A kind of manufacturing process of 100% soybean wax candle

A production process, soybean wax technology, applied in the production of candles, fatty acids, etc., can solve the problems of candle proportion limitation, homogeneous polycrystalline, surface blooming, etc., achieve the effect of dense structure, single crystal form, and inhibition of migration

Active Publication Date: 2019-01-01
QINGDAO KINGKING APPL CHEM CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the structure of natural soybean wax is relatively complex, and it is prone to high temperature oil production, asynchronous phenomenon and common homogeneous polycrystal phenomenon in the cooling process, which leads to the separation of essence and wax body and recrystallization caused by the separation of different components of wax body , it is easy to cause problems of uneven crystallization and flowering on the surface of the product, so the proportion in candles is limited to a certain extent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Embodiment 1: a kind of manufacturing process of 100% soybean wax candle comprises the following steps:

[0018] A. Preheat the transparent glass tire mold with the wick to 40~50°C in advance;

[0019] B. Mix two kinds of soybean waxes with melting points of 42°C and 52°C in a ratio of 40:60 by weight. After heating and melting completely, add isopropyl myristate of 2% of the total weight of soybean wax as crystal modification agent, mixed thoroughly and cast into the tire mold at 70~75°C;

[0020] C. Control the ambient temperature at 18~25°C, cool and form;

[0021] D. The ambient temperature is controlled at 30~35°C for aging for 48 hours to slowly cool the wax liquid and form a stable crystal form.

Embodiment 2

[0022] Embodiment 2: a kind of manufacturing process of 100% soybean wax candle, comprises the following steps: all the other steps are the same as embodiment 1, the difference is that the selected crystal modifier is methyl laurate.

Embodiment 3

[0023] Embodiment 3: a kind of manufacture craft of 100% soybean wax candle, comprises the following steps:

[0024] A. Preheat the transparent glass tire mold with the wick to 40~50°C in advance;

[0025] B. Mix two kinds of soybean waxes with hydrogenated melting points of 42°C and 52°C in a ratio of 50:50 by weight. After heating and melting completely, add isopropyl myristate and laurel with 1.5% of the total weight of soybean wax Methyl ester mixture is used as a crystal modifier, mixed thoroughly and cast into the tire mold at 70~75°C;

[0026] C. Control the ambient temperature at 18~25°C, cool and form;

[0027] D. The ambient temperature is controlled at 30~35°C and aged for 48 hours to slowly cool the wax liquid and form a stable crystal form.

[0028] Wherein, isopropyl myristate and methyl laurate are mixed in a weight ratio of 1:1.

[0029] In addition to glass, the tire mold material described in the above steps A and B can also be selected from ceramics, pott...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a manufacturing craft of a wax candle with 100% soy wax. The manufacturing craft is characterized by comprising the following steps: A, a forming die adhered to a lamp wick is preheated to between 40 DEG C and 50 DEG C to be reserved; B, two kinds of soy wax with the respective melting point of 42 DEG C and 52 DEG C are mixed with the proportion of 40 to 60 to 60 to 40 by weight, the soy wax is heated so as to be melt completely, a crystallization modifying agent is added, and the soy wax and the crystallization modifying agent are cast to the forming die after blending sufficiently under the temperature between 70 DEG C and 75 DEG C; C, the temperature is controlled between 18 DEG C and 25 DEG C, the wax candle is formed in a cooling mode; and D, the temperature is controlled between 30 DEG C and 35 DEG C for aging of 48h, wax liquid is cooled slowly, and a stable crystallization shape is formed. According to the manufacturing craft, the soy wax replaces paraffin wax completely, the 100% addition is achieved, crystallization synchronization of different components of the soy wax is achieved due to addition of the crystallization modifying agent, diffusion of small components such as essence is restrained, cup wall dropping resistance filling wax which is small in contraction is made, the product is compact in structure, and single in crystal form.

Description

technical field [0001] The invention relates to a candle making process, in particular to a 100% soybean wax candle making process. Background technique [0002] At present, the raw material for making candles is mainly paraffin wax extracted from petroleum. When lit, paraffin wax not only causes pollution, but also endangers human health. And soy wax is a pure natural product. Compared with paraffin wax, it does not contain petroleum and other harmful chemical components, is completely non-toxic, and also has its unique natural fragrance, so it is more and more popular among candle consumers. However, the structure of natural soybean wax is relatively complex, and it is prone to high temperature oil production, asynchronous phenomenon and common homogeneous polycrystal phenomenon in the cooling process, which leads to the separation of essence and wax body and recrystallization caused by the separation of different components of wax body , It is easy to cause problems of u...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C11C5/00
Inventor 陈索斌
Owner QINGDAO KINGKING APPL CHEM CO LTD