Toughened plastic tray and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology for tempering plastics and pallets, which is applied in the field of plastic product production, can solve the problems of unfavorable protection of forest resources, congenital material defects, and high manufacturing costs, and achieves the effects of low comprehensive cost, low price, and not easy to absorb water.
Inactive Publication Date: 2013-03-06
芜湖太平洋塑胶有限公司
View PDF2 Cites 14 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] At present, the pallets on the market are mainly wooden pallets and plastic pallets. Wooden pallets have a large demand for wood, which is not conducive to the protection of forest resources. In addition, fumigation or high-temperature disinfection treatment is required; while wooden pallets are subject to various restrictions, Some non-wood material pallets came into being
These non-wooden pallets, such as plywood pallets, paper pallets, plastic pallets and other new material pallets, do not need to be sterilized, but they are not perfect. Inherent material defects or high manufacturing costs make these pallets unable to fully replace wooden pallets
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment
[0022] The tempered plastic tray is made of the following raw materials in parts by weight: 60 parts of high-density polyethylene, 20 parts of polyvinyl chloride, 25 parts of wood flour, 12 parts of silicon carbide, 15 parts of modified kaolin, 40 parts of plastic recycled materials, active calcium 25 parts, 1 part of zinc stearate, 2 parts of calcium stearate, 3 parts of glycerol triglyceride, 0.4 part of polyethylene wax, 0.5 part of anilinomethyltriethoxysilane, 0.4 part of antioxidant 168 , 0.5 parts of anti-aging agent ODA, 8 parts of methyl methacrylate, 5 parts of ACM, 5 parts of MBS, 25 parts of oxidized polyethylene wax, 0.3 parts of azodicarbonamide, 6 parts of ACR, 10 parts of chlorinated polyvinyl chloride, 6 parts of high silica glass fiber, 5 parts of mineral fiber, 4 parts of semi-reinforcing carbon black.
[0023] The modified kaolin is prepared by the following method: adding an appropriate amount of water to the kaolin, then adding 3% of the dispersant sodium...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
bending strength
aaaaa
aaaaa
heat deflection temperature
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a toughened plastic tray prepared from the following raw materials in parts by weight: 50-60 parts of high density polyethylene, 20-30 parts of polyvinyl chloride, 20-30 parts of wood flour, 10-15 parts of silicon carbide, 10-20 parts of modified kaolin, 40-50 parts of recycled plastic polymer, 20-30 parts of active calcium, 1-2 parts of zinc stearate, 1-2 parts of calcium stearate, 2-3 parts of glycerol triglyceride, 0.3-0.5 part of polyethylene wax, 0.4-0.6 part of anilmomethyl triethoxy silane, 0.3-0.4 part of antioxidant 1680, 0.4-0.6 part of anti-aging agent ODA, 8-10 parts of foaming regulator, 4-8 parts of ACM, 4-8 parts of MBS, 25-30 parts of oxidized polyethlene wax, 0.2-0.3 part of foaming agent, 4-8 parts of ACR, 8-12 parts of chlorinated polyvinyl chloride, 5-8 parts of high silica glass fiber, 4-6 parts of mineral fiber and 3-4 parts of semi-reinforced carbon black. The toughened plastic tray produced by the invention has good mechanical properties, good durability, high repeated utilization rate, ageing resistance and corrosion resistance, the tray can be sawed, planed and nailed while needing no steaming or high temperature sterilization treatment, the tray can be flushed and has less possibility of absorbing water and deforming, and no mildew is generated, so that the toughened plastic tray is especially suitable for application at plum rain seasons in the south of the lower reaches of the Yangtze river.
Description
technical field [0001] The invention relates to a toughened plastic tray and a preparation method thereof, belonging to the technical field of plastic product production. Background technique [0002] At present, the pallets on the market are mainly wooden pallets and plastic pallets. Wooden pallets have a large demand for wood, which is not conducive to the protection of forest resources. In addition, fumigation or high-temperature disinfection treatment is required; while wooden pallets are subject to various restrictions, Some non-wood material pallets came into being. These non-wooden pallets, such as plywood pallets, paper pallets, plastic pallets and other new material pallets, do not need to be sterilized, but they are not perfect. Inherent material defects or high manufacturing costs make these pallets unable to fully replace wooden pallets . There have been plastic wood materials for this reason. Wood-plastic materials can produce many products, one of which is c...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.