A technology of automatic feeding and baking device, applied in the field of metallurgical industry, can solve the problems of increased operation interference, poor manual working environment, silicon burning loss, etc., and achieves the effect of high degree of automation

Inactive Publication Date: 2013-02-20
WISDRI ENG & RES INC LTD
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Alloy baking can solve the following problems: (1) After a large amount of alloy is damp, it is easy to add H to the molten steel, and the billet forms "white spots", which makes the steel brittle; (2) After the alloy is added to the ladle, it absorbs a lot of heat, and the converter is Forced to increase the tapping temperature, which not only deteriorates the quality of molten steel, but also reduces the life of the converter, causing many adverse effects on the production organization; (3) Low-temperature silicon is easy to oxidize, resulting in excessive burning of silicon and reducing the yield of silicon
[0006] This process method has the following disadvantages: (1) The material can be loaded by the material tank, and the amount of alloy added to the baking furnace cannot be precisely controlled
(2) The level of mechanization and automation is low, and the artificial working environment is poor
(3) Manual operation is not easy to accurately control the time point of alloy addition, and cannot match the production rhythm well
(4) It is only suitable for smelting silicon steel with small-scale converters. If large-scale converters are used to smelt silicon steel, the amount of baked alloy added to the converter will increase. If forklifts are still used to transport the baked alloys, the number of forklifts will increase and the operation will be more disturbed. , cannot meet the requirements of alloy transportation, it is necessary to develop a device that can add a large amount of alloy at one time to meet the requirements of large-scale converter baking alloy feeding

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method and device for automatic loading of roasting alloys in silicon steel production
  • Method and device for automatic loading of roasting alloys in silicon steel production
  • Method and device for automatic loading of roasting alloys in silicon steel production

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0036] Below in conjunction with specific embodiment, the present invention is further described:

[0037] Such as Figure 4 The shown automatic feeding device for baking alloys used in silicon steel production includes a conveying device, a baking device, a summarizing device, and an electric control system connected to the three, wherein the conveying device is a vertical belt conveyor 2, and its The bottom end is connected to the alloy underground silo 1, and the top is provided with a feeding port, wherein the roasting device includes a plurality of alloy roasters 4 arranged side by side, and an upper and lower position along the alignment direction of the alloy roasters 4 is arranged in parallel. For the guide rails, a slidable upper weighing trolley 3 is installed on the upper guide rail, and the upper weighing trolley 3 can move to the feeding port, and the lower guide rail extends out of the area of ​​the alloy roaster 4, and a slidable lower trolley is installed on it...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a method and a device for automatic loading of roasting alloys in silicon steel production. The device comprises a delivery device, a roasting device, a gathering device and an electric control system, wherein the electric control system is connected with the delivery device, the roasting device and the gathering device respectively, the roasting device comprises a plurality of parallel alloy roasting devices which are arranged in a row, a pair of guide rails are arranged in a parallel mode at upper and lower positions along the arrangement direction of alloy roasting devices, an upper weighing trolley which can slide is installed on the upper guide rail and can move to a position of a charging port, the lower guide rail extends out of the alloy roasting device area, a lower weighing trolley which can slide is installed on the lower guide rail, the gathering device comprises an alloy gathering hopper which is arranged below the extension position of the lower guide rail. The method adopts the device to conduct automatic loading of roasting alloys. By the aid of the device and the method, a large amount of iron alloys to be roasted are supplied to a revolving furnace quantitatively at the fixed time, the automation degree is high, and a large amount of alloys can be added in one time.

Description

technical field [0001] The invention belongs to the technical field of the metallurgical industry, and in particular relates to a fully automatic control method and device for automatically feeding baking alloys when a large-scale converter smelts silicon steel. Background technique [0002] Silicon steel is a ferrosilicon alloy with a silicon content of about 3% to 5%, and is an indispensable and important soft magnetic alloy for electric power, electronics and military industries. The production process of silicon steel is complicated, and the manufacturing technology is strict. The production technology at home and abroad pays more attention to technical confidentiality, which is regarded as the life of the enterprise. [0003] Compared with ordinary steel types, a large amount of baked ferroalloy needs to be added to the molten steel during the smelting and production of silicon steel. Alloy baking can solve the following problems: (1) After a large amount of alloy is d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): F27D13/00
Inventor 葛君生张佩灿陈鹏张发强雷加鹏胡晶晶袁晓峰李智
Owner WISDRI ENG & RES INC LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products