Manganese-iron alloy

A ferromanganese alloy, weight percentage technology, applied in the field of ferromanganese alloy, can solve problems such as excessive phosphorus and carbon content

Inactive Publication Date: 2013-05-08
黄宣斐
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a low-phosphorus, low-carbon ferromanganese alloy, which can effectively overcome the problem of excessive phosphorus and carbon content in the existing ferromanganese alloy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] The technical solutions of the present invention are described below through specific examples, and the following examples are only for illustrating the present invention rather than limiting the scope of the present invention.

[0012] A ferromanganese alloy, its composition includes by weight percentage, 50-70% of manganese, 3-5% of silicon, less than 1.0% of carbon, less than 0.1% of phosphorus, less than 0.02% of sulfur, not more than 2% other impurities, the balance being iron.

[0013] The preparation method of described ferromanganese alloy is:

[0014] Select scrap steel with a carbon content of less than 1.0% calculated by weight percentage, and add a calcium-based dephosphorization agent accounting for 13-15% of the weight of the steel, wherein the silicon weight content in the calcium-based dephosphorization agent is 30-35%; After all the above raw materials are melted, add a slagging agent to make slagging, and then add a slagging agent to remove the slaggi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a manganese-iron alloy. The manganese-iron alloy comprises the following components by weight percent: 50-70% of manganese, 3-5% of silicon, less than 1.0% of carbon, less than 1.0% of phosphorus, less than 0.02% of sulfur, less than 2% of other impurities and the balance of iron.

Description

technical field [0001] The invention belongs to the field of metal materials, in particular to a ferromanganese alloy used as a desulfurizer or a deoxidizer. Background technique [0002] With the development of the steel industry, many high-quality and high-quality alloy steels have been developed and used. However, the content of sulfur or oxygen in alloy steel has a great influence on the performance of alloy steel. Desulfurizers or deoxidizers are required when smelting alloy steel. At the same time, when special steel is required, the wear resistance and high strength of manganese alloy steel are widely used. Therefore, in the process of using ferromanganese alloy to prepare manganese alloy steel, it can be used as raw material and can also play the role of deoxidizer and desulfurizer, which is the first choice for refining manganese alloy steel. [0003] However, the content of phosphorus and carbon in the currently used ferromanganese alloy is too high, which incre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C22/00C21C7/06C21C7/064
Inventor 黄宣斐
Owner 黄宣斐