Vulcanized paper raw paper and manufacturing process thereof

A technology of steel paper and base paper, applied in papermaking, synthetic cellulose/non-cellulose material pulp/paper, textile and papermaking, etc., to achieve the effect of low cost, improved electrical strength, good strength and smoothness

Active Publication Date: 2015-01-07
杭州特种纸业有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to improve the technical deficiencies in the existing steel paper base paper production process to obtain high strength, good water absorption and deformation Low, good formation, good stiffness steel base paper, and the production process is simple and easy to control, low cost, short cycle

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] (1) Beating: put 94kg of refined cotton fibers into a beater for beating treatment, the beating degree is 35°SR, the wet weight is 8g, and the beating concentration is 3%;

[0031] (2) Rinse: Screen, purify and rinse the pulp obtained from beating;

[0032] (3) Homogenization: Mix the rinsed slurry with 6kg of glass fiber evenly to obtain a mixed slurry in which cotton fibers and glass fibers are interlaced and evenly distributed;

[0033] (4) Papermaking: the slurry obtained in step (3) is made on a paper machine, and then dried by pressing and dehydrating and hot-pressing drying equipment to obtain base paper;

[0034] (5) Packing: Cut, inspect and pack the paper obtained in step (4).

Embodiment 2

[0036] (1) Beating: put 97kg of refined cotton fibers into a beater for beating treatment, the beating degree is 36°SR, the wet weight is 7.6g, and the beating concentration is 10%;

[0037] (2) Rinse: Screen, purify and rinse the pulp obtained from beating;

[0038] (3) Homogenization: Mix the rinsed slurry with 3kg of glass fiber evenly to obtain a mixed slurry in which cotton fibers and glass fibers are interlaced and evenly distributed;

[0039] (4) Papermaking: the slurry obtained in step (3) is made on a paper machine, and then dried by pressing and dehydrating and hot-pressing drying equipment to obtain base paper;

[0040] (5) Packing: Cut, inspect and pack the paper obtained in step (4).

Embodiment 3

[0042] (1) Beating: put 95kg of refined cotton fibers into a beater for beating treatment, the beating degree is 37°SR, the wet weight is 7.2g, and the beating concentration is 5%;

[0043] (2) Rinse: Screen, purify and rinse the pulp obtained from beating;

[0044] (3) Homogenization: Mix the rinsed slurry with 5kg of glass fiber evenly to obtain a mixed slurry in which cotton fibers and glass fibers are interlaced and evenly distributed;

[0045] (4) Papermaking: the slurry obtained in step (3) is made on a paper machine, and then dried by pressing and dehydrating and hot-pressing drying equipment to obtain base paper;

[0046] (5) Packing: Cut, inspect and pack the paper obtained in step (4).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
whitenessaaaaaaaaaa
Login to View More

Abstract

Vulcanized paper raw paper is prepared from the following raw materials: by weight, 94%-97% of cotton fibers, and 3%-6% of glass fibers. A manufacturing method of the vulcanized paper raw paper comprises the following steps of beating, poaching, pulp evening, paper-making and packaging. The vulcanized paper raw paper is high in strength, good in water-absorbing capacity, low in deformability, good in evenness, and good in stiffness. Moreover, the manufacturing process is simple and easy to control, cost is low and period is short.

Description

technical field [0001] The invention relates to a steel paper base paper and a manufacturing process thereof. Background technique [0002] Steel paper base paper is a special paper made from plant fiber by paper machine. The steel paper base paper can be made into steel paper after layer-by-layer stacking and gelation reaction. Steel paper is as hard as steel and as light as paper. It has excellent electrical insulation and is widely used as an insulating material in the electrical industry, textile industry, transportation and other industries. [0003] Further improving the strength and other properties of finished steel paper has always been the goal pursued by the industry. At present, an effective method is to prepare glass fiber-steel paper composite materials, and use the advantages of high strength and good toughness of glass fiber to improve the strength performance of steel paper. For example, a high-strength product is made by wrapping a glass fiber layer on t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21H13/40
Inventor 吴安波
Owner 杭州特种纸业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com