Corrosion-resistant neodymium-iron-boron permanent magnet material and preparation method thereof

A permanent magnet material, NdFeB technology, applied in the direction of magnetic materials, magnetic objects, electrical components, etc., can solve the problems of insufficient corrosion resistance of materials, complex rare earth recovery process, etc., to achieve improved magnetic properties, good stability and practicality performance, cost reduction

Active Publication Date: 2013-05-01
XUZHOU NANFANG YONGCI MATERIAL
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The problem with this technical solution is that the rare earth recovery process is complex
The problem with this method is that the corrosion resistance of the material obtained by this method is insufficient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Corrosion-resistant neodymium-iron-boron permanent magnet material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Prepare corrosion-resistant NdFeB permanent magnet materials according to the following steps:

[0029] 1) Treatment of praseodymium and neodymium waste: mix praseodymium and neodymium waste in hydrochloric acid with a mass concentration of 25%, the mass ratio of praseodymium and neodymium waste to hydrochloric acid is 1:2.0, then add oxalic acid to the hydrochloric acid mixture and stir evenly, the oxalic acid and hydrochloric acid mixture The weight ratio was 2.5:1. The precipitate collected after 1 hour was dried at a temperature of 120° C. for 1 hour, and then kept at a temperature of 1050° C. for 1.5 hours to obtain a precipitated rare earth oxide.

[0030] 2) Grinding ingredients: determine the content of Nd, Pr and Sc in the precipitated rare earth oxide, add praseodymium oxide powder, neodymium oxide powder and scandium oxide powder to the precipitated rare earth oxide after the measurement to adjust the composition, and the adjusted precipitate rare earth oxide ...

Embodiment 2

[0036] Prepare corrosion-resistant NdFeB permanent magnet materials according to the following steps:

[0037] 1) Treatment of praseodymium and neodymium waste: mix praseodymium and neodymium waste in hydrochloric acid with a mass concentration of 30%, the mass ratio of praseodymium and neodymium waste to hydrochloric acid is 1:2.0, then add oxalic acid to the hydrochloric acid mixture and stir evenly, the oxalic acid and hydrochloric acid mixture The weight ratio is 2.5:1. The precipitate collected after 1.5 hours was dried at 120°C for 1 hour, and then kept at 1100°C for 1 hour to obtain the precipitated rare earth oxide.

[0038] 2) Grinding ingredients: determine the content of Nd, Pr and Sc in the precipitated rare earth oxide, add praseodymium oxide powder, neodymium oxide powder and scandium oxide powder to the precipitated rare earth oxide after the measurement to adjust the composition, and the adjusted precipitate rare earth oxide The weight ratio of Nd:Pr:Sc in the ...

Embodiment 3

[0044] When preparing the magnetic alloy ingot in step 4), the ingredients are distributed according to the following weight percentages: Nd 20.8%, Pr 5.2%, B 3%, Ir 0.053%, Os 0.053%, Sc 0.52%, Cu 0.6%, and the rest is Fe.

[0045] All the other processes are the same as in embodiment one.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Thicknessaaaaaaaaaa
Widthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a corrosion-resistant neodymium-iron-boron permanent magnet material and a preparation method thereof. The corrosion-resistant neodymium-iron-boron permanent magnet material comprises the following components in percentage by weight: 20-26 percent of Nd, 5-6.5 percent of Pr, 1-4 percent of B, 0.05-0.065 percent of Ir, 0.05-0.065 percent of Os, 0.5-0.65 percent of Sc, 0.5-0.65 percent of Cu and the balance of Fe. The corrosion-resistant neodymium-iron-boron permanent magnet material disclosed by the invention is provided with uniform tissue and a robust structure, so that the corrosion resistance of the material can be enhanced, and the magnetic performance is improved. According to the preparation method of the corrosion-resistant neodymium-iron-boron permanent magnet material, raw materials of an alloy are directly produced by fully utilizing praseodymium and neodymium waste, a component mixture ratio is flexible, and the quality is controlled appropriately; and moreover, the cost can be reduced, a process is simple, and powder waste with high oxygen content is fully utilized.

Description

technical field [0001] The invention belongs to the field of functional materials, and relates to a corrosion-resistant NdFeB permanent magnet material and a preparation method. Background technique [0002] CN200910241836.X discloses a method for recovering rare earth elements from NdFeB waste, the implementation steps are as follows: a. Add water to the NdFeB waste; b. Grinding the prepared raw materials and filtering the mud formed after grinding; c. Oxidizing and roasting the filtered mud; d. Secondary grinding of the oxidized roasted product; e. acid leaching the secondary ground product; f. Carrying out solid-liquid separation on the product leached by adding acid, and extracting and removing iron from the separated material-liquid to form rare earth chloride; g. Use P507 kerosene-hydrochloric acid separation system to extract and separate rare earth chloride; h. In the separated rare earth chloride, the praseodymium and neodymium chloride are extracted to remove...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01F1/057C22C38/16C22C33/02
Inventor 张作州
Owner XUZHOU NANFANG YONGCI MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com