ingredients in percentage by weight: 87 to 91.5 percent of basic oil, 7.5 to 12 percent of thickening agents, 0.5 percent of antioxidants, 0.03 percent of anti-rust agents and 0.5 percent of structure improving agents. The unique mixed thickening agent type is adopted, so the water-resistance and shearing performance of the lubricating grease are excellent, good low-temperature and viscosity-temperature performance is given to the lubricating agent through the proper basic oil type and mixture ratio, and the wide temperature use requirement being minus 40 DEG C to 70 DEG C of the automobile glass lifter accessories can be perfectly met. The prepared lubricating grease has the characteristics that the water resistance and the oxidation resistance are excellent, the oil rate is low, the evaporation loss is small, the shearing stability is high, the high-low temperature performance and the anti-corrosion protection effect are good, and the like, the use requirements of the automobile glass lifter can be perfectly met, and the use temperature range of the lubricating grease is minus 40 DEG C to 130 DEG C.

Description

technical field [0001] The invention belongs to the technical field of lubricating grease, and in particular relates to a lubricating grease composition for an automobile window regulator and a preparation method. Background technique [0002] Automotive body accessories grease is mainly used for body shells, doors, doors and windows, roof windows, seats, etc. Automotive body accessories include window regulators, windshield wipers, door locks, door hinges, armrests, and more. The lubricating grease used for body accessories is basically lubricated for life, and the working conditions of various parts are quite different. The lubricating grease must be targeted to meet the use requirements. [0003] The glass lifting mechanism is an important part of the car door system. With the improvement of people's requirements for the comfort and safety of the car, more and more attention is paid to the use of the glass lifting mechanism. In general, the glass regulator should have s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C10M169/06C10M177/00C10N40/04
Inventor 吴凤华刘洋高艳青吴宝杰赵宏菲
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap