Method for preparing single domain yttrium barium copper oxide superconduction block

A technology of yttrium barium copper oxide and seed crystal infiltration is applied in the directions of polycrystalline material growth, chemical instruments and methods, single crystal growth, etc. It can solve the problems of long preparation time and high process cost, achieve large magnetic levitation force and simplify experiments The effect of shortening the experimental period

Active Publication Date: 2013-02-13
SHAANXI NORMAL UNIV
View PDF3 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to overcome the technical problems of long preparation time and high process cost, the invention provides a kind of Only need to pre-prepare a BaCuO 2 The precursor powder can meet the needs of preparing solid-phase source and liquid-phase source powder, and the prepared single-domain yttrium-barium-copper-oxide superconducting block has high magnetic levitation force and is easy to grow directionally. Domain YBCO superconducting bulk method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing single domain yttrium barium copper oxide superconduction block
  • Method for preparing single domain yttrium barium copper oxide superconduction block
  • Method for preparing single domain yttrium barium copper oxide superconduction block

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] With the raw material Y used 2 o 3 Taking the initial powder of the solid-phase precursor powder as an example, the method for preparing monodomain yttrium-barium-copper-oxygen superconducting bulk material with the top seed crystal infiltration method consists of the following steps:

[0041] (1) Preparation of solid phase precursor powder

[0042] Take 106.9064g BaCO 3 Mix evenly with 43.0936g CuO in a molar ratio of 1:1, and make BaCuO by solid state reaction method 2 Powder, the Y 2 o 3 Primary powder and BaCuO 2 The powder is mixed in a molar ratio of 1:1.2, and 100g of the mixed powder is added to a ball mill and mixed to make (Y 2 o 3 +1.2BaCuO 2 ) solid phase precursor powder;

[0043] (2) Preparation of liquid source powder

[0044] Take 106.9064g BaCO 3 Mix evenly with 43.0936g CuO in a molar ratio of 1:1, and sinter into BaCuO by solid state reaction method 2 Powder, take 11.17g Y 2 o 3 The initial powder and 23.61g CuO, 115.21g BaCuO 2 The pow...

Embodiment 2

[0059] With the raw material Y used 2 o 3 Powder is used as the initial powder of solid-phase precursor powder as an example, and the method for preparing monodomain yttrium-barium-copper-oxygen superconducting bulk material with the top seed crystal infiltration method is made up of following steps:

[0060] (1) Preparation of solid phase precursor powder

[0061] Take 106.9064g BaCO 3 Mix evenly with 43.0936g CuO in a molar ratio of 1:1, and make BaCuO by solid state reaction method 2 Powder, the Y 2 o 3 Primary powder and BaCuO 2 The powder is mixed in a molar ratio of 1:1, and 100g of the mixed powder is added to a ball mill and mixed evenly to make (Y 2 o 3 +BaCuO 2 ) solid phase precursor powder;

[0062] (2) Preparation of liquid source powder

[0063] Take 106.9064g BaCO 3 Mix evenly with 43.0936g CuO in a molar ratio of 1:1, and sinter into BaCuO by solid state reaction method 2 Powder, take 11.17g Y 2 o 3 The initial powder and 23.61gCuO, 115.21g BaCuO ...

Embodiment 3

[0074] With the raw material Y used 2 o 3 Powder is used as the initial powder of solid-phase precursor powder as an example, and the method for preparing monodomain yttrium-barium-copper-oxygen superconducting bulk material with the top seed crystal infiltration method is made up of following steps:

[0075] (1) Preparation of solid phase precursor powder

[0076] Take 106.9064g BaCO 3 Mix evenly with 43.0936g CuO in a molar ratio of 1:1, and make BaCuO by solid state reaction method 2 Powder, the Y 2 o 3 Primary powder and BaCuO 2 The powder is mixed in a molar ratio of 1:2.5, and 100g of the mixed powder is taken and added to a ball mill for mixing to make (Y 2 o 3 +2.5BaCuO 2 ) solid phase precursor powder;

[0077] (2) Preparation of liquid source powder

[0078] Take 106.9064g BaCO 3 Mix evenly with 43.0936g CuO in a molar ratio of 1:1, and sinter into BaCuO by solid state reaction method 2 Powder, take 11.17g Y 2 o 3 The initial powder and 23.61gCuO, 115.2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing a single domain yttrium barium copper oxide superconduction block. Through changing components of solid phase source powder and liquid phase source powder which are used in a solid phase block, the whole infiltration growth process only needs precursor powder of BaCuO2, thus the experiment links are simplified, the experiment period is shortened, the experiment cost is lowered, and the efficiency is increased; and the single domain yttrium barium copper oxide superconduction block prepared by adopting the method provided by the invention has large magnetic levitation force and is beneficial to prevention of loss of a liquid phase and collapse of a sample, the full contact of the liquid phase with the solid phase and the orientated growth of crystals by adopting an assembly method that a liquid phase block is slightly larger than or equal to a solid phase precursor block in size.

Description

technical field [0001] The invention belongs to the technical field of high-temperature copper oxide superconducting materials, and in particular relates to the preparation of monodomain yttrium-barium-copper-oxygen superconducting block materials by a top seed crystal infiltration growth method. Background technique [0002] Monodomain copper oxide high temperature superconducting bulk material (RE-Ba-Cu-O, where RE is a rare earth element, such as Nd, Gd, Y, etc.) has a high critical temperature and critical current density, and has a strong magnetic field Strong flux pinning capability. This advantage has laid the foundation for the application of this type of material in magnetic levitation technology, especially in the development of superconducting magnetic levitation bearings, energy storage flywheels, and superconducting motors and generators. In the process of preparing single-domain copper oxide superconducting bulk materials, there are two main applications, one ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C30B1/00C30B29/22C04B35/45
Inventor 杨万民王孝江王明梓
Owner SHAANXI NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com